RAW MATERIAL DATA SHEET - DIN X12CrNi17-7 & W-Nr 1.4310
MATERIAL CATEGORY: Common alloy steel - Austenitic corrosion resisting steels
PRODUCT DESCRIPTION
The alloy is usually produced by AOD / BEF / EAF followed by electroslag refining (ESR) / VAR if necessary for special purpose.
Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied black/bright in the annealed condition.
Final heat treatment - solution treatment / QT
The alloy is usually produced by AOD / BEF / EAF followed by electroslag refining (ESR) / VAR if necessary for special purpose.
Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied black/bright in the annealed condition.
Final heat treatment - solution treatment / QT
Maraging steels are iron-nickel alloys with absence of carbon and have metals such as molybdenum, cobalt, titanium and aluminum.
The alloys have ultra-high strength, superior toughness characteristics and weldability. Typically, these alloys are used in aerospace applications, machinery and tooling and ordnance components and fasteners.
MATERIAL SPECIFICATIONS - DIN 17445,17440, DIN EN 10088-1, 10297,10272,10312
CHEMICAL COMPOSITION (Mass weight - %)
C (％): 0.05 ~ 0.12
Si (％): ≤ 2.00
Mn (％): ≤ 2.00
P (％)≤: 0.045
S (％)≤: 0.015
Cr (％): 16.0 ~ 19.0
Ni (％): 6.00 ~ 9.50
Mo (％): ≤ 0.80
Si (％): ≤ 2.00
Mn (％): ≤ 2.00
P (％)≤: 0.045
S (％)≤: 0.015
Cr (％): 16.0 ~ 19.0
Ni (％): 6.00 ~ 9.50
Mo (％): ≤ 0.80
N (％): ≤ 0.11
MECHANICAL PROPERTIES UNDER ROOM TEMPERATURE
Condition: solution treatment
Thickness/mm:40
Thickness/mm:40
Tensile strength, σb/MPa: 500 ~ 750
Yield strength, σ0.2≥/MPa: 185
Elongation, δ5≥(％): 40.0
Elongation, δ5≥(％): 40.0
Reduction of area, ψ≥(％): 50.0
Imapct, Akv≥/J: -
/40Hardness HBS30: 230max
Imapct, Akv≥/J: -
/40Hardness HBS30: 230max
MECHANICAL PROPERTIES FINAL HEAT TREATMENT ABOVE ROOM TEMPERATURE
Heat treatment temperature and cooling methods|annealing: -
Heat treatment temperature and cooling methods|quenching: 1000~1100 air/water cooled
Heat treatment temperature and cooling methods|tempering: -
Condition: -
High temperature yield strength σ0.2/MPa≥/MPa，at below temp/℃|100: -
High temperature yield strength σ0.2/MPa≥/MPa，at below temp/℃|200: -
High temperature yield strength σ0.2/MPa≥/MPa，at below temp/℃|200: -
High temperature yield strength σ0.2/MPa≥/MPa，at below temp/℃|300: -
High temperature yield strength σ0.2/MPa≥/MPa，at below temp/℃|400: -
High temperature yield strength σ0.2/MPa≥/MPa，at below temp/℃|400: -
High temperature yield strength σ0.2/MPa≥/MPa，at below temp/℃|500: -
HEAT TREATMENT PRACTICE
Heat treatment is only suitable for specific grades of stainless steel. When heat treating a stainless the hardening temperatures, including rate of heating, cooling and soaking times will vary due to several factors such as the shape and size of each component. Other considerations during the heat treatment process include the type of furnace, quenching medium and work piece transfer facilities. Please consult with the heat treatment provider for whole guidance on heat treatment of stainless steel grades. We are delighted to help to work with you the special heat treatment based on your special requirements.
Heat treatment is only suitable for specific grades of stainless steel. When heat treating a stainless the hardening temperatures, including rate of heating, cooling and soaking times will vary due to several factors such as the shape and size of each component. Other considerations during the heat treatment process include the type of furnace, quenching medium and work piece transfer facilities. Please consult with the heat treatment provider for whole guidance on heat treatment of stainless steel grades. We are delighted to help to work with you the special heat treatment based on your special requirements.
AVAILABILITY
Round bar / flat bar / steel strip / square bar
Bright - peeled + polishing, centerless grinding
Forged - ring, tube, pipe casing, discs, shaft
Round bar / flat bar / steel strip / square bar
Bright - peeled + polishing, centerless grinding
Forged - ring, tube, pipe casing, discs, shaft
PROFILE & DIMENSION
Round bar / Wire rod (Diameter): 5.5mm to 800mm
Square bar / Flat bar: 10mm to 800mm
Round bar / Wire rod (Diameter): 5.5mm to 800mm
Square bar / Flat bar: 10mm to 800mm
Length: Fixed length or random length or based on the customer's special requirement.
Heavy/middle plate via hot rolled: T60 - 300mm X W10 - 1200mm X L1000 ~ 4000mm
Sheet steel via cold rolled: T1.0 - 6mm X W6 - 1000mm X L1000 - 2000mm
Steel strip via cold rolled: T0.5 - 3mm X W5 - 200mm X L (or in coil form)
Forging piece: stepped shafts with flanks / discs /tubes /slugs /donuts /cubes /other different shapes based on OEM.
TYPICAL APPLICATIONS
Medical equipment.
Chemical equipments.
Mechanical parts used in the condition of corrosion resistance.
Bolt and nut.
Pressure vessel.
Mechanical parts used in the condition of corrosion resistance.
Bolt and nut.
Pressure vessel.
TECHNICAL SALES ASSISTANCE
If you meet further on any technical enquiry. pleased to EMAIL our resident team of qualified production engineers. E-mail: sales@ccsteels.com
If you meet further on any technical enquiry. pleased to EMAIL our resident team of qualified production engineers. E-mail: sales@ccsteels.com
INVENTORY - rolled/forged - Round bar: 30 / 45mm
Hot search：X12CrNi17-7
Previous page：1.4310 / DIN X10CrNi18-8
Last page：X2CrNiN18-10
Total list
Monthly rank
- 24X35CrMo17
- 23Z15CN17-03
- 23ASTM A565 Gr.616HT
- 21X10CrNiW17-13-3
- 19ASTM A638 Gr.660
- 18AISI 306
- 15SAE 51420
- 14P550
- 14SAE 51416
- 14X12CrMoWVNbN10-1-1