DIN 50CrV4
2015-04-02 09:02:16 Origin： Remark：0 Click：
Description 50CrV4 Round bar, Inventory 50CrV4 Suppliers, Hexagon 50CrV4 Bar, Wire rod, Sheet - steelmaking, ESR, Blooming, Hot forging, Rolling, Heat treatment, Straightened, Ultrasonic test, Cold working, Machined. We also possess advanced precision machining equipments for further processing.
Technical Standards - DIN 17221 (1988) or by agreement.
OFFICIAL TEST CERTIFICATE: issued by TUV - SGS - BV
TECHNICAL SPECIFICATION DATASHEET - Grade DIN 50CrV4
MATERIAL CATEGORY: Spring steel
MATERIAL SPECIFICATIONS: DIN 17221 (1988)
CHEMICAL COMPOSITION (Mass weight - %)
C (％): 0.47 ~ 0.55
Si (％): ≤ 0.40
Mn (％): 0.70 ~ 1.10
P (％)≤: 0.035
S (％)≤: 0.035
Cr (％): 0.90 ~ 1.20
Mo (％): -
Si (％): ≤ 0.40
Mn (％): 0.70 ~ 1.10
P (％)≤: 0.035
S (％)≤: 0.035
Cr (％): 0.90 ~ 1.20
Mo (％): -
V (％): 0.10 ~ 0.25
MECHANICAL PROPERTIES UNDER ROOM TEMPERATURE
Dimension scope /mm|Flat bar: 25
Dimension scope /mm|Round bar: 40
Tensile strength, ≥|σb/MPa: 1370～1620
Yield strength, ≥|σs/MPa: 1175
Elongation. ≥| δ5 (%): 6.0
Reduction of area, ≥|ψ(%): 40.0
Impact strength, ≥ |AKV - DVM-V /J: 21
Dimension scope /mm|Round bar: 40
Tensile strength, ≥|σb/MPa: 1370～1620
Yield strength, ≥|σs/MPa: 1175
Elongation. ≥| δ5 (%): 6.0
Reduction of area, ≥|ψ(%): 40.0
Impact strength, ≥ |AKV - DVM-V /J: 21
PRODUCT PROFILE
Round bar / Wire rod (Diameter1): 0.50mm to 800mm
Square bar / Flat bar: 3mm to 800mm
Length: Fixed length or random length or based on the customer's special requirement.
Round bar / Wire rod (Diameter1): 0.50mm to 800mm
Square bar / Flat bar: 3mm to 800mm
Length: Fixed length or random length or based on the customer's special requirement.
Heavy/middle plate via hot rolled: T6 - 200mm X W1000- 2500mm X L1000-12000mm
Sheet steel via cold rolled: T0.5 - 6mm X W600- 1000mm X L1000 - 2000mm
Steel strip via cold rolled: T0.1 - 3mm X W5 - 200mm X L (or in coil form)
Forging piece: stepped shafts with flanks / discs /tubes /slugs /donuts /cubes /other different shapes based on OEM.
Sheet steel via cold rolled: T0.5 - 6mm X W600- 1000mm X L1000 - 2000mm
Steel strip via cold rolled: T0.1 - 3mm X W5 - 200mm X L (or in coil form)
Forging piece: stepped shafts with flanks / discs /tubes /slugs /donuts /cubes /other different shapes based on OEM.
HOT WORKING AND HEAT TREATMENT
Hot working temperature /℃: 1050～850
Thermal forming temperature /℃: 920～830
/℃|Annealed: 640～680
/℃|Normalized: 850~880
/℃|Quenched: 830～860 oil cooled
/℃|Tempered: 350～550
Annealed hardness ≤HBS: 248
Thermal forming temperature /℃: 920～830
/℃|Annealed: 640～680
/℃|Normalized: 850~880
/℃|Quenched: 830～860 oil cooled
/℃|Tempered: 350～550
Annealed hardness ≤HBS: 248
PRODUCT DESCRIPTION
The alloy is usually produced by LF /EAF /IFF /VD followed by electroslag refining (ESR) if necessary for special purpose.
Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied black/bright in the annealed condition.
Final heat treatment - solution treatment
The alloy is usually produced by LF /EAF /IFF /VD followed by electroslag refining (ESR) if necessary for special purpose.
Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied black/bright in the annealed condition.
Final heat treatment - solution treatment
TECHNICAL SALES ASSISTANCE & SERVICE
If you meet further on any technical enquiry or help, pleased to EMAIL our resident team of qualified production engineers, Email: sales@ccsteels.com.
If you meet further on any technical enquiry or help, pleased to EMAIL our resident team of qualified production engineers, Email: sales@ccsteels.com.
Previous page：1.8159
Last page：DIN 58CrV4
Total list
Monthly rank
- 3438NCD4
- 3424CrMo5
- 3119CrNi5
- 2938B3
- 28ASTM A739 type B11
- 2826NiCrMoV11-5
- 2742Cr4Mo2
- 24S135
- 24EN 38
- 22EN20B