DIN EN 10028-2 High Temperature Steel 17MnMoV6-4 Round bar, Ex-stock 17MnMoV6-4 ESR melted, 1.5403 Hot forging, Hot rolling, Heat treatment,
Official Test Certificate: issued by TUV - SGS - BV
TECHNICAL DATA SHEET - 17MnMoV6-4 & 1.5403
MATERIAL TYPE: High temperature alloy steel
MATERIAL STANDARDS: DIN EN 10028-2, DIN 17755
CHEMICAL COMPOSITION (mass weight - %)
Carbon, C (%): ≤ 0.19
Silicon, Si (%): 0.20 ~ 0.50
Manganese, Mn (%): 1.40 ~ 1.70
Phosphorus, P (%) ≤: 0.035
Sulfur, S (%) ≤: 0.035
Chromium, Cr (%): -
Nickel, Ni (%): ≤ 1.00
Molybdenum, Mo (%): 0.20 ~ 0.50
Other(%): Vanadium ≤ 0.19, Nitrogen ≤ 0.020
MECHANICAL PROPERTIES UNDER ROOM TEMP.
Molybdenum, Mo (%): 0.20 ~ 0.50
Other(%): Vanadium ≤ 0.19, Nitrogen ≤ 0.020
MECHANICAL PROPERTIES UNDER ROOM TEMP.
Mechanical property ≥|σb/MPa: 570~740
Mechanical property ≥|σs/MPa: 410
Mechanical property ≥|δ5(%): 16.0
Mechanical property ≥|Akv /J: 31
Mechanical property ≥|σs/MPa: 410
Mechanical property ≥|δ5(%): 16.0
Mechanical property ≥|Akv /J: 31
Hardness after annealed HBW: -
HOT WORKING & HEAT TREATMENT
Hot working temperature /℃: 1100~850
Heat treatment temperature/℃|annealing /℃: 880~940
Heat treatment temperature/℃|quenching /℃: -
Heat treatment temperature/℃|tempering /℃: 610~690
HOT WORKING & HEAT TREATMENT
Hot working temperature /℃: 1100~850
Heat treatment temperature/℃|annealing /℃: 880~940
Heat treatment temperature/℃|quenching /℃: -
Heat treatment temperature/℃|tempering /℃: 610~690
PRODUCT DESCRIPTION
High room and elevated temperature strength.Good creep.
High notch tolerance.
Thermal expansion coefficients compatible with low alloy steel turbine casing materials.
Lower design and operating risks
Simplified design for bolting configuration compared with martensitic steels or high nickel alloys.
High room and elevated temperature strength.Good creep.
High notch tolerance.
Thermal expansion coefficients compatible with low alloy steel turbine casing materials.
Lower design and operating risks
Simplified design for bolting configuration compared with martensitic steels or high nickel alloys.
Proven performance in long-term service.
Extensive database of long term, high temperature test results.
Extensive database of long term, high temperature test results.
Alloy structural steel is provided with higher yield strength, tensile strength, endurance strength, yield ratio (about 0.85 generally ) enough plasticity and toughness.
The concentration of alloy element of this kind of steel is quite high, mainly are corrosion resistant steel, heat resistant steel, wear resistant steel, and other special steels of physical and chemical properties. Alloy structural steel has preferable mechanical property than that of carbon structural steel, high performance of heat treatment especially.
The alloy is usually produced by EAF /VD /LF followed by electroslag refining (ESR) if necessary for special purpose. Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different level according to the buyers' requirements.
Bars are usually supplied bright in the annealed condition, or bright annealing specially.
Final heat treatment - heat treatment / QT
The concentration of alloy element of this kind of steel is quite high, mainly are corrosion resistant steel, heat resistant steel, wear resistant steel, and other special steels of physical and chemical properties. Alloy structural steel has preferable mechanical property than that of carbon structural steel, high performance of heat treatment especially.
The alloy is usually produced by EAF /VD /LF followed by electroslag refining (ESR) if necessary for special purpose. Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different level according to the buyers' requirements.
Bars are usually supplied bright in the annealed condition, or bright annealing specially.
Final heat treatment - heat treatment / QT
TYPICAL APPLICATIONS
Alloy structural steels are widely used in the filed of ship, vehicle, airplane, guided missile, weapons, railway, bridges, pressure vessel, machine tools, mechanical components with a bigger sectional size and so on.
Power generation – turbine fasteners – boiler support rods.
Process plant – fasteners.
Mechanical gears, gear shaft, main axis, valve rod.
Mechanical parts - connecting rod, bolt and nut.
Multidiameter shaft, Pressure vessel.
Alloy structural steels are widely used in the filed of ship, vehicle, airplane, guided missile, weapons, railway, bridges, pressure vessel, machine tools, mechanical components with a bigger sectional size and so on.
Power generation – turbine fasteners – boiler support rods.
Process plant – fasteners.
Mechanical gears, gear shaft, main axis, valve rod.
Mechanical parts - connecting rod, bolt and nut.
Multidiameter shaft, Pressure vessel.
PROFILE & DIMENSIONS
Round bar / Wire rod (Diameter): 5.5mm to 800mm
Square bar / Flat bar: 3mm to 800mm
Length: Fixed length or random length or based on the customer's special requirement.
Heavy/middle plate via hot rolled: T6 - 200mm X W10 - 1500mm X L1000-12000mm
Forging piece: stepped shafts, and other different shapes based on OEM.
Round bar / Wire rod (Diameter): 5.5mm to 800mm
Square bar / Flat bar: 3mm to 800mm
Length: Fixed length or random length or based on the customer's special requirement.
Heavy/middle plate via hot rolled: T6 - 200mm X W10 - 1500mm X L1000-12000mm
Forging piece: stepped shafts, and other different shapes based on OEM.
TECHNICAL SALES ASSISTANCE
If you meet further on any technical enquiry or help, pleased to EMAIL (sales@ccsteels.com) our resident team of qualified production engineers.
If you meet further on any technical enquiry or help, pleased to EMAIL (sales@ccsteels.com) our resident team of qualified production engineers.
Hot search:17MnMoV6-4 /1.5403
Previous page:20MnMoNi4-5 / 1.6311
Last page:20NiCrMoS2-2
Total list
Monthly rank
- 3438NCD4
- 3424CrMo5
- 3119CrNi5
- 2938B3
- 28ASTM A739 type B11
- 2826NiCrMoV11-5
- 2742Cr4Mo2
- 24S135
- 24EN 38
- 22EN20B