ASTM A182 Specification F91 type 2 Round bar, Flat bar, Plate and Forgings, P91 Stock available, Hot forging, Hot rolling, Heat treatment
TECHNICAL DATA SHEET - ASTM A182 Grade F91 type 2
MATERIAL TECHNICAL STANDARDS: ASTM A182 - 2018
MATERIAL TYPE: 9.0Cr - 1.0Mo - 0.2V Alloy steel
CHEMICAL COMPOSITION (mass weight - %)
Carbon, C (％): 0.08 ~ 0.12
Manganese, Mn (％): 0.30 ~ 0.50
Silicon, Si (％): 0.20 ~ 0.40
Phosphorus, P (％) ≤: 0.020
Sulfur, S (％) ≤: 0.005
Chromium, Cr (%): 8.00 ~ 9.50
Molybdenum, Mo (%): 0.85 ~ 1.05
Nickel, Ni (%): ≤ 0.20
Niobium, Nb (%): 0.05 ~ 0.11
Titanium, Ti (%): ≤ 0.01
Nitrogen, N (%): 0.035 ~ 0.07
Vanadium, V (%): 0.18 ~ 0.25
Copper, Cu (%): ≤ 0.10
TYPICAL MECHANICAL PROPERTIES
Tensile strength, Rm ≥ MPa: 620
Yield strength, Rp0.2 ≥ MPa: 415
Elongation, A5 ≥(％): 20.0
Reduction of area, Z ≥ (％): 40.0
Hardness via heat treatment /HBW: 190 ~ 248
HEAT TREATMENT PRACTICE
Condition: Solution annealed 1040 ~ 1080 Deg. C
Cooling medium: air cool
PRODUCT DESCRIPTION
The alloy is usually produced by BEF / BEF + AOD / EAF, followed by electroslag refining (ESR or VAR ) if necessary for special purpose. Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' specific requirements.
Round bar / Wire rod (Diameter): 0.50mm to 450mm
Square bar / Flat bar: 3mm to 800mm
Length: Fixed length or random length or based on the customer's special requirement.
Heavy/middle plate via hot rolled: T6 ~ 400mm X W200 ~ 1000mm X L1000 ~ 2000mm
Forging piece: stepped shafts, other different shapes based on OEM.
TECHNICAL SALES ASSISTANCE & SERVICE
If you meet further on any technical inquiry. pleased to EMAIL (sales@ccsteels.com) our resident team of qualified production engineers.
MATERIAL TECHNICAL STANDARDS: ASTM A182 - 2018
MATERIAL TYPE: 9.0Cr - 1.0Mo - 0.2V Alloy steel
CHEMICAL COMPOSITION (mass weight - %)
Carbon, C (％): 0.08 ~ 0.12
Manganese, Mn (％): 0.30 ~ 0.50
Silicon, Si (％): 0.20 ~ 0.40
Phosphorus, P (％) ≤: 0.020
Sulfur, S (％) ≤: 0.005
Chromium, Cr (%): 8.00 ~ 9.50
Molybdenum, Mo (%): 0.85 ~ 1.05
Nickel, Ni (%): ≤ 0.20
Niobium, Nb (%): 0.05 ~ 0.11
Titanium, Ti (%): ≤ 0.01
Nitrogen, N (%): 0.035 ~ 0.07
Vanadium, V (%): 0.18 ~ 0.25
Copper, Cu (%): ≤ 0.10
TYPICAL MECHANICAL PROPERTIES
Tensile strength, Rm ≥ MPa: 620
Yield strength, Rp0.2 ≥ MPa: 415
Elongation, A5 ≥(％): 20.0
Reduction of area, Z ≥ (％): 40.0
Hardness via heat treatment /HBW: 190 ~ 248
HEAT TREATMENT PRACTICE
Condition: Solution annealed 1040 ~ 1080 Deg. C
Cooling medium: air cool
PRODUCT DESCRIPTION
The alloy is usually produced by BEF / BEF + AOD / EAF, followed by electroslag refining (ESR or VAR ) if necessary for special purpose. Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' specific requirements.
Round bar / Wire rod (Diameter): 0.50mm to 450mm
Square bar / Flat bar: 3mm to 800mm
Length: Fixed length or random length or based on the customer's special requirement.
Heavy/middle plate via hot rolled: T6 ~ 400mm X W200 ~ 1000mm X L1000 ~ 2000mm
Forging piece: stepped shafts, other different shapes based on OEM.
TECHNICAL SALES ASSISTANCE & SERVICE
If you meet further on any technical inquiry. pleased to EMAIL (sales@ccsteels.com) our resident team of qualified production engineers.
Total list
Monthly rank
- 3438NCD4
- 3424CrMo5
- 3119CrNi5
- 2938B3
- 28ASTM A739 type B11
- 2826NiCrMoV11-5
- 2742Cr4Mo2
- 24S135
- 24EN 38
- 22EN20B