28NiCrMoV8-5 / 1.6932
2025-02-24 16:35:00 Origin： Remark：0 Click：
Peeled bar 1.6932 Inventory, 28NiCrMoV8-5 Specifications Exporter from Melting, ESR technique, Hot forging, Hot rolling, Heat treatment
TECHNICAL DATA SHEET - 28NiCrMoV8-5 & 1.6932
MATERIAL FORM - Round bar, Plate, forgings
Stock available - Diameter 70, peeled bright round bar
MATERIAL TYPE: 2Ni - Cr - Mo -V Structural steel
Official Test Certificate Report: issued by TUV - SGS - BV
CHEMICAL COMPOSITION (mass weight - %)
Carbon, C (％): 0.24 ~ 0.32
Silicon, Si (％): ≤ 0.40
Manganese, Mn (％): 0.15 ~ 0.40
Phosphorus, P (％) ≤: 0.025
Sulfur, S (％) ≤: 0.015
Chromium, Cr (％): 1.00 ~ 1.50
Molybdenum, Mo (％): 0.35 ~ 0.55
Nickel, Ni (％): 1.80 ~ 2.10
Vanadium, V (％): 0.05 ~ 0.15
CHEMICAL COMPOSITION (mass weight - %)
Carbon, C (％): 0.24 ~ 0.32
Silicon, Si (％): ≤ 0.40
Manganese, Mn (％): 0.15 ~ 0.40
Phosphorus, P (％) ≤: 0.025
Sulfur, S (％) ≤: 0.015
Chromium, Cr (％): 1.00 ~ 1.50
Molybdenum, Mo (％): 0.35 ~ 0.55
Nickel, Ni (％): 1.80 ~ 2.10
Vanadium, V (％): 0.05 ~ 0.15
MECHANICAL PROPERTIES UNDER ROOM TEMP.
Hot working temperature /℃: 1050～850
Heat treatment temperature /℃| annealing: 650～700
Heat treatment temperature /℃| annealing: 650～700
Heat treatment temperature /℃| Normalizing: 850～880
Heat treatment temperature /℃| Quenching: -
Heat treatment temperature /℃| Tempering : -
Hardness after annealing ≤HBS: 248
Heat treatment temperature /℃| Quenching: -
Heat treatment temperature /℃| Tempering : -
Hardness after annealing ≤HBS: 248
Steel dimension /mm: 101 - 160
Tensile strength, |σb ≥ MPa: 800 ~ 950
Yield strength, |σs ≥ MPa: 630
Elongation, |δ5 ≥ (%): 14.0
Reduction of area, |ψ ≥ (%): -
Impact strength, |AKv ≥ J: 45
Tensile strength, |σb ≥ MPa: 800 ~ 950
Yield strength, |σs ≥ MPa: 630
Elongation, |δ5 ≥ (%): 14.0
Reduction of area, |ψ ≥ (%): -
Impact strength, |AKv ≥ J: 45
PRODUCT DESCRIPTION
The alloy 1.6932 is usually produced by BEF / EAF followed by electroslag refining (ESR), Vacuum Arc Melting (VAR) if necessary for special purpose.
Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' specific requirements.
Round bar / Disc (diameter) 5.5mm to 650mm
Square bar / Flat bar: 3mm to 400mm
Length: Fixed length or random length or based on the customer's special requirement.
Heavy/middle plate via hot rolled: T60 - 400mm X W60 - 1000mm X L1000 - 6000mm
Forging piece: stepped shafts, other different shapes based on OEM.
TECHNICAL SALES ASSISTANCE & SERVICE
If you meet further on any technical enquiry, pleased to EMAIL our resident team of qualified production engineer. E-mail: sales@ccsteels.com.
If you meet further on any technical enquiry, pleased to EMAIL our resident team of qualified production engineer. E-mail: sales@ccsteels.com.
Hot search：28NiCrMoV8-5 / 1.6932
Total list
Monthly rank
- 6238NCD4
- 5326NiCrMoV11-5
- 5342Cr4Mo2
- 41EN52 & EN 52
- 3924CrMo5
- 3720C15
- 3440Cr4
- 33ASTM A739 type B11
- 33815M17
- 2816NC6