DIN 26CrMo7
2015-02-10 09:30:54 Origin： Remark：0 Click：
Material specification 26CrMo7 datasheet,26CrMo7 Chemical,26CrMo7 Ring forging,26CrMo7 Bar,
26CrMo7 Wire rod,26CrMo7 Sheet - steelmaking,ESR,blooming,forging,rolling,heat treatment,
straightened,ultrasonic test,cold working,machined. We also possess advanced precision machining equipments for further processing.
Technical standards - DIN SEW 028 (1993), DIN EN 10216-2 (2004) or by agreement.
OFFICIAL TEST CERTIFICATE: issued by TUV - SGS - BV
TECHNICAL SPECIFICATION / DATASHEET - DIN 26CrMo7 / W-Nr 1.7259
MATERIAL CATEGORY: high temperature pressure vessel steel
MATERIAL SPECIFICATIONS: DIN SEW 028 (1993), DIN EN 10216-2 (2004)
CHEMICAL COMPOSITION (WEIGHT %)
C(％): 0.22～0.30
Si(％): 0.15~0.35
Mn(％): 0.50～0.70
P(％)≤: 0.035
S(％)≤: 0.035
Cr(％): 1.50～1.80
Mo(％): 0.20～0.25
Si(％): 0.15~0.35
Mn(％): 0.50～0.70
P(％)≤: 0.035
S(％)≤: 0.035
Cr(％): 1.50～1.80
Mo(％): 0.20～0.25
Other(％): -
MECHANICAL PROPERTIES - UNDER ROOM TEMPERATURE
Condition: quenched and tempered
Tensile strength σb≥/MPa: 640～780
Yield strength σs≥/MPa: 440
Elongation δ5≥(%): 17
AKV≥/J: 48
Annealed hardness HBS: 190～235
Yield strength σs≥/MPa: 440
Elongation δ5≥(%): 17
AKV≥/J: 48
Annealed hardness HBS: 190～235
HOT WORKING AND HEAT TREATMENT
Hot working temperature /℃: 1100～850
Annealing temperature /℃: 680～730
Quenching temperature /℃: 890～940
Cooling medium: Oil or Air quenched
Annealing temperature /℃: 680～730
Quenching temperature /℃: 890～940
Cooling medium: Oil or Air quenched
Tempering temperature /℃: 650～700
AVAILABLE SHAPES
Plate /Steel strip /sheet / bar / shaft
Bright - milling, polishing, cold machined/finished
Plate /Steel strip /sheet / bar / shaft
Bright - milling, polishing, cold machined/finished
PRODUCT DESCRIPTION
High room and elevated temperature strength.Good creep.
High notch tolerance.
Thermal expansion coefficients compatible with low alloy steel turbine casing materials.
Lower design and operating risks
Simplified design for bolting configuration compared with martensitic steels or high nickel alloys.
High room and elevated temperature strength.Good creep.
High notch tolerance.
Thermal expansion coefficients compatible with low alloy steel turbine casing materials.
Lower design and operating risks
Simplified design for bolting configuration compared with martensitic steels or high nickel alloys.
Proven performance in long-term service.
Extensive database of long term, high temperature test results.
Extensive database of long term, high temperature test results.
Alloy structural steel is provided with higher yield strength, tensile strength, endurance strength, yield ratio (about 0.85 generally ) enough plasticity and toughness.
The concentration of alloy element of this kind of steel is quite high, mainly are corrosion resistant steel, heat resistant steel, wear resistant steel, and other special steels of physical and chemical properties. Alloy structural steel has preferable mechanical property than that of carbon structural steel, high performance of heat treatment especially.
The alloy is usually produced by EAF /VD /LF followed by electroslag refining (ESR) if necessary for special purpose.
Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different level according to the buyers' requirements.
Bars are usually supplied bright in the annealed condition, or bright annealing specially.
Final heat treatment - heat treatment / QT
The concentration of alloy element of this kind of steel is quite high, mainly are corrosion resistant steel, heat resistant steel, wear resistant steel, and other special steels of physical and chemical properties. Alloy structural steel has preferable mechanical property than that of carbon structural steel, high performance of heat treatment especially.
The alloy is usually produced by EAF /VD /LF followed by electroslag refining (ESR) if necessary for special purpose.
Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different level according to the buyers' requirements.
Bars are usually supplied bright in the annealed condition, or bright annealing specially.
Final heat treatment - heat treatment / QT
TYPICAL APPLICATIONS
Alloy structural steels are widely used in the filed of ship, vehicle, airplane, guided missile, weapons, railway, bridges, pressure vessel, machine tools, mechanical components with a bigger sectional size and so on.
Power generation – turbine fasteners – boiler support rods
Process plant – fasteners
Mechanical gears, gear shaft, main axis, valve rod
Mechanical parts - connecting rod, bolt and nut
Multidiameter shaft
Pressure vessel, seamless pipe
Alloy structural steels are widely used in the filed of ship, vehicle, airplane, guided missile, weapons, railway, bridges, pressure vessel, machine tools, mechanical components with a bigger sectional size and so on.
Power generation – turbine fasteners – boiler support rods
Process plant – fasteners
Mechanical gears, gear shaft, main axis, valve rod
Mechanical parts - connecting rod, bolt and nut
Multidiameter shaft
Pressure vessel, seamless pipe
TECHNICAL SALES ASSISTANCE
If you meet further on any technical enquiry. pleased to EMAIL our resident team of qualified production engineers.
Mr Chen, Mr.Jiang - Email: lh.steel@hotmail.com
If you meet further on any technical enquiry. pleased to EMAIL our resident team of qualified production engineers.
Mr Chen, Mr.Jiang - Email: lh.steel@hotmail.com
PRODUCT PROFILE
Round bar / Wire rod (Diameter): 0.50mm to 800mm
Square bar / Flat bar: 3mm to 800mm
Length: Fixed length or random length or based on the customer's special requirement.
Round bar / Wire rod (Diameter): 0.50mm to 800mm
Square bar / Flat bar: 3mm to 800mm
Length: Fixed length or random length or based on the customer's special requirement.
Heavy/middle plate via hot rolled: T6 - 200mm X W1000- 2500mm X L1000-12000mm
Sheet steel via cold rolled: T0.5 - 6mm X W600- 1000mm X L1000 - 2000mm
Steel strip via cold rolled: T0.1 - 3mm X W5 - 200mm X L (or in coil form)
Forging piece: stepped shafts with flanks / discs /tubes /slugs /donuts /cubes /other different shapes based on OEM.
Pipes / Tubings: OD 3-219 mm, with wall thickness ranging from 0.50 to 35 mm.
Sheet steel via cold rolled: T0.5 - 6mm X W600- 1000mm X L1000 - 2000mm
Steel strip via cold rolled: T0.1 - 3mm X W5 - 200mm X L (or in coil form)
Forging piece: stepped shafts with flanks / discs /tubes /slugs /donuts /cubes /other different shapes based on OEM.
Pipes / Tubings: OD 3-219 mm, with wall thickness ranging from 0.50 to 35 mm.
Previous page：FV520B Martensitic Aging Steel
Last page：W-Nr 1.7259
Total list
Monthly rank
- 3438NCD4
- 3424CrMo5
- 3119CrNi5
- 2938B3
- 28ASTM A739 type B11
- 2826NiCrMoV11-5
- 2742Cr4Mo2
- 24S135
- 24EN 38
- 22EN20B