40CrMoV13-9
2019-11-23 17:52:21 Origin: Remark:0 Click:
DIN 10085 Specification of Carburized Structural Steel 40CrMoV13-9 Round bars, Shaft 40CrMoV13-9 Forged plate, ESR & VAR technique, Heat treatment.
MATERIAL DATA SHEET - GRADE 40CrMoV13-9
MATERIAL CATEGORY - Carburized structural steel
Official Test Certificate: issued by TUV - SGS - BV
PRODUCT DESCRIPTION
Proven performance in long-term service.
Extensive database of long term, high temperature test results.
High room and elevated temperature strength.
High notch tolerance.
Thermal expansion coefficients compatible with low alloy steel turbine casing materials.
Lower design and operating risks
Simplified design for bolting configuration compared with martensitic steels or high nickel alloys.
Proven performance in long-term service.
Extensive database of long term, high temperature test results.
High room and elevated temperature strength.
High notch tolerance.
Thermal expansion coefficients compatible with low alloy steel turbine casing materials.
Lower design and operating risks
Simplified design for bolting configuration compared with martensitic steels or high nickel alloys.
Alloy structural steel is provided with higher yield strength, tensile strength, endurance strength, yield ratio (about 0.85 generally ) enough plasticity and toughness.
The concentration of alloy element of this kind of steel is quite high, mainly are corrosion resistant steel, heat resistant steel, wear resistant steel, and other special steels of physical and chemical properties. Alloy structural steel has preferable mechanical property than that of carbon structural steel, high performance of heat treatment especially.
The alloy is usually produced by EAF +VD+LF/ BEF followed by electroslag refining (ESR / VAR) if necessary for special purpose. Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different level according to the buyers' requirements.
Bars are usually supplied bright in the annealed condition, or bright annealing specially.
Final heat treatment - heat treatment / QT
The concentration of alloy element of this kind of steel is quite high, mainly are corrosion resistant steel, heat resistant steel, wear resistant steel, and other special steels of physical and chemical properties. Alloy structural steel has preferable mechanical property than that of carbon structural steel, high performance of heat treatment especially.
The alloy is usually produced by EAF +VD+LF/ BEF followed by electroslag refining (ESR / VAR) if necessary for special purpose. Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different level according to the buyers' requirements.
Bars are usually supplied bright in the annealed condition, or bright annealing specially.
Final heat treatment - heat treatment / QT
MATERIAL SPECIFICATIONS - DIN EN 10085 (2001), DIN 17211 (1987)
CHEMICAL COMPOSITION (mass weight - %)
Carbon, C (%): 0.35 ~ 0.42
Silicon, Si (%): 0.15 ~ 0.40
Manganese, Mn (%): 0.40 ~ 0.70
Phosphorus, P (%)≤: 0.030
Sulfur, S (%)≤: 0.035
Chromium, Cr (%): 3.00 ~ 3.50
Molybdenum, Mo (%): 0.80 ~ 1.10
Vanadium, V (%): 0.15 ~ 0.25
Silicon, Si (%): 0.15 ~ 0.40
Manganese, Mn (%): 0.40 ~ 0.70
Phosphorus, P (%)≤: 0.030
Sulfur, S (%)≤: 0.035
Chromium, Cr (%): 3.00 ~ 3.50
Molybdenum, Mo (%): 0.80 ~ 1.10
Vanadium, V (%): 0.15 ~ 0.25
MECHANICAL PROPERTIES - HOT WORKING, HEAT TREATMENT AND HARDNESS
Hardness of Carburized layer |HV: 800
TYPICAL APPLICATIONS
Hot working temperature /℃: 1050~850
Heat treatment temperature /℃|annealing: 650~700
Heat treatment temperature /℃|quenching: 920~960 Oil or air cooled
Heat treatment temperature /℃|tempering: 570~650
Heat treatment temperature /℃|annealing: 650~700
Heat treatment temperature /℃|quenching: 920~960 Oil or air cooled
Heat treatment temperature /℃|tempering: 570~650
Heat treatment temperature /℃|carburizing: 490~510
Hardness after annealing HBS≤: 262
Hardness after annealing HBS≤: 262
Size /mm: ≤ 40
Tensile strength, ≥|σb/MPa: 1240
Yield strength, ≥|σs≥/MPa: 1080
Elongatio, ≥|δ5 (%)≥: 8.0
Impact, ≥|AKV/J (DVM-V form sampling): 27
Impact, ≥|AKV/J (DVM-V form sampling): 27
Size /mm: ≤ 100
Tensile strength, ≥|σb/MPa: 1270
Yield strength, |σs≥/MPa: -
Elongation, ≥|δ5 (%)≥: -
≥|AKV/J (DVM-V form sampling): -
≥|AKV/J (DVM-V form sampling): -
Size /mm: ≤ 250
Tensile strength, |σb/MPa: 1080
Yield strength, |σs≥/MPa: -
Elongation, ≥|δ5 (%)≥: -
≥|AKV/J (DVM-V form sampling): -
≥|AKV/J (DVM-V form sampling): -
TYPICAL APPLICATIONS
Alloy structural steels are widely used in the filed of ship, vehicle, airplane, guided missile, weapons, railway, bridges, pressure vessel, machine tools, mechanical components with a bigger sectional size and so on.
Power generation – turbine fasteners – boiler support rods.
Process plant – fasteners. Mechanical gears, gear shaft, main axis, valve rod.
Mechanical parts - connecting rod, bolt and nut. Multidiameter shaft. Pressure vessel.
Power generation – turbine fasteners – boiler support rods.
Process plant – fasteners. Mechanical gears, gear shaft, main axis, valve rod.
Mechanical parts - connecting rod, bolt and nut. Multidiameter shaft. Pressure vessel.
TECHNICAL SALES ASSISTANCE
If you meet further on any technical enquiry. pleased to EMAIL (sales@ccsteels.com) our resident team of qualified production engineers.
If you meet further on any technical enquiry. pleased to EMAIL (sales@ccsteels.com) our resident team of qualified production engineers.
Hot search:40CrMoV13-9
Previous page:N06686
Last page:DIN 2.4606
Total list
Monthly rank
- 3438NCD4
- 3424CrMo5
- 3119CrNi5
- 2938B3
- 28ASTM A739 type B11
- 2826NiCrMoV11-5
- 2742Cr4Mo2
- 24S135
- 24EN 38
- 22EN20B