1.1133
2020-03-20 11:22:02 Origin： Remark：0 Click：
Specifications DIN EN 10083-3 type1.1133 Forging Bar, DIN 1.1133 ESR & VAR technique, Hot forging & rolling, Heat treatment, Straightening, Ultrasonic flaw detection test.
MATERIAL TECHNICAL DATASHEET - Grade W-Nr 1.1133
MATERIAL CATEGORY: hardened and tempered steel
PRODUCT DESCRIPTION
Alloy structural steel is provided with higher yield strength, tensile strength, endurance strength, yield ratio (about 0.85 generally ) enough plasticity and toughness.
The concentration of alloy element of this kind of steel is quite high, mainly are corrosion resistant steel, heat resistant steel, wear resistant steel, and other special steels of physical and chemical properties. Alloy structural steel has preferable mechanical property than that of carbon structural steel, high performance of heat treatment especially.
The alloy is usually produced by EAF /VD /LF followed by electroslag refining (ESR) if necessary for special purpose. Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different level according to the buyers' requirements.
Bars are usually supplied bright in the annealed condition.
Final heat treatment - heat treatment / QT
MATERIAL SPECIFICATIONS - DIN EN 10083-3 (2006), DIN 17200 (1987)
CHEMICAL COMPOSITION (mass weight %)
Carbon, C (％): 0.17 ~ 0.23
Silicon, Si (％): ≤ 0.60
Manganese, Mn (％): 1.00 ~ 1.50
Phosphorus, P (％)≤: 0.035
Sulfur, S (％)≤: 0.030
Chromium, Cr (％): -
Molybdenum, Mo (％): -
Nickel, Ni (％): -
Aluminum, Al (％): 0.015～0.050, Cr+Ni+Mo≤ 0.63
Silicon, Si (％): ≤ 0.60
Manganese, Mn (％): 1.00 ~ 1.50
Phosphorus, P (％)≤: 0.035
Sulfur, S (％)≤: 0.030
Chromium, Cr (％): -
Molybdenum, Mo (％): -
Nickel, Ni (％): -
Aluminum, Al (％): 0.015～0.050, Cr+Ni+Mo≤ 0.63
MECHANICAL PROPERTIES - HOT WORKING, HEAT TREATMENT AND HARDNESS
Hot working temperature /℃: 1100～850
Heat treatment temperature /℃| annealing: 650～700
Heat treatment temperature /℃| Normalizing: 850～880
Heat treatment temperature /℃| Quenching: 820～850water, 830 ~ 860oil
Heat treatment temperature /℃| Tempering: 550～660
Hardness after annealing ≤HBS: -
Heat treatment temperature /℃| annealing: 650～700
Heat treatment temperature /℃| Normalizing: 850～880
Heat treatment temperature /℃| Quenching: 820～850water, 830 ~ 860oil
Heat treatment temperature /℃| Tempering: 550～660
Hardness after annealing ≤HBS: -
Steel dimension /mm: ≤16
|σb≥/MPa: 540 ~ 690
|σs≥/MPa: 390
|δ5≥/(%): 22.0
|ψ≥/(%): 50
|AKV≥/J: 69
|σb≥/MPa: 540 ~ 690
|σs≥/MPa: 390
|δ5≥/(%): 22.0
|ψ≥/(%): 50
|AKV≥/J: 69
Steel dimension /mm: 17 - 40
|σb≥/MPa: 490 ~ 640
|σs≥/MPa: 345
|δ5≥/(%): 20
|σb≥/MPa: 490 ~ 640
|σs≥/MPa: 345
|δ5≥/(%): 20
|ψ≥/(%): 55
|AKV≥/J: 69
Steel dimension /mm: 41 - 100
|σb≥/MPa: 490 ~ 590
|σs≥/MPa: 295
|δ5≥/(%): 18
|ψ≥/(%): 60
|AKV≥/J: 76
|σb≥/MPa: 490 ~ 590
|σs≥/MPa: 295
|δ5≥/(%): 18
|ψ≥/(%): 60
|AKV≥/J: 76
TYPICAL APPLICATIONS
Alloy structural steels are widely used in the filed of ship, vehicle, airplane, guided missile, weapons, railway, bridges, pressure vessel, machine tools, mechanical components with a bigger sectional size and so on.
Mechanical gears, gear shaft, main axis, valve rod.
Mechanical parts - connecting rod, bolt and nut, Multidiameter shaft, Pressure vessel.
TECHNICAL SALES ASSISTANCE
If you meet further on any technical enquiry. pleased to Email (sales@ccsteels.com) or call our resident team of qualified production engineers.
PRODUCT PROFILE
Round bar / Wire rod (Diameter): 5.5mm to 800mm
Square bar / Flat bar: 3mm to 1000mm
Plate / Sheet steel / Steel strip: 0.1mm to 1000mm
Width: 8mm to 1000mm
Length: random length or based on the customer's special requirement.
Forged steel shape: stepped shafts with flanks / discs /tubes /slugs /donuts /cubes /other different shapes based on OEM
Hot search：1.1133
Total list
Monthly rank
- 3438NCD4
- 3424CrMo5
- 3119CrNi5
- 2938B3
- 28ASTM A739 type B11
- 2826NiCrMoV11-5
- 2742Cr4Mo2
- 24S135
- 24EN 38
- 22EN20B