P235GH
2014-09-11 10:42:08 Origin: Remark:0 Click:
DIN EN 10028-2 of High temperature Steel P235GH Round bar, Plate, P235GH Forging Bar Technical specifications Melting, ESR & VAR technique
DIN P235GH - MATERIAL DATA SHEET
MATERIAL CATEGORY - High temperature structural steel
TYPICAL APPLICATIONS
Mechanical gears, gear shaft, main axis, valve rod.
Mechanical parts - connecting rod, bolt and nut.
Multidiameter shaft. Pressure vessel.
PRODUCT DESCRIPTION
The alloy is usually produced by EAF /VD /LF followed by electroslag refining (ESR) if necessary for special purpose. Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different level according to the buyers' requirements.
Bars are usually supplied bright in the softened condition.
Final heat treatment - heat treatment / QT
MATERIAL SPECIFICATIONS - DIN EN 10028-2 (2003), DIN 17755 (1983)
CHEMICAL COMPOSITION (mass weight - %)
Carbon, C (%): ≤ 0.16
Silicon, Si (%): ≤ 0.35
Manganese, Mn (%): 0.40 ~ 1.20
Phsphorus, P (%)≤: 0.030
Sulfur, S (%)≤: 0.025
Chromium, Cr (%): ≤ 0.30
Molybdenum, Mo (%): ≤ 0.08
Nickel, Ni (%): ≤ 0.30
Other (%): Cu ≤0.30;Al ≤0.020;Nb ≤0.01;Ti ≤0.03;V ≤0.02
Silicon, Si (%): ≤ 0.35
Manganese, Mn (%): 0.40 ~ 1.20
Phsphorus, P (%)≤: 0.030
Sulfur, S (%)≤: 0.025
Chromium, Cr (%): ≤ 0.30
Molybdenum, Mo (%): ≤ 0.08
Nickel, Ni (%): ≤ 0.30
Other (%): Cu ≤0.30;Al ≤0.020;Nb ≤0.01;Ti ≤0.03;V ≤0.02
MECHANICAL PROPERTIES - HOT WORKING, HEAT TREATMENT AND HARDNESS
Hot working temperature /℃: 1100~850
Heat treatment temperature /℃|annealing / normalizing : 890~950
Heat treatment temperature /℃|quenching: —
Heat treatment temperature /℃|tempering: —
HBS: 105~140
(≥)|σb/MPa: 350~480
(≥)|σs/MPa: 215
(≥)|δ5(%): 25
(≥)|AKV/J: 47
Heat treatment temperature /℃|annealing / normalizing : 890~950
Heat treatment temperature /℃|quenching: —
Heat treatment temperature /℃|tempering: —
HBS: 105~140
(≥)|σb/MPa: 350~480
(≥)|σs/MPa: 215
(≥)|δ5(%): 25
(≥)|AKV/J: 47
MECHANICAL PROPERTY UNDER HIGH TEMPERATURE
Yield strength σ0.2≥/MPa|200℃: 170
Yield strength σ0.2≥/MPa|300℃: 130
Yield strength σ0.2≥/MPa|350℃: 120
Yield strength σ0.2≥/MPa|400℃: 110
Yield strength σ0.2≥/MPa|450℃: 95
Yield strength σ0.2≥/MPa|500℃: —
Yield strength σ0.2≥/MPa|300℃: 130
Yield strength σ0.2≥/MPa|350℃: 120
Yield strength σ0.2≥/MPa|400℃: 110
Yield strength σ0.2≥/MPa|450℃: 95
Yield strength σ0.2≥/MPa|500℃: —
TECHNICAL SALES ASSISTANCE
If you meet further on any technical enquiry. pleased to email or call our resident team of qualified production engineers. Email: sales@ccsteels.com
PRODUCT PROFILE
Round bar (diameter): 5.5mm to 500mm
Square bar / flat bar: 10mm to 1000mm
Plate / Sheet steel / Steel strip: 0.1mm to 1000mm
Width: 8mm to 1000mm
Length: random length or based on the customer's special requirement.
Forged steel shape: stepped shafts, other different shapes based on OEM.
Pipes / Tubings: OD 3-219 mm, with wall thickness ranging from 0.50 to 35 mm.
Hot search:P235GH
Total list
Monthly rank
- 3438NCD4
- 3424CrMo5
- 3119CrNi5
- 2938B3
- 28ASTM A739 type B11
- 2826NiCrMoV11-5
- 2742Cr4Mo2
- 24S135
- 24EN 38
- 22EN20B