ASTM A182 type F11 Class 1
2019-10-30 11:11:39 Origin： Remark：0 Click：
Standard Specification of forged or rolled alloy and stainless steel pipe flanges,forged fittings,and valves and parts for high temperature service Grade F11 Class 1 datasheet, Grade F11 Class 1 Chemical compositions, Grade F11 Class 1 Mechanical property from Steelmaking, ESR melted, Blooming, Hot forging, Hot rolling, Heat treatment, Straightening, 100% Ultrasonic test, Cold working or rough turned machining. Technical specification - ASTM A182 - 2018.
TECHNICAL DATA SHEET - ASTM A182 Grade F11 Class 1
MATERIAL TECHNICAL STANDARDS: ASTM A182 - 2018
MATERIAL TYPE: 1Cr - 0.5Mo Alloy steel
CHEMICAL COMPOSITION (WEIGHT %)
C (％): 0.05 ~ 0.11
CHEMICAL COMPOSITION (WEIGHT %)
C (％): 0.05 ~ 0.11
Mn (％): 0.30 ~ 0.60
Si (％): 0.50 ~ 1.00
Si (％): 0.50 ~ 1.00
P (％)≤: 0.030
S (％)≤: 0.020
Cr (%): 1.00 ~ 1.50
Mo (%): 0.44 ~ 0.65
S (％)≤: 0.020
Cr (%): 1.00 ~ 1.50
Mo (%): 0.44 ~ 0.65
Ni (%): -
Nb (%): -
Ti (%): -
TYPICAL MECHANICAL PROPERTIES
Tensile strength, σb/≥ MPa: 415
Yield strength, σ0.2/MPa: 205
Elongation, δ ≥(％): 20.0
Reduction of area, ф ≥ (％): 45.0
Hardness via heat treatment /HBW: 121 ~ 174
Reduction of area, ф ≥ (％): 45.0
Hardness via heat treatment /HBW: 121 ~ 174
HEAT TREATMENT PRACTICE
Condition: annealed 900 Deg. C
Cooling medium: furnace cool
Tempering temperature: -
Condition: normalize and tempered 900 Deg. C
Cooling medium: air cool
Tempering temperature: 620 Deg. C
PRODUCT DESCRIPTION
The alloy is usually produced by BEF / BEF + AOD / EAF, followed by electroslag refining (ESR or VAR ) if necessary for special purpose.
Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' specific requirements.
Round bar / Wire rod (Diameter): 0.50mm to 600mm
Square bar / Flat bar: 3mm to 500mm
Length: Fixed length or random length or based on the customer's special requirement.
Heavy/middle plate via hot rolled: T6 ~ 400mm X W200 ~ 1000mm X L1000 ~ 3500mm
Forging piece: stepped shafts with flanks / discs /tubes /slugs /donuts /cubes /other different shapes based on OEM.
The alloy is usually produced by BEF / BEF + AOD / EAF, followed by electroslag refining (ESR or VAR ) if necessary for special purpose.
Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' specific requirements.
Round bar / Wire rod (Diameter): 0.50mm to 600mm
Square bar / Flat bar: 3mm to 500mm
Length: Fixed length or random length or based on the customer's special requirement.
Heavy/middle plate via hot rolled: T6 ~ 400mm X W200 ~ 1000mm X L1000 ~ 3500mm
Forging piece: stepped shafts with flanks / discs /tubes /slugs /donuts /cubes /other different shapes based on OEM.
TECHNICAL SALES ASSISTANCE & SERVICE
If you meet further on any technical inquiry. pleased to EMAIL ( lh.steel@hotmail.com ) our resident team of qualified production engineers.
If you meet further on any technical inquiry. pleased to EMAIL ( lh.steel@hotmail.com ) our resident team of qualified production engineers.
Total list
Monthly rank
- 3438NCD4
- 3424CrMo5
- 3119CrNi5
- 2938B3
- 28ASTM A739 type B11
- 2826NiCrMoV11-5
- 2742Cr4Mo2
- 24S135
- 24EN 38
- 22EN20B