C101E / CK101
2015-11-19 11:23:35 Origin： Remark：0 Click：
Description C101E Suppliers, Round bar Ck101 Inventory, Ex-stock C101E Properties Steelmaking, ESR melted, Blooming, Hot forging, Hot rolling, Heat treated, Straightening, 100% Ultrasonic test, Cold working or Machined. Technical specification - DIN 17221. We also possess the advanced precision machining equipments for further processing. Please just let us know what you inquire.
Official Test Certificate: issued by TUV - SGS - BV
TECHNICAL SPECIFICATION DATASHEET - Grade DIN C101E / Ck101 / 1.1274
MATERIAL TYPE: Spring Steel
MATERIAL STANDARDS: DIN 17221
CHEMICAL COMPOSITION (Mass weight - %)
C (％): 0.95 ~ 1.05
Si (％): 0.15 ~ 0.35
Mn (％): 0.30 ~ 0.60
P (％)≤: 0.025
S (％)≤: 0.025
P (％)≤: 0.025
S (％)≤: 0.025
Cr (%): ≤ 0.40
Mo (%): ≤ 0.10
V (%): -
Other(％): Ni ≤0.40
MECHANICAL PROPERTIES UNDER ROOM TEMP.
Range of size/mm|flat bar: -
Range of size/mm|round bar: -
Mechanical property ≥|σb/MPa: 1470～1670
Mechanical property ≥|σs/MPa: 1275
Mechanical property ≥|δ5(%): 6
Mechanical property ≥|ψ(%): 20
Mechanical property ≥|Akv /J: —
Range of size/mm|round bar: -
Mechanical property ≥|σb/MPa: 1470～1670
Mechanical property ≥|σs/MPa: 1275
Mechanical property ≥|δ5(%): 6
Mechanical property ≥|ψ(%): 20
Mechanical property ≥|Akv /J: —
HOT WORKING & HEAT TREATMENT
Hot working temperature /℃: 1050~850
Thermal forming temperature /℃: 880~800
Heat treatment temperature/℃|annealing /℃: 640～680
Heat treatment temperature/℃|normalizing /℃: 800~830
Heat treatment temperature/℃|quenching /℃: 780～810 oil
Heat treatment temperature/℃|tempering /℃: 430～500
Hardness after annealing ≤HBW: 220
Thermal forming temperature /℃: 880~800
Heat treatment temperature/℃|annealing /℃: 640～680
Heat treatment temperature/℃|normalizing /℃: 800~830
Heat treatment temperature/℃|quenching /℃: 780～810 oil
Heat treatment temperature/℃|tempering /℃: 430～500
Hardness after annealing ≤HBW: 220
MAIN FEATURES & PERFORMANCE REQUIREMENTS
Spring steel is specialized in producing the spring and elastic components due to its elasticity under the condition of quenching and tempering. The elasticity of steel depends on its capacity of elastic deformation.
This allows objects made of spring steel to return to their original shape despite significant bending or twisting occurs.
Spriing steel should possess excellent combination property, such as mechanical property (limit of elasticity, ultimate strength, yield ratio), relaxation resistant, fatigue property, hardenability, physical and chemical property (heat resistance,low temperature resistant, antioxidation, corrosion resistance). To meet the above performance requirement, Spring steel has fine metallurgical quality ( high purity, homogeneity), excellent surface quality ( specially on surface defect and decarburization), precise external form and dimensions.
HEAT TREATMENT
Spring Steel requires higher strength and fatigue limit, usage in the condition of quenching + mesothermal tempering, then it can get higher elastic limit. Process engineering of heat treatment is very important to inherent quality of spring steel.
MANUFACTURING TECHNIQUE
General spring steels are produced in electric furnace, open hearth furnace, oxygen converter,and high quality spring steel of higher quality or special performance can be made in electro slag furnace or vacuum furnace.
PROCESSING PROPERTY
Spring Steel is commonly used in the condition of impact, vibration, or long-term stress. which makes the spring steel require higher tensile strength, limit of elasticity, fatigue strength. also requirement of definite hardenability, good surface quality, not easy decarburization.
PRODUCT PROFILE & DIMENSION
Round bar / Wire rod (Diameter): 5.5mm to 800mm
Square bar / Flat bar: 3mm to 800mm
Length: Fixed length or random length or based on the customer's special requirement.
Round bar / Wire rod (Diameter): 5.5mm to 800mm
Square bar / Flat bar: 3mm to 800mm
Length: Fixed length or random length or based on the customer's special requirement.
Heavy/middle plate via hot rolled: T6 - 200mm X W10 - 1500mm X L1000-12000mm
Forging piece: stepped shafts with flanks / discs /tubes /slugs /donuts /cubes /other different shapes based on OEM.
Forging piece: stepped shafts with flanks / discs /tubes /slugs /donuts /cubes /other different shapes based on OEM.
TECHNICAL SALES ASSISTANCE
If you meet further on any technical enquiry or help, pleased to EMAIL our resident team of qualified production engineers, Email:sales@ccsteels.com.
If you meet further on any technical enquiry or help, pleased to EMAIL our resident team of qualified production engineers, Email:sales@ccsteels.com.
Previous page：C85E /Ck85 /1.1269
Last page：38Si6
Total list
Monthly rank
- 3438NCD4
- 3424CrMo5
- 3119CrNi5
- 2938B3
- 28ASTM A739 type B11
- 2826NiCrMoV11-5
- 2742Cr4Mo2
- 24S135
- 24EN 38
- 22EN20B