Technical specifications of German standards high temperature alloy steel DIN X20CrMoV12-1 datasheet,X20CrMoV12-1 Chemical compositions,mechanical properties from Steelmaking, ESR melted, Blooming, Hot forging, Hot rolling, Heat treatment, Straightening, 100% Ultrasonic test, Cold working or Machined. Technical specification -DIN 10028-2.We also possess the advanced precision machining equipments for further processing.
TECHNICAL DATA SHEET - X20CrMoV12-1 & 1.4922
Official Test Certificate: issued by TUV - SGS - BV
MATERIAL TYPE: High temperature alloy steel MATERIAL STANDARDS: DIN EN 10028-2, DIN 17755
CHEMICAL COMPOSITION (WEIGHT %)
C (％): 0.17 ~ 0.23
Si (％): ≤ 0.50
Mn (％): ≤ 1.00
P (％)≤: 0.030
S (％)≤: 0.030
Cr (%): 10.0 ~ 12.5
Ni (%): 0.30 ~ 0.80
Mo (%): 0.80 ~ 1.20
Other(％): V 0.25 ~ 0.35
MECHANICAL PROPERTIES
Mo (%): 0.80 ~ 1.20
Other(％): V 0.25 ~ 0.35
MECHANICAL PROPERTIES
Mechanical property ≥|σb/MPa: 690～830
Mechanical property ≥|σs/MPa: 490
Mechanical property ≥|δ5(%): 16
Mechanical property ≥|Akv /J: 41
Mechanical property ≥|σs/MPa: 490
Mechanical property ≥|δ5(%): 16
Mechanical property ≥|Akv /J: 41
Hardness after annealed HBW: 205~250
HOT WORKING & HEAT TREATMENT
Hot working temperature /℃: 1100~850
Heat treatment temperature/℃|annealing /℃: 700～780
Heat treatment temperature/℃|quenching /℃: 1020～1070 Oil or Air cooled
Heat treatment temperature/℃|tempering /℃: 700～760
HOT WORKING & HEAT TREATMENT
Hot working temperature /℃: 1100~850
Heat treatment temperature/℃|annealing /℃: 700～780
Heat treatment temperature/℃|quenching /℃: 1020～1070 Oil or Air cooled
Heat treatment temperature/℃|tempering /℃: 700～760
PRODUCT DESCRIPTION
High room and elevated temperature strength.Good creep.
High notch tolerance.
Thermal expansion coefficients compatible with low alloy steel turbine casing materials.
Lower design and operating risks
Simplified design for bolting configuration compared with martensitic steels or high nickel alloys.
High room and elevated temperature strength.Good creep.
High notch tolerance.
Thermal expansion coefficients compatible with low alloy steel turbine casing materials.
Lower design and operating risks
Simplified design for bolting configuration compared with martensitic steels or high nickel alloys.
Proven performance in long-term service.
Extensive database of long term, high temperature test results.
Extensive database of long term, high temperature test results.
Alloy structural steel is provided with higher yield strength, tensile strength, endurance strength, yield ratio (about 0.85 generally ) enough plasticity and toughness.
The concentration of alloy element of this kind of steel is quite high, mainly are corrosion resistant steel, heat resistant steel, wear resistant steel, and other special steels of physical and chemical properties. Alloy structural steel has preferable mechanical property than that of carbon structural steel, high performance of heat treatment especially.
The alloy is usually produced by EAF /VD /LF followed by electroslag refining (ESR) if necessary for special purpose.
Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different level according to the buyers' requirements.
Bars are usually supplied bright in the annealed condition, or bright annealing specially.
Final heat treatment - heat treatment / QT
The concentration of alloy element of this kind of steel is quite high, mainly are corrosion resistant steel, heat resistant steel, wear resistant steel, and other special steels of physical and chemical properties. Alloy structural steel has preferable mechanical property than that of carbon structural steel, high performance of heat treatment especially.
The alloy is usually produced by EAF /VD /LF followed by electroslag refining (ESR) if necessary for special purpose.
Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different level according to the buyers' requirements.
Bars are usually supplied bright in the annealed condition, or bright annealing specially.
Final heat treatment - heat treatment / QT
TYPICAL APPLICATIONS
Alloy structural steels are widely used in the filed of ship, vehicle, airplane, guided missile, weapons, railway, bridges, pressure vessel, machine tools, mechanical components with a bigger sectional size and so on.
Power generation – turbine fasteners – boiler support rods
Process plant – fasteners
Mechanical gears, gear shaft, main axis, valve rod
Mechanical parts - connecting rod, bolt and nut
Multidiameter shaft
Pressure vessel, seamless pipe
Alloy structural steels are widely used in the filed of ship, vehicle, airplane, guided missile, weapons, railway, bridges, pressure vessel, machine tools, mechanical components with a bigger sectional size and so on.
Power generation – turbine fasteners – boiler support rods
Process plant – fasteners
Mechanical gears, gear shaft, main axis, valve rod
Mechanical parts - connecting rod, bolt and nut
Multidiameter shaft
Pressure vessel, seamless pipe
PRODUCT PROFILE
Round bar / Wire rod (Diameter): 0.50mm to 800mm
Square bar / Flat bar: 3mm to 800mm
Length: Fixed length or random length or based on the customer's special requirement.
Heavy/middle plate via hot rolled: T6 - 200mm X W1000- 2500mm X L1000-12000mm
Forging piece: stepped shafts with flanks / discs /tubes /slugs /donuts /cubes /other different shapes based on OEM.
Round bar / Wire rod (Diameter): 0.50mm to 800mm
Square bar / Flat bar: 3mm to 800mm
Length: Fixed length or random length or based on the customer's special requirement.
Heavy/middle plate via hot rolled: T6 - 200mm X W1000- 2500mm X L1000-12000mm
Forging piece: stepped shafts with flanks / discs /tubes /slugs /donuts /cubes /other different shapes based on OEM.
TECHNICAL SALES ASSISTANCE
If you meet further on any technical enquiry. pleased to EMAIL our resident team of qualified production engineer. - Email: lh.steel@hotmail.com
Hot search：X20CrMoV12-1 /1.4922
Previous page：21CrMoV5-11 / 1.8070
Last page：20MnMoNi4-5 / 1.6311
Total list
Monthly rank
- 3438NCD4
- 3424CrMo5
- 3119CrNi5
- 2938B3
- 28ASTM A739 type B11
- 2826NiCrMoV11-5
- 2742Cr4Mo2
- 24S135
- 24EN 38
- 22EN20B