Specification W-Nr 1.5919 datasheet, 1.5919 Chemical, 1.5919 Ring forging, Bar, Wire rod,W-Nr 1.5919 Sheet - steelmaking, ESR, hot blooming, hot forging, hot rolling, heat treat, straightened, ultrasonic test, cold working, machined. We also possess advanced precision machining equipments for further processing.
Technical standards - DIN EN 10263-4 (2002), DIN 1654 (1989) or by agreement.
Official Test Certificate: issued by TUV - SGS - BV
TECHNICAL SPECIFICATION - W-Nr 1.5919
MATERIAL CATEGORY: Cold heading & extruding steel
MATERIAL SPECIFICATIONS: DIN EN 10263-4 (2002), DIN 1654 (1989)
CHEMICAL COMPOSITION (WEIGHT %)
C (％): 0.14 ~ 0.19
Si (％): ≤ 0.40
Mn (％): 0.40 ~ 0.60
P (％)≤: 0.035
S (％)≤: 0.035
Cr (％): 1.40 ~ 1.70
Mo (％): —
Ni (％): 1.40 ~ 1.70
Si (％): ≤ 0.40
Mn (％): 0.40 ~ 0.60
P (％)≤: 0.035
S (％)≤: 0.035
Cr (％): 1.40 ~ 1.70
Mo (％): —
Ni (％): 1.40 ~ 1.70
MECHANICAL PROPERTIES - HEAT TREATMENT
Soft annealing temperature /℃: 650～720
Soft annealed (≤100mm)|σb/MPa: 610
Soft annealed (≤100mm)|ψ(％): 60
Cold draw soft annealed (≤60mm)|σb/MPa: 590
Cold draw soft annealed (≤60mm)|ψ(％): 62
Soft annealed (≤100mm)|σb/MPa: 610
Soft annealed (≤100mm)|ψ(％): 60
Cold draw soft annealed (≤60mm)|σb/MPa: 590
Cold draw soft annealed (≤60mm)|ψ(％): 62
Heat treatment / quenching temperature /℃| water quenching: -
Heat treatment / quenching temperature /℃|oil quenching: 800 - 830
Heat treatment / tempering temperature /℃: -
Heat treatment / quenching temperature /℃|oil quenching: 800 - 830
Heat treatment / tempering temperature /℃: -
Mechancial after heat treatment
≥|σb/MPa: 880 - 1180
≥|σs/MPa: 635
≥|δ5(％): 9
≥|ψ(％): 40
≥|σb/MPa: 880 - 1180
≥|σs/MPa: 635
≥|δ5(％): 9
≥|ψ(％): 40
≥|AKV DVM-V form sampling /J: 41
PRODUCT DESCRIPTION
Proven performance in long-term service.
Extensive database of long term, high temperature test results.
High room and elevated temperature strength.Good creep.
High notch tolerance.
Thermal expansion coefficients compatible with low alloy steel turbine casing materials.
Lower design and operating risks
Simplified design for bolting configuration compared with martensitic steels or high nickel alloys.
Proven performance in long-term service.
Extensive database of long term, high temperature test results.
High room and elevated temperature strength.Good creep.
High notch tolerance.
Thermal expansion coefficients compatible with low alloy steel turbine casing materials.
Lower design and operating risks
Simplified design for bolting configuration compared with martensitic steels or high nickel alloys.
Alloy structural steel is provided with higher yield strength, tensile strength, endurance strength, yield ratio (about 0.85 generally ) enough plasticity and toughness.
The concentration of alloy element of this kind of steel is quite high, mainly are corrosion resistant steel, heat resistant steel, wear resistant steel, and other special steels of physical and chemical properties. Alloy structural steel has preferable mechanical property than that of carbon structural steel, high performance of heat treatment especially.
The alloy is usually produced by EAF /VD /LF followed by electroslag refining (ESR) if necessary for special purpose.
Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different level according to the buyers' requirements.
Bars are usually supplied bright in the annealed condition, or bright annealing specially.
Final heat treatment - heat treatment / QT
The concentration of alloy element of this kind of steel is quite high, mainly are corrosion resistant steel, heat resistant steel, wear resistant steel, and other special steels of physical and chemical properties. Alloy structural steel has preferable mechanical property than that of carbon structural steel, high performance of heat treatment especially.
The alloy is usually produced by EAF /VD /LF followed by electroslag refining (ESR) if necessary for special purpose.
Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different level according to the buyers' requirements.
Bars are usually supplied bright in the annealed condition, or bright annealing specially.
Final heat treatment - heat treatment / QT
TYPICAL APPLICATIONS
Alloy structural steels are widely used in the filed of ship, vehicle, airplane, guided missile, weapons, railway, bridges, pressure vessel, machine tools, mechanical components with a bigger sectional size and so on.
Power generation – turbine fasteners – boiler support rods
Process plant – fasteners
Mechanical gears, gear shaft, main axis, valve rod
Mechanical parts - connecting rod, bolt and nut
Multidiameter shaft
Pressure vessel, seamless pipe
Alloy structural steels are widely used in the filed of ship, vehicle, airplane, guided missile, weapons, railway, bridges, pressure vessel, machine tools, mechanical components with a bigger sectional size and so on.
Power generation – turbine fasteners – boiler support rods
Process plant – fasteners
Mechanical gears, gear shaft, main axis, valve rod
Mechanical parts - connecting rod, bolt and nut
Multidiameter shaft
Pressure vessel, seamless pipe
TECHNICAL SALES ASSISTANCE
If you meet further on any technical enquiry, pleased to EMAIL our resident team of qualified production engineers. - Email: sales@ccsteels.com
If you meet further on any technical enquiry, pleased to EMAIL our resident team of qualified production engineers. - Email: sales@ccsteels.com
PROFILE & DIMENSIONS
Round bar / Wire rod (Diameter): 5.5mm to 550mm
Square bar / Flat bar: 3mm to 800mm
Length: Fixed length or random length or based on the customer's special requirement.
Round bar / Wire rod (Diameter): 5.5mm to 550mm
Square bar / Flat bar: 3mm to 800mm
Length: Fixed length or random length or based on the customer's special requirement.
Heavy/middle plate via hot rolled: T60 - 400mm X W60 - 1000mm X L1000-12000mm
Sheet steel via cold rolled: T0.5 - 6mm X W600- 1000mm X L1000 - 2000mm
Steel strip via cold rolled: T0.1 - 3mm X W5 - 200mm X L (or in coil form)
Forging piece: stepped shafts with flanks / discs /tubes /slugs /donuts /cubes /other different shapes based on OEM.
Sheet steel via cold rolled: T0.5 - 6mm X W600- 1000mm X L1000 - 2000mm
Steel strip via cold rolled: T0.1 - 3mm X W5 - 200mm X L (or in coil form)
Forging piece: stepped shafts with flanks / discs /tubes /slugs /donuts /cubes /other different shapes based on OEM.
Previous page：15CrNi6
Last page：DIN 20NiCrMo2-2
Total list
Monthly rank
- 3438NCD4
- 3424CrMo5
- 3119CrNi5
- 2938B3
- 28ASTM A739 type B11
- 2826NiCrMoV11-5
- 2742Cr4Mo2
- 24S135
- 24EN 38
- 22EN20B