Specifications 65C2BA, Ex-stock 65C2BA Forge bar plate machined, 65S2VA exporter, from Melting, ESR & VAR technique, Hot rolling, Heat treatment.
TECHNICAL DATA SHEET - Grade 65C2BA
MATERIAL TYPE: Si-W Spring Structural steel
CHEMICAL COMPOSITION (mass weight - %)
Carbon, C (％): 0.61 ~ 0.69
Silicon, Si (％): 1.50 ~ 2.00
Manganese, Mn (％): 0.70 ~ 1.00
CHEMICAL COMPOSITION (mass weight - %)
Carbon, C (％): 0.61 ~ 0.69
Silicon, Si (％): 1.50 ~ 2.00
Manganese, Mn (％): 0.70 ~ 1.00
Phosphorus, P (％)≤: 0.025
Sulfur, S (％)≤: 0.015
Chromium, Cr (%): ≤ 0.30
Nickel, Ni (%): ≤ 0.25
Sulfur, S (％)≤: 0.015
Chromium, Cr (%): ≤ 0.30
Nickel, Ni (%): ≤ 0.25
Tungsten, W (%): 0.80 ~ 1.20
Copper, Cu (%): ≤ 0.25
MECHANICAL PROPERTY UNDER ROOM TEMP.
Tensile strength, σb/≥ MPa: -
Yield strength, σ0.2/MPa: -
Elongation, δ ≥(％): -
Reduction of area, ф ≥ (％): -
Hardness via heat treatment /HBW: 279
Reduction of area, ф ≥ (％): -
Hardness via heat treatment /HBW: 279
PRODUCT DESCRIPTION
The alloy is usually produced by EAF / BEF followed by electroslag refining (ESR or VAR) if necessary for special purpose. Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' specific requirements.
Round bar / Wire rod (Diameter): 5.5mm to 800mm
Square bar / Flat bar: 10mm to 800mm
Length: Fixed length or random length or based on the customer's special requirement.
Heavy/middle plate via hot rolled: T50 - 400mm X W50 - 1000mm X L1000 ~ 5000mm
Forging piece: stepped shafts, other different shapes based on OEM.
The alloy is usually produced by EAF / BEF followed by electroslag refining (ESR or VAR) if necessary for special purpose. Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' specific requirements.
Round bar / Wire rod (Diameter): 5.5mm to 800mm
Square bar / Flat bar: 10mm to 800mm
Length: Fixed length or random length or based on the customer's special requirement.
Heavy/middle plate via hot rolled: T50 - 400mm X W50 - 1000mm X L1000 ~ 5000mm
Forging piece: stepped shafts, other different shapes based on OEM.
TECHNICAL SALES ASSISTANCE & SERVICE
If you meet further on any technical enquiry. pleased to EMAIL (sales@ccsteels.com) our resident team of qualified production engineers.
If you meet further on any technical enquiry. pleased to EMAIL (sales@ccsteels.com) our resident team of qualified production engineers.
Hot search：65C2BA
Previous page：65S2VA
Last page：ASTM A182 Gr.F304LN
Total list
Monthly rank
- 3438NCD4
- 3424CrMo5
- 3119CrNi5
- 2938B3
- 28ASTM A739 type B11
- 2826NiCrMoV11-5
- 2742Cr4Mo2
- 24S135
- 24EN 38
- 22EN20B