39CrMoV13-9
2016-09-17 08:10:28 Origin： Remark：0 Click：
High strength steel 39CrMoV13-9 round bar, flat bar, forgings 1.8523 Steelmaking, ESR melted, Hot forging / rolling, Heat treatment, 100% Ultrasonic test, Cold working, machining.
TECHNICAL SPECIFICATIONS - Grade 39CrMoV13-9
MATERIAL CATEGORY: High-strength low alloy structural steel
MATERIAL CATEGORY: High-strength low alloy structural steel
OFFICIAL TEST CERTIFICATE: issued by TUV - SGS - BV
CHEMICAL COMPOSITION (mass weight %)
Carbon, C (％): 0.35 ~ 0.42
CHEMICAL COMPOSITION (mass weight %)
Carbon, C (％): 0.35 ~ 0.42
Silicon, Si (%): ≤ 0.40
Manganese, Mn (％): 0.40 ~ 0.70
Manganese, Mn (％): 0.40 ~ 0.70
Phosphorus, P (％)≤: 0.025
Sulfur, S (％)≤: 0.035
Chromium, Cr (%): 3.00 ~ 3.50
Vanadium, V (%): 0.15 ~ 0.25
Molybdenum, Mo (%): 0.80 ~ 1.10
MECHANICAL PROPERTY UNDER ROOM-TEMPERATURE
Condition: quenched and tempered, nitrided
Bar size /mm: ≤ 40
Tensile strength, σb/≥ MPa: 1420
Yield strength, σ0.2/≥ MPa: 1080
Elongation, δ ≥(％): 8.0
Reduction of area, ф ≥ (％): -
Hardness | HBW: -
Yield strength, σ0.2/≥ MPa: 1080
Elongation, δ ≥(％): 8.0
Reduction of area, ф ≥ (％): -
Hardness | HBW: -
Hardness after soft annealing: HBW 262 Max.
Bar size /mm: ≤ 100
Tensile strength, σb/≥ MPa: 1270
Yield strength, σ0.2/≥ MPa: -
Yield strength, σ0.2/≥ MPa: -
Elongation, δ ≥(％): -
Reduction of area, ф ≥ (％): -
Reduction of area, ф ≥ (％): -
Bar size /mm: ≤ 250
Tensile strength, σb/≥ MPa: 1080
Yield strength, σ0.2/≥ MPa: -
Yield strength, σ0.2/≥ MPa: -
Elongation, δ ≥(％): -
Reduction of area, ф ≥ (％): -
Reduction of area, ф ≥ (％): -
PRODUCT PROFILE AND DIMENSIONS
Round bar (Diameter): 5.5mm to 600mm
Square bar / Flat bar: 3mm to 500mm
Length: random length, fixed length or based on the customer's special requirement.
Heavy/middle plate via hot rolled: T50 - 400mm X W60 - 1000mm X L1000 - 12000mm
Forging piece: stepped shafts, other different shapes based on OEM requirement.
Round bar (Diameter): 5.5mm to 600mm
Square bar / Flat bar: 3mm to 500mm
Length: random length, fixed length or based on the customer's special requirement.
Heavy/middle plate via hot rolled: T50 - 400mm X W60 - 1000mm X L1000 - 12000mm
Forging piece: stepped shafts, other different shapes based on OEM requirement.
TECHNICAL SALES ASSISTANCE & SERVICE
If you meet further on any technical enquiry, pleased to EMAIL our resident team of qualified production engineers. Email: sales@ccsteels.com.
If you meet further on any technical enquiry, pleased to EMAIL our resident team of qualified production engineers. Email: sales@ccsteels.com.
Hot search：39CrMoV13-9
Previous page：4130H / H41300
Last page：AISI 660 / S66286 / A286
Total list
Monthly rank
- 3438NCD4
- 3424CrMo5
- 3119CrNi5
- 2938B3
- 28ASTM A739 type B11
- 2826NiCrMoV11-5
- 2742Cr4Mo2
- 24S135
- 24EN 38
- 22EN20B