1.7102
2015-03-31 10:03:40 Origin： Remark：0 Click：
Description 1.7102 Inventory, Suppliers 1.7102 Ex-stock, Forgings 1.7102 Bars Steelmaking, ESR, Blooming, Forging, Rolling, Heat treatment, Straightened, Ultrasonic test, Cold working, Machined. We also possess advanced precision machining equipments for further processing.
Technical Standards - DIN 17221 (1988) or by agreement.
OFFICIAL TEST CERTIFICATE: issued by TUV - SGS - BV
MATERIAL TECHNICAL DATASHEET - Grade 1.7102
MATERIAL CATEGORY: Spring steel
MATERIAL SPECIFICATIONS: DIN 17221 (1988)
CHEMICAL COMPOSITION (Mass weight - %)
C (％): 0.51～0.59
Si (％): 1.20～1.60
Mn (％): 0.50～0.80
P (％)≤: 0.030
S (％)≤: 0.030
Cr (％): 0.50～0.80
Mo (％):
Si (％): 1.20～1.60
Mn (％): 0.50～0.80
P (％)≤: 0.030
S (％)≤: 0.030
Cr (％): 0.50～0.80
Mo (％):
MECHANICAL PROPERTIES UNDER ROOM TEMPERATURE
Dimension scope /mm|Flat bar: 12
Dimension scope /mm|Round bar: -
≥|σb/MPa: 1350～1600
≥|σs/MPa: 1150
≥|δ5(%): 6.0
≥|ψ(%): 25.0
≥|AKV - DVM-V /J: 14
Dimension scope /mm|Round bar: -
≥|σb/MPa: 1350～1600
≥|σs/MPa: 1150
≥|δ5(%): 6.0
≥|ψ(%): 25.0
≥|AKV - DVM-V /J: 14
HOT WORKING AND HEAT TREATMENT
Hot working temperature /℃: 1050～850
Thermal forming temperature /℃: 900～830
/℃|Annealed: 640～680
/℃|Normalized: 850～880
/℃|Quenched: 840～870 oil cooled
/℃|Tempered: 430～500
Annealed hardness ≤HBS: 255
Thermal forming temperature /℃: 900～830
/℃|Annealed: 640～680
/℃|Normalized: 850～880
/℃|Quenched: 840～870 oil cooled
/℃|Tempered: 430～500
Annealed hardness ≤HBS: 255
PRODUCT PROFILE
Round bar / Wire rod (Diameter1): 0.50mm to 800mm
Square bar / Flat bar: 3mm to 800mm
Length: Fixed length or random length or based on the customer's special requirement.
Round bar / Wire rod (Diameter1): 0.50mm to 800mm
Square bar / Flat bar: 3mm to 800mm
Length: Fixed length or random length or based on the customer's special requirement.
Heavy/middle plate via hot rolled: T6 - 200mm X W1000- 2500mm X L1000-12000mm
Sheet steel via cold rolled: T0.5 - 6mm X W600- 1000mm X L1000 - 2000mm
Steel strip via cold rolled: T0.1 - 3mm X W5 - 200mm X L (or in coil form)
Forging piece: stepped shafts with flanks / discs /tubes /slugs /donuts /cubes /other different shapes based on OEM.
Sheet steel via cold rolled: T0.5 - 6mm X W600- 1000mm X L1000 - 2000mm
Steel strip via cold rolled: T0.1 - 3mm X W5 - 200mm X L (or in coil form)
Forging piece: stepped shafts with flanks / discs /tubes /slugs /donuts /cubes /other different shapes based on OEM.
PRODUCT DESCRIPTION
The alloy is usually produced by EAF /IFF /VD followed by electroslag refining (ESR) if necessary for special purpose.
Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied black/bright in the annealed condition.
Final heat treatment - solution treatment
The alloy is usually produced by EAF /IFF /VD followed by electroslag refining (ESR) if necessary for special purpose.
Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied black/bright in the annealed condition.
Final heat treatment - solution treatment
TECHNICAL SALES ASSISTANCE
If you meet further on any technical enquiry or help, pleased to EMAIL our resident team of qualified production engineers, Email:sales@ccsteels.com.
If you meet further on any technical enquiry or help, pleased to EMAIL our resident team of qualified production engineers, Email:sales@ccsteels.com.
Hot search：1.7102
Total list
Monthly rank
- 3438NCD4
- 3424CrMo5
- 3119CrNi5
- 2938B3
- 28ASTM A739 type B11
- 2826NiCrMoV11-5
- 2742Cr4Mo2
- 24S135
- 24EN 38
- 22EN20B