1.0460 Steels Ex-stock, Alloy 1.0460 Suppliers, Properties 1.0460 Forging Bar Plate,Grade 1.0460 Technical specifications Melting, ESR & VAR technique, Blooming, Hot forging, Hot rolling, Heat treatment, Straightening, Ultrasonic flaw detection test.
W-Nr 1.0460 - MATERIAL DATA SHEET
MATERIAL CATEGORY - High temperature structural steel
TYPICAL APPLICATIONS
Mechanical gears, gear shaft, main axis, valve rod
Mechanical parts - connecting rod, bolt and nut
Multidiameter shaft
Pressure vessel, seamless pipe
PRODUCT DESCRIPTION
The alloy is usually produced by EAF /VD /LF followed by electroslag refining (ESR) if necessary for special purpose.
Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different level according to the buyers' requirements.
Bars are usually supplied bright in the softened condition.
Final heat treatment - heat treatment / QT
MATERIAL SPECIFICATIONS - DIN EN 10028-2 (2003), DIN 17755 (1983)
AVAILABLE SHAPES
Round bar / flat bar / hollow bar / plate
Bright - peeled + polishing, centerless grinding
Forged - ring, tube, pipe casing, discs, shaft
Alloy structural steels are widely used in the filed of ship, vehicle, airplane, guided missile, weapons, railway, bridges, pressure vessel, machine tools, mechanical components with a bigger sectional size and so on.
CHEMICAL COMPOSITION (WEIGHT %)
C (％): 0.18 ~ 0.23
Si (％): ≤ 0.40
Mn (％): 0.30 ~ 0.90
P (％)≤: 0.025
S (％)≤: 0.015
Cr (％): -
Mo (％): -
Ni (％): -
Other(％): Cu ≤0.30；Al ≤0.020；Nb ≤0.01；Ti ≤0.03；V ≤0.02
Si (％): ≤ 0.40
Mn (％): 0.30 ~ 0.90
P (％)≤: 0.025
S (％)≤: 0.015
Cr (％): -
Mo (％): -
Ni (％): -
Other(％): Cu ≤0.30；Al ≤0.020；Nb ≤0.01；Ti ≤0.03；V ≤0.02
MECHANICAL PROPERTIES - HOT WORKING, HEAT TREATMENT AND HARDNESS
Hot working temperature /℃: 1100～850
Heat treatment temperature /℃|annealing / normalizing : 890～950
Heat treatment temperature /℃|quenching: —
Heat treatment temperature /℃|tempering: —
HBS: 120～160
(≥)|σb/MPa: 410～540
(≥)|σs/MPa: 240
(≥)|δ5(%): 25.0
(≥)|AKV/J: 44
Heat treatment temperature /℃|annealing / normalizing : 890～950
Heat treatment temperature /℃|quenching: —
Heat treatment temperature /℃|tempering: —
HBS: 120～160
(≥)|σb/MPa: 410～540
(≥)|σs/MPa: 240
(≥)|δ5(%): 25.0
(≥)|AKV/J: 44
MECHANICAL PROPERTY UNDER HIGH TEMPERATURE
Yield strength σ0.2≥/MPa|200℃: 185
Yield strength σ0.2≥/MPa|300℃: 145
Yield strength σ0.2≥/MPa|350℃: 125
Yield strength σ0.2≥/MPa|400℃: 100
Yield strength σ0.2≥/MPa|450℃: 80
Yield strength σ0.2≥/MPa|500℃: —
Yield strength σ0.2≥/MPa|300℃: 145
Yield strength σ0.2≥/MPa|350℃: 125
Yield strength σ0.2≥/MPa|400℃: 100
Yield strength σ0.2≥/MPa|450℃: 80
Yield strength σ0.2≥/MPa|500℃: —
PROFILE & DIMENSIONS
Round bar / Wire rod (Diameter): 5.5mm to 650mm
Square bar / Flat bar: 10mm to 1500mm
Plate / Sheet steel / Steel strip: 0.1mm to 400mm
Width: 8mm to 1000mm
Length: random length or based on the customer's special requirement.
Forged steel shape: stepped shafts with flanks / discs /tubes /slugs /donuts /cubes /other different shapes based on OEM.
TECHNICAL SALES ASSISTANCE
If you meet further on any technical enquiry. pleased to email or call our resident team of qualified production engineers. Email: sales@ccsteels.com
Hot search：1.0460
Total list
Monthly rank
- 3438NCD4
- 3424CrMo5
- 3119CrNi5
- 2938B3
- 28ASTM A739 type B11
- 2826NiCrMoV11-5
- 2742Cr4Mo2
- 24S135
- 24EN 38
- 22EN20B