1.7176
2015-04-01 08:59:55 Origin： Remark：0 Click：
Specification 1.7176 Datasheet, Inventory 1.7176 Chemical, Ring forging 1.7176 ESR, Blooming, Forging, Rolling, Heat treatment, Straightened, Ultrasonic test, Cold working, Machined. We also possess advanced precision machining equipments for further processing.
Technical Standards - DIN 17221 (1988) or by agreement.
OFFICIAL TEST CERTIFICATE: issued by TUV - SGS - BV
TECHNICAL SPECIFICATION DATASHEET - 1.7176
MATERIAL CATEGORY - Spring steel
MATERIAL SPECIFICATIONS - DIN 17221 (1988)
CHEMICAL COMPOSITION (WEIGHT %)
C (％): 0.52～0.59
Si (％): 0.25～0.50
Mn (％): 0.70～1.00
P (％)≤: 0.030
S (％)≤: 0.030
Cr (％): 0.70～1.00
Mo (％): —
Si (％): 0.25～0.50
Mn (％): 0.70～1.00
P (％)≤: 0.030
S (％)≤: 0.030
Cr (％): 0.70～1.00
Mo (％): —
Other (％): -
MECHANICAL PROPERTIES UNDER ROOM TEMPERATURE
Dimension scope /mm|Flat bar: 20
Dimension scope /mm|Round bar: 40
≥|σb/MPa: 1320～1720
≥|σs/MPa: 1175
≥|δ5(%): 6.0
≥|ψ(%): 30
≥|AKV - DVM-V /J: -
Dimension scope /mm|Round bar: 40
≥|σb/MPa: 1320～1720
≥|σs/MPa: 1175
≥|δ5(%): 6.0
≥|ψ(%): 30
≥|AKV - DVM-V /J: -
HOT WORKING AND HEAT TREATMENT
Hot working temperature /℃: 1050～850
Thermal forming temperature /℃: 920～830
/℃|Annealed: 640～680
/℃|Normalized: 850～880
/℃|Quenched: 830～860 oil cooled
/℃|Tempered: 350～550
Annealed hardness ≤HBS: 250
Thermal forming temperature /℃: 920～830
/℃|Annealed: 640～680
/℃|Normalized: 850～880
/℃|Quenched: 830～860 oil cooled
/℃|Tempered: 350～550
Annealed hardness ≤HBS: 250
PROFILE & DIMENSIONS
Round bar / Wire rod (Diameter1): 5.5mm to 650mm
Square bar / Flat bar: 3mm to 800mm
Length: Fixed length or random length or based on the customer's special requirement.
Round bar / Wire rod (Diameter1): 5.5mm to 650mm
Square bar / Flat bar: 3mm to 800mm
Length: Fixed length or random length or based on the customer's special requirement.
Heavy/middle plate via hot rolled: T60 - 400mm X W50 - 1300mm X L1000 - 5000mm
Sheet steel via cold rolled: T0.5 - 6mm X W100 - 1000mm X L1000 - 2000mm
Steel strip via cold rolled: T0.1 - 3mm X W5 - 200mm X L (or in coil form)
Forging piece: stepped shafts with flanks / discs /tubes /slugs /donuts /cubes /other different shapes based on OEM.
Sheet steel via cold rolled: T0.5 - 6mm X W100 - 1000mm X L1000 - 2000mm
Steel strip via cold rolled: T0.1 - 3mm X W5 - 200mm X L (or in coil form)
Forging piece: stepped shafts with flanks / discs /tubes /slugs /donuts /cubes /other different shapes based on OEM.
PRODUCT DESCRIPTION
The alloy is usually produced by LF /EAF / VD followed by electroslag refining (ESR) if necessary for special purpose.
Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied black/bright in the annealed condition.
Final heat treatment - Q + T treated
The alloy is usually produced by LF /EAF / VD followed by electroslag refining (ESR) if necessary for special purpose.
Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied black/bright in the annealed condition.
Final heat treatment - Q + T treated
TECHNICAL SALES ASSISTANCE
If you meet further on any technical enquiry, pleased to EMAIL our resident team of qualified production engineers, E-mail: sales@ccsteels.com.
If you meet further on any technical enquiry, pleased to EMAIL our resident team of qualified production engineers, E-mail: sales@ccsteels.com.
Hot search：1.7176
Total list
Monthly rank
- 3438NCD4
- 3424CrMo5
- 3119CrNi5
- 2938B3
- 28ASTM A739 type B11
- 2826NiCrMoV11-5
- 2742Cr4Mo2
- 24S135
- 24EN 38
- 22EN20B