C17E2C Stockist, C17E2C Equivalent Steel

C17E2C
2018-01-17 16:32:39   Origin:   Remark:0 Click:

Material Technical Standard of BS EN-10263-3 Cold extrusion and cold heading steel C17E2C data sheet, C17E2C Chemical compositions, C17E2C Mechanical properties from Steelmaking, C17E2C ESR melted, Blooming, Hot forging, Hot rolling, Heat treatment, Straightening, 100% Ultrasonic test/Magnetic powder inspection, Cold working, Peeled or rough turned machining. 100% Ultrasonic test ASTM E2375 /SAE AMS 2154 /SEP 1923 /GB/T 4162 /EN 10228-3.
TECHNICAL DATA SHEET - Grade C17E2C

MATERIAL CATEGORY: cold extrusion and cold heading steel
MATERIAL SPECIFICATIONS: BS EN
 - 10263-3 2001
CHEMICAL COMPOSITIONS (WEIGHT - %)
C (%):     0.15 ~ 0.19
Si (%):     ≤ 0.30
Mn (%):   0.30 ~ 0.60
P (%)≤:   0.025
S (%)≤:   0.025
Cr (%):    -
Mo (%):   -
TYPICAL MECHANICAL PROPERTY UNDER ROOM TEMP.
Tensile strength,σb/≥ MPa: 395
Yield strength, σ0.2/≥ MPa: 245
Elongation, δ ≥(%): 25.0
Reduction of area, (%): 50.0
Annealed hardness, HB ≤: -
MELTING PROCESS
This
alloy is generally smelt in Non-VIM + ESR, Electric Arc Furnace (EAF), EAF+LF+VD, EF + Electroslag remelting (ESR).
For a purpose of superior quality, it should be smelt via technology of vacuum refining or by agreement.

PRODUCT PROFILE AND AVAILABLE FORMS
Round bar (Diameter):  5.50mm to 650mm
Square bar / Flat bar: T3 to 500mm X W3 ~ 1200mm
Wire rod (Diameter):  1.00mm to 16mm
Length: Fixed length or random length or based on the customer's special requirement.
Other different shapes based on OEM.

TECHNICAL SALES ASSISTANCE & SERVICE
If you meet further on any technical enquiry. pleased to EMAIL our resident team of qualified production engineers.
- Email us:
lh.steel@hotmail.com

Hot search:C17E2C

Previous page:C15E2C
Last page:Z50CD15

Share to: