DIN EN 10085 Material Specification Carburized Structural Steel 40CrMoV13-9 Forgings, Inventory 1.8523 & S132 Round bar, Flat bar Stock Available, ESR & VAR technique
Official Test Certificate: issued by TUV - SGS - BV
RAM MATERIAL SPECIFICATION - Grade 40CrMoV13-9
MATERIAL CATEGORY - Carburized Structural Steel
MATERIAL SPECIFICATIONS - DIN EN 10085 (2001), DIN 17211 (1987)
CHEMICAL COMPOSITION (mass weight - %)
Carbon, C (％): 0.35 ~ 0.43
Silicon, Si (％): 0.15 ~ 0.40
Manganese, Mn (％): 0.40 ~ 0.70
Phosphorus, P (％) ≤: 0.030
Sulfur, S (％) ≤: 0.035
Chromium, Cr (％): 3.00 ~ 3.50
Molybdenum, Mo (％): 0.80 ~ 1.10
Vanadium, V (％): 0.15 ~ 0.25
Carbon, C (％): 0.35 ~ 0.43
Silicon, Si (％): 0.15 ~ 0.40
Manganese, Mn (％): 0.40 ~ 0.70
Phosphorus, P (％) ≤: 0.030
Sulfur, S (％) ≤: 0.035
Chromium, Cr (％): 3.00 ~ 3.50
Molybdenum, Mo (％): 0.80 ~ 1.10
Vanadium, V (％): 0.15 ~ 0.25
MECHANICAL PROPERTIES - HOT WORKING, HEAT TREATMENT CYCLE
Hot working temperature /℃: 1050～850
Heat treatment temperature /℃|annealing: 650～700
Heat treatment temperature /℃|quenching: 920~960 Oil or air cooled
Heat treatment temperature /℃|tempering: 570～650
Hot working temperature /℃: 1050～850
Heat treatment temperature /℃|annealing: 650～700
Heat treatment temperature /℃|quenching: 920~960 Oil or air cooled
Heat treatment temperature /℃|tempering: 570～650
Heat treatment temperature /℃|carburizing: 490～510
Hardness after annealing HBS≤: 262
Hardness after annealing HBS≤: 262
Size /mm: ≤ 40
Tensile strength, ≥|σb/MPa: 1240
Yield strength, ≥|σs≥/MPa: 1080
Elongation, ≥|δ5(％)≥: 8.0
Impact strength, ≥|AKv /J (DVM-V form sampling): 27
Impact strength, ≥|AKv /J (DVM-V form sampling): 27
Size /mm: ≤ 100
≥|σb /MPa: 1270
≥|σs ≥/MPa: -
≥|δ5 (％)≥: -
≥|AKV /J (DVM-V form sampling): -
≥|AKV /J (DVM-V form sampling): -
Size /mm: ≤ 250
Tensile strength, ≥|σb /MPa: 1080
Yield strength, ≥|σs /MPa: -
Elongation, ≥| δ5 (％)≥: -
Impact strength, ≥ |AKV/J (DVM-V form sampling): -
Impact strength, ≥ |AKV/J (DVM-V form sampling): -
TYPICAL APPLICATIONS
Alloy structural steels are widely used in the filed of ship, vehicle, airplane, guided missile, weapons, railway, bridges, pressure vessel, machine tools, mechanical components with a bigger sectional size and so on.
Power generation – turbine fasteners – boiler support rods.
Process plant – fasteners.
Mechanical gears, gear shaft, main axis, valve rod.
Mechanical parts - connecting rod, bolt and nut.
Multidiameter shaft and pressure vessel.
Alloy structural steels are widely used in the filed of ship, vehicle, airplane, guided missile, weapons, railway, bridges, pressure vessel, machine tools, mechanical components with a bigger sectional size and so on.
Power generation – turbine fasteners – boiler support rods.
Process plant – fasteners.
Mechanical gears, gear shaft, main axis, valve rod.
Mechanical parts - connecting rod, bolt and nut.
Multidiameter shaft and pressure vessel.
PROFILE & DIMENSIONS
Round bar / Disc (diameter): 5.5mm to 800mm
Square bar / Flat bar: 10mm to 800mm
Length: Fixed length or random length or based on the customer's special requirement.
Round bar / Disc (diameter): 5.5mm to 800mm
Square bar / Flat bar: 10mm to 800mm
Length: Fixed length or random length or based on the customer's special requirement.
Heavy / middle plate via hot rolled: T60 - 400mm X W100 - 1000mm X L1000 ~ 4000mm
Sheet steel via cold rolled: T1.0 - 6mm X W100 - 1000mm X L1000 - 2000mm
Forging piece: stepped shafts, and other different shapes based on OEM.
Sheet steel via cold rolled: T1.0 - 6mm X W100 - 1000mm X L1000 - 2000mm
Forging piece: stepped shafts, and other different shapes based on OEM.
PRODUCT DESCRIPTION
Alloy structural steel is provided with higher yield strength, tensile strength, endurance strength, yield ratio (about 0.85 generally ) enough plasticity and toughness.
Alloy structural steel is provided with higher yield strength, tensile strength, endurance strength, yield ratio (about 0.85 generally ) enough plasticity and toughness.
The concentration of alloy element of this kind of steel is quite high, mainly are corrosion resistant steel, heat resistant steel, wear resistant steel, and other special steels of physical and chemical properties. Alloy structural steel has preferable mechanical property than that of carbon structural steel, high performance of heat treatment especially.
The alloy is usually produced by EAF /VD /LF followed by electroslag refining (ESR) if necessary for special purpose. Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different level according to the buyers' requirements.
Bars are usually supplied bright in the annealed condition, or bright annealing specially.
Final heat treatment - heat treatment / QT
The alloy is usually produced by EAF /VD /LF followed by electroslag refining (ESR) if necessary for special purpose. Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different level according to the buyers' requirements.
Bars are usually supplied bright in the annealed condition, or bright annealing specially.
Final heat treatment - heat treatment / QT
TECHNICAL SALES ASSISTANCE
If you meet further on any technical enquiry. pleased to EMAIL (sales@ccsteels.com) our resident team of qualified production engineers.
If you meet further on any technical enquiry. pleased to EMAIL (sales@ccsteels.com) our resident team of qualified production engineers.
Hot search：40CrMoV13-9
Previous page：1.8523
Last page：34CrAlN7-10
Total list
Monthly rank
- 3438NCD4
- 3424CrMo5
- 3119CrNi5
- 2938B3
- 28ASTM A739 type B11
- 2826NiCrMoV11-5
- 2742Cr4Mo2
- 24S135
- 24EN 38
- 22EN20B