AMS 6512 / K92890
2017-11-06 09:18:31 Origin： Remark：0 Click：
Description AMS 6512 Wire rod, Ex-stock AMS 6512B Steel strip, Inventory AMS 6512 Plate Sheet Properties from Steelmaking, ESR melted, Hot blooming, Hot forging, Hot rolling, Heat treatment, Straightening, 100% Nondestructive ultrasonic test, Cold working or rough turned machining. All of these materials conform to Military standard, nuclear power. 100% Ultrasonic test ASTM E2375 / SAE AMS 2154 /SEP 1923 /GB/T 4162 /EN 10228-3.
RAW MATERIAL SPECIFICATIONS - Grade AMS 6512 & K92890
MATERIAL FORM: Bar, Forge piece, Plate, Sheet
TECHNIQUE AND QUALITY: Annealed
MATERIAL TYPE: Aerospace Material Specification - Structural steel
MELTING PROCESS - Consumable electrode remelted steel
H S CODE For Customs - 7228 4000 / 7228 5000 / 7228 6000
OFFICIAL TEST REPORT - issued by TUV - SGS - BV
CHEMICAL COMPOSITIONS (Mass Weight - %)
H S CODE For Customs - 7228 4000 / 7228 5000 / 7228 6000
OFFICIAL TEST REPORT - issued by TUV - SGS - BV
CHEMICAL COMPOSITIONS (Mass Weight - %)
C (％): ≤ 0.030
Si (％): ≤ 0.10
Mn (％): ≤ 0.10
P (％)≤: 0.010
S (％)≤: 0.010
Cr (％): ≤ 0.50
Ni (％): 18.0 ~ 19.0
Mo (％): 4.60 ~ 5.20
Si (％): ≤ 0.10
Mn (％): ≤ 0.10
P (％)≤: 0.010
S (％)≤: 0.010
Cr (％): ≤ 0.50
Ni (％): 18.0 ~ 19.0
Mo (％): 4.60 ~ 5.20
Co (%): 7.00 ~ 8.20
Ti (%): 0.35 ~ 0.50
Other (％): Al 0.05 ~ 0.15, Cu ≤ 0.50
MECHANICAL PROPERTIES UNDER ROOM TEMP.
Tensile strength σb≥/MPa: 1750
Yield strength σs≥/MPa: 1550
Yield strength σs≥/MPa: 1550
Elongation δ5≥(%): 6.0
Impact, AKV≥/J: -
Hardness HB: 48HRC min.
Hardness HB: 48HRC min.
PRODUCT DESCRIPTION
The alloy is usually produced by VM /CVM followed by electroslag refining (ESR), Vacuum Arc Melting (VAR) if necessary for special purpose.
Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' specific requirements.
Round bar / Wire rod (Diameter): 5.5mm to 650mm
Square bar / Flat bar: 3mm to 400mm
Length: Fixed length or random length or based on the customer's special requirement.
Heavy/middle plate via hot rolled: T6 - 200mm X W1000- 2500mm X L1000-12000mm
Forging piece: stepped shafts with flanks / discs /tubes /slugs /donuts /cubes /other different shapes based on OEM.
The alloy is usually produced by VM /CVM followed by electroslag refining (ESR), Vacuum Arc Melting (VAR) if necessary for special purpose.
Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' specific requirements.
Round bar / Wire rod (Diameter): 5.5mm to 650mm
Square bar / Flat bar: 3mm to 400mm
Length: Fixed length or random length or based on the customer's special requirement.
Heavy/middle plate via hot rolled: T6 - 200mm X W1000- 2500mm X L1000-12000mm
Forging piece: stepped shafts with flanks / discs /tubes /slugs /donuts /cubes /other different shapes based on OEM.
TECHNICAL SALES ASSISTANCE & SERVICE
If you meet further on any technical enquiry, pleased to EMAIL our resident team of qualified production engineers, Email: sales@ccsteels.com.
If you meet further on any technical enquiry, pleased to EMAIL our resident team of qualified production engineers, Email: sales@ccsteels.com.
Previous page：Alloy 255/SD40
Last page：Z2CDT29-04
Total list
Monthly rank
- 3438NCD4
- 3424CrMo5
- 3119CrNi5
- 2938B3
- 28ASTM A739 type B11
- 2826NiCrMoV11-5
- 2742Cr4Mo2
- 24S135
- 24EN 38
- 22EN20B