X3CrNiMo13-4
2014-11-18 10:37:57 Origin： Remark：0 Click：
Martensitic Steel X3CrNiMo13-4 Round bar, Flat bar, Plate Inventory X3CrNiMo13-4 Stock Available Properties from steelmaking, hot forging/rolling, heat treatment
MATERIAL DATA SHEET - DIN X3CrNiMo13-4
MATERIAL CATEGORY - Martensitic corrosion resisting steels
MATERIAL SPECIFICATIONS - DIN 17445,17440, DIN EN 10088-1, 10297,10272,10312
CHEMICAL COMPOSITION (mass Weight - %)
Carbon, C (％): ≤ 0.05
Silicon, Si (％)≤: 0.70
Manganese, Mn (％)≤: 1.50
Phosphorus, P (％) ≤: 0.040
Sulfur, S (％) ≤: 0.015
Chromium, Cr (％): 12.0～14.0
Nickel, Ni (％): 3.50～4.50
Molybdneum, Mo (％): 0.30～0.70
Other(％): Nitrogen, N ≥ 0.020
Silicon, Si (％)≤: 0.70
Manganese, Mn (％)≤: 1.50
Phosphorus, P (％) ≤: 0.040
Sulfur, S (％) ≤: 0.015
Chromium, Cr (％): 12.0～14.0
Nickel, Ni (％): 3.50～4.50
Molybdneum, Mo (％): 0.30～0.70
Other(％): Nitrogen, N ≥ 0.020
MECHANICAL PROPERTIES FINAL HEAT TREATMENT
Condition: heat treatment
Thickness/mm: 160~25
Thickness/mm: 160~25
Tensile strength, σb/MPa: 650～830
Yield strengt, σ0.2≥/MPa: 520
Elongation, δ5≥(％): 15/12
Reduction of area, ψ≥(％): —
Impact strength, Akv≥/J: 70/50
Yield strengt, σ0.2≥/MPa: 520
Elongation, δ5≥(％): 15/12
Reduction of area, ψ≥(％): —
Impact strength, Akv≥/J: 70/50
/40Hardness HBS30: -
Condition: heat treatment
Thickness/mm: 160~25
Thickness/mm: 160~25
σb/MPa: 780～980
σ0.2≥/MPa: 620
δ5≥(％): 15/12
ψ≥(％): —
Akv≥/J: 70/50
σ0.2≥/MPa: 620
δ5≥(％): 15/12
ψ≥(％): —
Akv≥/J: 70/50
/40Hardness HBS30: -
Thickness/mm: 160~25
σb/MPa: 900～1100
σ0.2≥/MPa: 800
δ5≥(％): 12/10
ψ≥(％): —
Akv≥/J: 50/40
σ0.2≥/MPa: 800
δ5≥(％): 12/10
ψ≥(％): —
Akv≥/J: 50/40
/40Hardness HBS30: -
MECHANICAL PROPERTIES ABOVE ROOM TEMP.
Heat treatment temperature and cooling methods|annealing: 600~640
Heat treatment temperature and cooling methods|quenching: 950~1050 air/oil cooled
Heat treatment temperature and cooling methods|tempering: 520~700
Condition: heat treatment
High temperature yield strength σ0.2/MPa≥/MPa，at below temp/℃|100: 500
High temperature yield strength σ0.2/MPa≥/MPa，at below temp/℃|200: 480
High temperature yield strength σ0.2/MPa≥/MPa，at below temp/℃|200: 480
High temperature yield strength σ0.2/MPa≥/MPa，at below temp/℃|300: 460
High temperature yield strength σ0.2/MPa≥/MPa，at below temp/℃|400: -
High temperature yield strength σ0.2/MPa≥/MPa，at below temp/℃|400: -
High temperature yield strength σ0.2/MPa≥/MPa，at below temp/℃|500: -
Condition: heat treatment
High temperature yield strength σ0.2/MPa≥/MPa，at below temp/℃|100: 590
High temperature yield strength σ0.2/MPa≥/MPa，at below temp/℃|200: 560
High temperature yield strength σ0.2/MPa≥/MPa，at below temp/℃|200: 560
High temperature yield strength σ0.2/MPa≥/MPa，at below temp/℃|300: 530
High temperature yield strength σ0.2/MPa≥/MPa，at below temp/℃|400: -
High temperature yield strength σ0.2/MPa≥/MPa，at below temp/℃|400: -
High temperature yield strength σ0.2/MPa≥/MPa，at below temp/℃|500: -
Condition: heat treatment
High temperature yield strength σ0.2/MPa≥/MPa，at below temp/℃|100: 720
High temperature yield strength σ0.2/MPa≥/MPa，at below temp/℃|200: 665
High temperature yield strength σ0.2/MPa≥/MPa，at below temp/℃|200: 665
High temperature yield strength σ0.2/MPa≥/MPa，at below temp/℃|300: 620
High temperature yield strength σ0.2/MPa≥/MPa，at below temp/℃|400: -
High temperature yield strength σ0.2/MPa≥/MPa，at below temp/℃|400: -
High temperature yield strength σ0.2/MPa≥/MPa，at below temp/℃|500: -
TYPICAL APPLICATIONS
Medical equipments, Chemical equipments.
Mechanical parts used in the condition of corrosion resistance.
Bolt and nuts, Pressure vessel.
Bolt and nuts, Pressure vessel.
PROFILE & DIMENSIONS
Round bar / Disc (diameter): 5.5mm to 850mm
Square bar / Flat bar: 8mm to 800mm
Round bar / Disc (diameter): 5.5mm to 850mm
Square bar / Flat bar: 8mm to 800mm
Length: Fixed length or random length or based on the customer's special requirement.
Heavy/middle plate via hot rolled: T60 - 400mm X W50 - 1000mm X L1000 - 5000mm
Heavy/middle plate via hot rolled: T60 - 400mm X W50 - 1000mm X L1000 - 5000mm
Sheet steel via cold rolled: T0.5 - 6mm X W100 - 1000mm X L1000 - 2000mm
Steel strip via cold rolled: T0.1 - 3mm X W5 - 200mm X L (or in coil form)
Forging piece: stepped shafts, other different shapes based on OEM.
TECHNICAL SALES ASSISTANCE
If you meet further on any technical enquiry. pleased to EMAIL our resident team of qualified production engineers. Email: sales@ccsteels.com.
If you meet further on any technical enquiry. pleased to EMAIL our resident team of qualified production engineers. Email: sales@ccsteels.com.
Hot search：X3CrNiMo13-4
Previous page：1.4311 / X2CrNiN18-10
Last page：X4CrNi13-4
Total list
Monthly rank
- 24X35CrMo17
- 23Z15CN17-03
- 23ASTM A565 Gr.616HT
- 21X10CrNiW17-13-3
- 19ASTM A638 Gr.660
- 18AISI 306
- 15SAE 51420
- 14P550
- 14SAE 51416
- 14X12CrMoWVNbN10-1-1