X105CrMo17
2014-11-17 10:46:52 Origin： Remark：0 Click：
X105CrMo17 is a Martensitic & precipitation hardening Corrosion-resisting steel, X105CrMo17 is generally supplied in form of round bar, flat bar, hollow bar, and forging piece fabricated from steelmaking, hot forging, hot rolling, heat treatment, cold machined.
MATERIAL TECHNICAL DATASHEET - Grade DIN X105CrMo17
MATERIAL CATEGORY - Martensitic and precipitation hardening corrosion resisting steels
MATERIAL SPECIFICATIONS - DIN 17445,17440, DIN EN 10088-1, 10297,10272,10312
CHEMICAL COMPOSITION (mass weight %)
C (％): 0.95～1.20
Si (％)≤: 1.00
Mn (％)≤: 1.00
P (％)≤: 0.040
S (％)≤: 0.030
Cr (％): 16.0～18.0
Ni (％): -
Mo (％): 0.40～0.80
Si (％)≤: 1.00
Mn (％)≤: 1.00
P (％)≤: 0.040
S (％)≤: 0.030
Cr (％): 16.0～18.0
Ni (％): -
Mo (％): 0.40～0.80
MECHANICAL PROPERTIES UNDER ROOM TEMPERATURE
Tensile strenght, σb/MPa: -
Yield strength, σ0.2≥/MPa:
Elongation, δ5 ≥(％): -
Elongation, δ5 ≥(％): -
Reduction of area, ψ ≥(％): -
Impact strength, Akv≥/J: -
/40Hardness HBS30: 285 max
Impact strength, Akv≥/J: -
/40Hardness HBS30: 285 max
MECHANICAL PROPERTIES ABOVE ROOM TEMPERATURE
Hot forming temp/℃: 1100 ~ 900
Heat treatment temperature and cooling methods|annealing: 780 ~ 840 furnace cooled
Heat treatment temperature and cooling methods|quenching: 1000~1050 oil cooled
Heat treatment temperature and cooling methods|tempering: 100~300
Condition: -
High temperature yield strength σ0.2/MPa≥/MPa，at below temp/℃|100: -
High temperature yield strength σ0.2/MPa≥/MPa，at below temp/℃|200: -
High temperature yield strength σ0.2/MPa≥/MPa，at below temp/℃|200: -
High temperature yield strength σ0.2/MPa≥/MPa，at below temp/℃|300: -
High temperature yield strength σ0.2/MPa≥/MPa，at below temp/℃|400: -
High temperature yield strength σ0.2/MPa≥/MPa，at below temp/℃|400: -
High temperature yield strength σ0.2/MPa≥/MPa，at below temp/℃|500: -
PRODUCT DESCRIPTION
The alloy is usually produced by AOD / VOD /VIM followed by electroslag refining (ESR) / VAR if necessary for special purpose. Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied black/bright in the annealed condition.
Final heat treatment - solution treatment / QT
The alloy is usually produced by AOD / VOD /VIM followed by electroslag refining (ESR) / VAR if necessary for special purpose. Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied black/bright in the annealed condition.
Final heat treatment - solution treatment / QT
The alloys have ultra-high strength, superior toughness characteristics and weldability. Typically, these alloys are used in aerospace applications, machinery and tooling and ordnance components and fasteners.
TYPICAL APPLICATIONS
Medical equipment & parts.
Chemical equipments, Mechanical parts used in the condition of corrosion resistance.
Bolt and nut, Pressure vessel.
Bolt and nut, Pressure vessel.
PRODUCT PROFILE & DIMENSIONS
Round bar / Wire rod (Diameter): 5.5mm to 550mm
Square bar / Flat bar: 3mm to 800mm
Round bar / Wire rod (Diameter): 5.5mm to 550mm
Square bar / Flat bar: 3mm to 800mm
Length: Fixed length or random length or based on the customer's special requirement.
Heavy/middle plate via hot rolled: T60 - 450mm X W50 - 1000mm X L1000 - 6000mm
Heavy/middle plate via hot rolled: T60 - 450mm X W50 - 1000mm X L1000 - 6000mm
Sheet steel via cold rolled: T0.5 - 6mm X W600- 1000mm X L1000 - 2000mm
Steel strip via cold rolled: T0.1 - 3mm X W5 - 200mm X L (or in coil form)
Forging piece: stepped shafts with flanks / discs /tubes /slugs /donuts /cubes /other different shapes based on OEM.
TECHNICAL SALES ASSISTANCE
If you meet further on any technical enquiry, pleased to EMAIL our resident team of qualified production engineers, Email: sales@ccsteels.com.
If you meet further on any technical enquiry, pleased to EMAIL our resident team of qualified production engineers, Email: sales@ccsteels.com.
Hot search：X105CrMo17
Total list
Monthly rank
- 24X35CrMo17
- 23Z15CN17-03
- 23ASTM A565 Gr.616HT
- 21X10CrNiW17-13-3
- 19ASTM A638 Gr.660
- 18AISI 306
- 15SAE 51420
- 14P550
- 14SAE 51416
- 14X12CrMoWVNbN10-1-1