1.4305 /DIN X8CrNiS18-9
2014-11-17 16:33:58 Origin: Remark:0 Click:
1.4305/DIN X8CrNiS18-9 belong to Free Machining Austenitic Stainless steel, it is available in form of round bar, flat bar, forging pieces. it offers superior Mechanical properties from steelmaking, hot forging, hot rolling, heat treatment, cold working.
TECHNICAL DATA SHEET - DIN X8CrNiS18-9 / W-Nr 1.4305
MATERIAL CATEGORY - Austenitic corrosion resisting steels
PRODUCT DESCRIPTION
The alloy is usually produced by AOD or EAF if necessary for special purpose.
Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied black/bright in the annealed condition.
Final heat treatment - solution treatment / QT
The alloy is usually produced by AOD or EAF if necessary for special purpose.
Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied black/bright in the annealed condition.
Final heat treatment - solution treatment / QT
Maraging steels are iron-nickel alloys with absence of carbon and have metals such as molybdenum, cobalt, titanium and aluminum.
The alloys have ultra-high strength, superior toughness characteristics and weldability. Typically, these alloys are used in aerospace applications, machinery and tooling and ordnance components and fasteners.
MATERIAL SPECIFICATIONS - DIN 17445,17440(1999/1996), DIN EN 10088-1, 10297,10272,10312
CHEMICAL COMPOSITION (mass weight %)
C (%): ≤ 0.10
Si (%)≤: 1.00
Mn (%)≤: 2.00
P (%)≤: 0.045
S (%)≤: 0.15 ~ 0.35
Cr (%): 17.0 ~ 19.0
Ni (%): 8.00 ~ 10.0
Mo (%): -
Other(%): Cu ≤ 0.11, N ≤ 0.11
Si (%)≤: 1.00
Mn (%)≤: 2.00
P (%)≤: 0.045
S (%)≤: 0.15 ~ 0.35
Cr (%): 17.0 ~ 19.0
Ni (%): 8.00 ~ 10.0
Mo (%): -
Other(%): Cu ≤ 0.11, N ≤ 0.11
MECHANICAL PROPERTIES ( FINAL HEAT TREATMENT OR Q/T) UNDER ROOM TEMPERATURE
Condition: solution treatment
Thickness/mm:160
Thickness/mm:160
σb/MPa: 500~750
σ0.2≥/MPa:190
δ5≥(%): 35
δ5≥(%): 35
ψ≥(%): 60
Akv≥/J: -
/40Hardness HBS30: 230max
Akv≥/J: -
/40Hardness HBS30: 230max
MECHANICAL PROPERTIES ( FINAL HEAT TREATMENT OR Q/T) ABOVE ROOM TEMPERATURE
Hot forming temp/℃: 1200 ~ 900
Heat treatment temperature and cooling methods|annealing: -
Heat treatment temperature and cooling methods|quenching: 1000~1100 air/water cooled
Heat treatment temperature and cooling methods|tempering: -
Condition: -
High temperature yield strength σ0.2/MPa≥/MPa,at below temp/℃|100: -
High temperature yield strength σ0.2/MPa≥/MPa,at below temp/℃|200: -
High temperature yield strength σ0.2/MPa≥/MPa,at below temp/℃|200: -
High temperature yield strength σ0.2/MPa≥/MPa,at below temp/℃|300: -
High temperature yield strength σ0.2/MPa≥/MPa,at below temp/℃|400: -
High temperature yield strength σ0.2/MPa≥/MPa,at below temp/℃|400: -
High temperature yield strength σ0.2/MPa≥/MPa,at below temp/℃|500: -
AVAILABILITY
Round bar / flat bar / steel strip / sheet / square bar
Bright - peeled + polishing, centerless grinding
Forged - ring, tube, pipe casing, discs, shaft
Bright - peeled + polishing, centerless grinding
Forged - ring, tube, pipe casing, discs, shaft
TYPICAL APPLICATIONS
Medical equipment, Chemical equipments, Mechanical parts used in the condition of corrosion resistance.
Bolt and nut, Pressure vessel.
PRODUCT PROFILE
Round bar / Wire rod (Diameter): 5.5mm to 550mm
Square bar / flat bar: 10mm to 800mm
Square bar / flat bar: 10mm to 800mm
Length: Fixed length or random length or based on the customer's special requirement.
Heavy/middle plate via hot rolled: T6 - 200mm X W10 - 1500mm X L1000-12000mm
Sheet steel via cold rolled: T0.5 - 6mm X W6 - 1000mm X L1000 - 2000mm
Steel strip via cold rolled: T0.1 - 3mm X W5 - 200mm X L (or in coil form)
Forging piece: stepped shafts / other different shapes based on OEM.
TECHNICAL SALES ASSISTANCE
If you meet further on any technical enquiry. pleased to EMAIL our resident team of qualified production engineers. Email: sales@ccsteels.com
Hot search:1.4305 /DIN X8CrNiS18-9
Previous page:X8CrNiS18-9
Last page:X2CrNi19-11
Total list
Monthly rank
- 24X35CrMo17
- 23Z15CN17-03
- 23ASTM A565 Gr.616HT
- 21X10CrNiW17-13-3
- 19ASTM A638 Gr.660
- 18AISI 306
- 15SAE 51420
- 14P550
- 14SAE 51416
- 14X12CrMoWVNbN10-1-1