DIN EN 10028-2 Material Specification High temperature Steel P265GH Round bar, P265GH Plate Hot rolling, Heat treatment, Ultrasonic flaw detection test.
DIN P265GH - MATERIAL DATA SHEET
MATERIAL CATEGORY High temperature structural steel
TYPICAL APPLICATIONS
Mechanical gears, gear shaft, main axis, valve rod.
Mechanical parts - connecting rod, bolt and nut.
Multidiameter shaft, Pressure vessel.
PRODUCT DESCRIPTION
The alloy is usually produced by EAF /VD /LF followed by electroslag refining (ESR) if necessary for special purpose. Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different level according to the buyers' requirements.
Bars are usually supplied bright in the softened condition.
Final heat treatment - heat treatment / QT
MATERIAL SPECIFICATIONS - DIN EN 10028-2 (2003), DIN 17755 (1983)
PROFILE & DIMENSIONS
Round bar / Disc (diameter): 5.5mm to 550mm
Square bar / Flat bar: 3mm to 600mm
Plate / Sheet steel / Steel strip: 0.1mm to 300mm
Width: 8mm to 1000mm
Length: random length or based on the customer's special requirement.
Forged steel shape: stepped shafts, other different shapes based on OEM.
Alloy structural steels are widely used in the filed of ship, vehicle, airplane, guided missile, weapons, railway, bridges, pressure vessel, machine tools, mechanical components with a bigger sectional size and so on.
CHEMICAL COMPOSITION (mass weight -%)
Carbon, C (％): ≤ 0.20
Silicon, Si (％): ≤ 0.40
Manganese, Mn (％): 0.50 ~ 1.40
Phosphorus, P (％)≤: 0.030
Sulfur, S (％)≤: 0.025
Chromium, Cr (％): ≤ 0.30
Molybdenum, Mo (％): ≤ 0.08
Nickel, Ni (％): ≤ 0.30
Other (％): Cu ≤ 0.30；Al ≤ 0.020；Nb ≤ 0.01；Ti ≤ 0.03；V ≤ 0.02
Silicon, Si (％): ≤ 0.40
Manganese, Mn (％): 0.50 ~ 1.40
Phosphorus, P (％)≤: 0.030
Sulfur, S (％)≤: 0.025
Chromium, Cr (％): ≤ 0.30
Molybdenum, Mo (％): ≤ 0.08
Nickel, Ni (％): ≤ 0.30
Other (％): Cu ≤ 0.30；Al ≤ 0.020；Nb ≤ 0.01；Ti ≤ 0.03；V ≤ 0.02
MECHANICAL PROPERTIES - HOT WORKING, HEAT TREATMENT AND HARDNESS
Heat treatment temperature /℃|annealing / normalizing : 890～950
Heat treatment temperature /℃|quenching: —
Heat treatment temperature /℃|tempering: —
HBS: 120～155
(≥)|σb/MPa: 410～530
(≥)|σs/MPa: 245
(≥)|δ5(%): 23
(≥)|AKV/J: 47
Heat treatment temperature /℃|quenching: —
Heat treatment temperature /℃|tempering: —
HBS: 120～155
(≥)|σb/MPa: 410～530
(≥)|σs/MPa: 245
(≥)|δ5(%): 23
(≥)|AKV/J: 47
MECHANICAL PROPERTY UNDER HIGH TEMPERATURE
Yield strength σ0.2≥/MPa|200℃: 195
Yield strength σ0.2≥/MPa|300℃: 155
Yield strength σ0.2≥/MPa|350℃: 140
Yield strength σ0.2≥/MPa|400℃: 130
Yield strength σ0.2≥/MPa|450℃: 115
Yield strength σ0.2≥/MPa|500℃: —
Yield strength σ0.2≥/MPa|300℃: 155
Yield strength σ0.2≥/MPa|350℃: 140
Yield strength σ0.2≥/MPa|400℃: 130
Yield strength σ0.2≥/MPa|450℃: 115
Yield strength σ0.2≥/MPa|500℃: —
TECHNICAL SALES ASSISTANCE
If you meet further on any technical enquiry. pleased to email or call our resident team of qualified production engineers. Email: sales@ccsteels.com
Hot search：P265GH
Total list
Monthly rank
- 3438NCD4
- 3424CrMo5
- 3119CrNi5
- 2938B3
- 28ASTM A739 type B11
- 2826NiCrMoV11-5
- 2742Cr4Mo2
- 24S135
- 24EN 38
- 22EN20B