1.7001
2015-02-05 11:19:35 Origin： Remark：0 Click：
Description 1.7001 Ex-stock Suppliers Shaft, Inventory 1.7001 Sheet Hot forging, rolling, heat treatment,straightened,ultrasonic test,cold working,machined. Technical standards - DIN EN 10263-4 (2002), DIN 1654 (1989) or by agreement.
OFFICIAL TEST CERTIFICATE: issued by TUV - SGS - BV
MATERIAL TECHNICAL DATASHEET - Grade W-Nr 1.7001
MATERIAL CATEGORY: Cold heading & cold extruding steel
MATERIAL SPECIFICATIONS: DIN EN 10263-4 (2002), DIN 1654 (1989)
CHEMICAL COMPOSITION (Mass weight - %)
C (％): 0.34 ~ 0.41
Si (％): ≤ 0.40
Mn (％): 0.50 ~ 0.80
P (％)≤: 0.035
S (％)≤: 0.035
Cr (％): 0.30 ~ 0.40
Mo (％): —
Ni (％): —
Si (％): ≤ 0.40
Mn (％): 0.50 ~ 0.80
P (％)≤: 0.035
S (％)≤: 0.035
Cr (％): 0.30 ~ 0.40
Mo (％): —
Ni (％): —
MECHANICAL PROPERTIES - HEAT TREATMENT
Soft annealing temperature /℃: 680～700
Soft annealed (≤100mm)|σb/MPa: 610
Soft annealed (≤100mm)|ψ(％): 58
Cold draw soft annealed (≤60mm)|σb/MPa: 590
Cold draw soft annealed (≤60mm)|ψ(％): 60
Soft annealed (≤100mm)|σb/MPa: 610
Soft annealed (≤100mm)|ψ(％): 58
Cold draw soft annealed (≤60mm)|σb/MPa: 590
Cold draw soft annealed (≤60mm)|ψ(％): 60
Heat treatment / quenching temperature /℃| water quenching: -
Heat treatment / quenching temperature /℃|oil quenching: 860 - 890
Heat treatment / tempering temperature /℃: 500~670
Heat treatment / quenching temperature /℃|oil quenching: 860 - 890
Heat treatment / tempering temperature /℃: 500~670
Mechancial after heat treatment
Tensile strength, ≥|σb/MPa: 780 - 980
Yield strength, ≥|σs/MPa: 630
Elongation, ≥|δ5(％): 12.0
Reduction of area, ≥|ψ(％): 45.0
Tensile strength, ≥|σb/MPa: 780 - 980
Yield strength, ≥|σs/MPa: 630
Elongation, ≥|δ5(％): 12.0
Reduction of area, ≥|ψ(％): 45.0
≥|AKV DVM-V form sampling /J: 48
PRODUCT DESCRIPTION
Proven performance in long-term service.
Extensive database of long term, high temperature test results.
High room and elevated temperature strength.Good creep.
High notch tolerance.
Thermal expansion coefficients compatible with low alloy steel turbine casing materials.
Lower design and operating risks
Simplified design for bolting configuration compared with martensitic steels or high nickel alloys.
Proven performance in long-term service.
Extensive database of long term, high temperature test results.
High room and elevated temperature strength.Good creep.
High notch tolerance.
Thermal expansion coefficients compatible with low alloy steel turbine casing materials.
Lower design and operating risks
Simplified design for bolting configuration compared with martensitic steels or high nickel alloys.
Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different level according to the buyers' requirements.
Bars are usually supplied bright in the annealed condition, or bright annealing specially.
Final heat treatment - heat treatment / Quenched and tempered.
Bars are usually supplied bright in the annealed condition, or bright annealing specially.
Final heat treatment - heat treatment / Quenched and tempered.
AVAILABLE SHAPES
Round bar / flat bar / hexagon bar / strip / shaft
Bright - peeled + polishing, centerless grinding
Forged - ring, tube, pipe casing, discs, shaft.
PRODUCT PROFILE & DIMENSION
Round bar (Diameter): 5.5 to 500mm
Square bar / Flat bar: 10 to 800mm
Length: Fixed length or random length or based on the customer's special requirement.
Round bar (Diameter): 5.5 to 500mm
Square bar / Flat bar: 10 to 800mm
Length: Fixed length or random length or based on the customer's special requirement.
Heavy/middle plate via hot rolled: T6 - 200 X W10 - 1500 X L1000-12000mm
Sheet steel via cold rolled: T0.5 - 6 X W6 - 1000 X L1000 - 2000mm
Steel strip via cold rolled: T0.1 - 3 X W5 - 200 X L (or in coil form)
Forging piece: stepped shafts with flanks / discs /tubes /slugs /donuts /cubes /other different shapes based on OEM.
Sheet steel via cold rolled: T0.5 - 6 X W6 - 1000 X L1000 - 2000mm
Steel strip via cold rolled: T0.1 - 3 X W5 - 200 X L (or in coil form)
Forging piece: stepped shafts with flanks / discs /tubes /slugs /donuts /cubes /other different shapes based on OEM.
TYPICAL APPLICATIONS
Alloy structural steels are widely used in the filed of ship, vehicle, airplane, guided missile, weapons, railway, bridges, pressure vessel, machine tools, mechanical components with a bigger sectional size and so on.
Power generation – turbine fasteners – boiler support rods.
Process plant – fasteners, Mechanical gears, gear shaft, main axis, valve rod.
Mechanical parts - connecting rod, bolt and nut.
Multidiameter shaft and pressure vessel.
Alloy structural steels are widely used in the filed of ship, vehicle, airplane, guided missile, weapons, railway, bridges, pressure vessel, machine tools, mechanical components with a bigger sectional size and so on.
Power generation – turbine fasteners – boiler support rods.
Process plant – fasteners, Mechanical gears, gear shaft, main axis, valve rod.
Mechanical parts - connecting rod, bolt and nut.
Multidiameter shaft and pressure vessel.
TECHNICAL SALES ASSISTANCE
If you meet further on any technical enquiry. pleased to EMAIL our resident team of qualified production engineers, Email: sales@ccsteels.com.
If you meet further on any technical enquiry. pleased to EMAIL our resident team of qualified production engineers, Email: sales@ccsteels.com.
Hot search：1.7001
Total list
Monthly rank
- 3438NCD4
- 3424CrMo5
- 3119CrNi5
- 2938B3
- 28ASTM A739 type B11
- 2826NiCrMoV11-5
- 2742Cr4Mo2
- 24S135
- 24EN 38
- 22EN20B