Material specification W-Nr 1.5225 datasheet,W-Nr 1.5225 Chemical, Ring forging,W-Nr 1.5225 Bar, Wire rod,DIN 1.5225 Sheet -steelmaking,ESR,Blooming,Forging,Rolling,Heat treatment, Straightened,
Ultrasonic test, Cold working, Machined. We also possess advanced precision machining equipments for further processing.
Technical Standards - DIN 17221 (1988) or by agreement.
OFFICIAL TEST CERTIFICATE: issued by TUV - SGS - BV
TECHNICAL SPECIFICATION / DATASHEET - DIN 51MnV7 / 1.5225
MATERIAL CATEGORY: Spring steel
MATERIAL SPECIFICATIONS: DIN 17221 (1988)
CHEMICAL COMPOSITION (WEIGHT %)
C(％): 0.48～0.55
Si(％): 0.15～0.35
Mn(％): 1.60～1.90
P(％)≤: 0.035
S(％)≤: 0.035
Cr(％): —
Mo(％): —
Other(％): V 0.07～0.12
Si(％): 0.15～0.35
Mn(％): 1.60～1.90
P(％)≤: 0.035
S(％)≤: 0.035
Cr(％): —
Mo(％): —
Other(％): V 0.07～0.12
MECHANICAL PROPERTIES UNDER ROOM TEMPERATURE
Dimension scope /mm|Flat bar: 12
Dimension scope /mm|Round bar: 20
≥|σb/MPa: 1230～1420
≥|σs/MPa: 1080
≥|δ5(%): 8
≥|ψ(%): 30
≥|AKV - DVM-V /J: 21
Dimension scope /mm|Round bar: 20
≥|σb/MPa: 1230～1420
≥|σs/MPa: 1080
≥|δ5(%): 8
≥|ψ(%): 30
≥|AKV - DVM-V /J: 21
HOT WORKING AND HEAT TREATMENT
Hot working temperature /℃: 1050～850
Thermal forming temperature /℃: 800～880
/℃|Annealed: 640～680
/℃|Normalized: 830～860
/℃|Quenched: 830～860 oil cooled
/℃|Tempered: 430～500
Annealed hardness ≤HBS: 230
Thermal forming temperature /℃: 800～880
/℃|Annealed: 640～680
/℃|Normalized: 830～860
/℃|Quenched: 830～860 oil cooled
/℃|Tempered: 430～500
Annealed hardness ≤HBS: 230
PRODUCT DESCRIPTION
The alloy is usually produced by LF /EAF /IFF /VD followed by electroslag refining (ESR) if necessary for special purpose.
Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied black/bright in the annealed condition.
Final heat treatment - solution treatment
The alloy is usually produced by LF /EAF /IFF /VD followed by electroslag refining (ESR) if necessary for special purpose.
Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied black/bright in the annealed condition.
Final heat treatment - solution treatment
TECHNICAL SALES ASSISTANCE
If you meet further on any technical enquiry. pleased to EMAIL our resident team of qualified production engineers.
Mr Chen, Mr.Jiang - Email: lh.steel@hotmail.com
If you meet further on any technical enquiry. pleased to EMAIL our resident team of qualified production engineers.
Mr Chen, Mr.Jiang - Email: lh.steel@hotmail.com
PRODUCT PROFILE
Round bar / Wire rod (Diameter1): 0.50mm to 800mm
Square bar / Flat bar: 3mm to 800mm
Length: Fixed length or random length or based on the customer's special requirement.
Round bar / Wire rod (Diameter1): 0.50mm to 800mm
Square bar / Flat bar: 3mm to 800mm
Length: Fixed length or random length or based on the customer's special requirement.
Heavy/middle plate via hot rolled: T6 - 200mm X W1000- 2500mm X L1000-12000mm
Sheet steel via cold rolled: T0.5 - 6mm X W600- 1000mm X L1000 - 2000mm
Steel strip via cold rolled: T0.1 - 3mm X W5 - 200mm X L (or in coil form)
Forging piece: stepped shafts with flanks / discs /tubes /slugs /donuts /cubes /other different shapes based on OEM.
Pipes / Tubings: OD 3-219 mm, with wall thickness ranging from 0.50 to 35 mm.
Sheet steel via cold rolled: T0.5 - 6mm X W600- 1000mm X L1000 - 2000mm
Steel strip via cold rolled: T0.1 - 3mm X W5 - 200mm X L (or in coil form)
Forging piece: stepped shafts with flanks / discs /tubes /slugs /donuts /cubes /other different shapes based on OEM.
Pipes / Tubings: OD 3-219 mm, with wall thickness ranging from 0.50 to 35 mm.