15NiMoSiCr10
2024-11-15 05:29:00   Origin：   Remark：0 Click：

TECHNICAL DATA SHEET - 15NiMoSiCr10

MATERIAL TYPE: Cr-Ni-Mo Alloy steel
MELTING PROCESS - Consumable electrode remelted
H S CODE For Customs - 7228 4000 / 7228 5000 / 7228 6000
OFFICIAL TEST REPORT - issued by TUV - SGS -  BV
CHEMICAL COMPOSITIONS (mass weight - %)
Carbon, C (％): 0.10 ~ 0.20
Silicon, Si (％): 0.90 ~ 1.20
Manganese, Mn (％): ≤ 1.00
Phosphorus, P (％) ≤: 0.025
Sulfur, S (％) ≤: 0.015
Chromium, Cr (%): 0.80 ~ 1.20
Molybdenum, Mo (%): 1.70 ~ 2.25
Nickel, Ni (%): 2.30 ~ 2.70
Vanadium, V (%): ≤ 0.50
MECHANICAL PROPERTY UNDER ROOM TEMP.
Tensile strength, Rm ≥ MPa: 1210
Yield strength, Rp0.2 / MPa: 950
Elongation, A5 ≥ (％): 7.0
Reduction of area, Z ≥ (％): 35.0

Hardness via heat treatment /HBW: 345 Min.
Hardness via heat treatment /HBW: 345 Min.
PRODUCT DESCRIPTION
15NiMoSiCr10 is usually produced by BEF / VIM followed by electroslag refining (ESR) if necessary for special purpose. Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' specific requirements.
Round bar / rod / disc (diameter): 5.5mm to 600mm
Square bar / Flat bar: 10mm to 600mm
Length: Fixed length or random length or based on the customer's special requirement.
Heavy/middle plate via hot rolled: T60 - 400mm X W10 - 100mm X Lmm
Forging piece: stepped shafts, and other different shapes based on OEM.