Description K41545 Ex-stock, Suppliers K41545 Round bar, Specifications K41545 Property from Steelmaking, ESR melted, Blooming, Hot forging, Hot rolling, Heat treatment, Straightening
TECHNICAL DATA SHEET - Grade UNS K41545
MATERIAL TECHNICAL STANDARDS: ASTM A182 - 2018
MATERIAL TYPE: 5.0Cr- 0.5Mo Alloy steel
CHEMICAL COMPOSITION (mass weight - %)
Carbon, C (％): ≤ 0.15
Carbon, C (％): ≤ 0.15
Manganese, Mn (％): 0.30 ~ 0.60
Silicon, Si (％): ≤ 0.50
Phosphorus, P (％)≤: 0.030
Sulfur, S (％)≤: 0.030
Chromium, Cr (%): 4.00 ~ 6.00
Molybdenum, Mo (%): 0.44 ~ 0.65
Nickel, Ni (%): -
TYPICAL MECHANICAL PROPERTIES
Tensile strength, σb/≥ MPa: 485
Yield strength, σ0.2/MPa: 275
Elongation, δ ≥(％): 20.0
Reduction of area, ф ≥ (％): 30.0
Hardness via heat treatment /HBW: 143 ~ 217
Hardness via heat treatment /HBW: 143 ~ 217
HEAT TREATMENT PRACTICE
Condition: annealed 955 Deg.
Cooling medium: furnace cool
PRODUCT DESCRIPTION
The alloy is usually produced by BEF / BEF + AOD / EAF, followed by electroslag refining (ESR or VAR ) if necessary for special purpose.
Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' specific requirements.
Round bar / Wire rod (Diameter): 5.5mm to 650mm
Square bar / Flat bar: 3mm to 800mm
Length: Fixed length or random length or based on the customer's special requirement.
Heavy/middle plate via hot rolled: T6 - 400mm X W20 - 1200mm X L1000-5000mm
Forging piece: stepped shafts, other different shapes based on OEM.
TECHNICAL SALES ASSISTANCE & SERVICE
If you meet further on any technical inquiry. pleased to EMAIL our resident team of qualified production engineers, Email: sales@ccsteels.com.
MATERIAL TECHNICAL STANDARDS: ASTM A182 - 2018
MATERIAL TYPE: 5.0Cr- 0.5Mo Alloy steel
CHEMICAL COMPOSITION (mass weight - %)
Carbon, C (％): ≤ 0.15
Carbon, C (％): ≤ 0.15
Manganese, Mn (％): 0.30 ~ 0.60
Silicon, Si (％): ≤ 0.50
Phosphorus, P (％)≤: 0.030
Sulfur, S (％)≤: 0.030
Chromium, Cr (%): 4.00 ~ 6.00
Molybdenum, Mo (%): 0.44 ~ 0.65
Nickel, Ni (%): -
TYPICAL MECHANICAL PROPERTIES
Tensile strength, σb/≥ MPa: 485
Yield strength, σ0.2/MPa: 275
Elongation, δ ≥(％): 20.0
Reduction of area, ф ≥ (％): 30.0
Hardness via heat treatment /HBW: 143 ~ 217
Hardness via heat treatment /HBW: 143 ~ 217
HEAT TREATMENT PRACTICE
Condition: annealed 955 Deg.
Cooling medium: furnace cool
PRODUCT DESCRIPTION
The alloy is usually produced by BEF / BEF + AOD / EAF, followed by electroslag refining (ESR or VAR ) if necessary for special purpose.
Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' specific requirements.
Round bar / Wire rod (Diameter): 5.5mm to 650mm
Square bar / Flat bar: 3mm to 800mm
Length: Fixed length or random length or based on the customer's special requirement.
Heavy/middle plate via hot rolled: T6 - 400mm X W20 - 1200mm X L1000-5000mm
Forging piece: stepped shafts, other different shapes based on OEM.
TECHNICAL SALES ASSISTANCE & SERVICE
If you meet further on any technical inquiry. pleased to EMAIL our resident team of qualified production engineers, Email: sales@ccsteels.com.
Hot search：K41545
Previous page：ASTM A182 Gr. F5
Last page：STS304J3
Total list
Monthly rank
- 3438NCD4
- 3424CrMo5
- 3119CrNi5
- 2938B3
- 28ASTM A739 type B11
- 2826NiCrMoV11-5
- 2742Cr4Mo2
- 24S135
- 24EN 38
- 22EN20B