1.0482 Steels Ex-stock, Alloy 1.0482 Suppliers, Properties 1.0482 Forging Bar Plate, DIN 1.0482 Technical specifications Melting, ESR & VAR technique, Hot blooming, Hot forging, Hot rolling, Heat treatment, Straightening, Ultrasonic flaw detection test.
TECHNICAL DATA SHEET - DIN 1.0482
MATERIAL CATEGORY: High temperature structural steel
PRODUCT DESCRIPTION
Alloy structural steel is provided with higher yield strength, tensile strength, endurance strength, yield ratio (about 0.85 generally ) enough plasticity and toughness.
The concentration of alloy element of this kind of steel is quite high, mainly are corrosion resistant steel, heat resistant steel, wear resistant steel, and other special steels of physical and chemical properties. Alloy structural steel has preferable mechanical property than that of carbon structural steel, high performance of heat treatment especially.
The alloy is usually produced by EAF /VD /LF followed by electroslag refining (ESR) if necessary for special purpose.
Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different level according to the buyers' requirements.
Bars are usually supplied bright in the annealed condition.
Final heat treatment - heat treatment / QT
MATERIAL SPECIFICATIONS
DIN EN 10028-2 (2003), DIN 17755 (1983)
CHEMICAL COMPOSITION (WEIGHT %)
C (％): 0.17 ~ 0.22
Si (％): 0.30 ~ 0.60
Mn (％): 1.00 ~ 1.30
P (％)≤: 0.045
S (％)≤: 0.045
Cr (％): ≤ 0.30
Mo (％): -
Ni (％): -
Si (％): 0.30 ~ 0.60
Mn (％): 1.00 ~ 1.30
P (％)≤: 0.045
S (％)≤: 0.045
Cr (％): ≤ 0.30
Mo (％): -
Ni (％): -
MECHANICAL PROPERTIES - HOT WORKING, HEAT TREATMENT AND HARDNESS
Hot working temperature /℃: 1100～850
Heat treatment temperature /℃|annealing / normalizing: 880～910
Heat treatment temperature /℃|quenching: -
Heat treatment temperature /℃|tempering: 530~620
HBS: 152～180
(≥)|σb/MPa: 510～610
(≥)|σs/MPa: 315
(≥)|δ5(%): 20.0
(≥)|AKV/J: 34
Heat treatment temperature /℃|annealing / normalizing: 880～910
Heat treatment temperature /℃|quenching: -
Heat treatment temperature /℃|tempering: 530~620
HBS: 152～180
(≥)|σb/MPa: 510～610
(≥)|σs/MPa: 315
(≥)|δ5(%): 20.0
(≥)|AKV/J: 34
MECHANICAL PROPERTY UNDER HIGH TEMPERATURE
Yield strength σ0.2≥/MPa|200℃: 314
Yield strength σ0.2≥/MPa|300℃: 226
Yield strength σ0.2≥/MPa|350℃: 206
Yield strength σ0.2≥/MPa|400℃: 177
Yield strength σ0.2≥/MPa|450℃: 157
Yield strength σ0.2≥/MPa|500℃: —
Yield strength σ0.2≥/MPa|300℃: 226
Yield strength σ0.2≥/MPa|350℃: 206
Yield strength σ0.2≥/MPa|400℃: 177
Yield strength σ0.2≥/MPa|450℃: 157
Yield strength σ0.2≥/MPa|500℃: —
AVAILABLE SHAPES
Black bar /Flat bar / Square bar /Pipe, /Steel strip, /sheet
Bright - peeled + polishing, centerless grinding
Forged - ring, tube, pipe casing, discs, shaft
TYPICAL APPLICATIONS
Alloy structural steels are widely used in the filed of ship, vehicle, airplane, guided missile, weapons, railway, bridges, pressure vessel, machine tools, mechanical components with a bigger sectional size and so on.
Mechanical gears, gear shaft, main axis, valve rod
Mechanical parts - connecting rod, bolt and nut
Multidiameter shaft
Pressure vessel, seamless pipe
TECHNICAL SALES ASSISTANCE
If you meet further on any technical enquiry. pleased to Email (sales@ccsteels.com) or call our resident team of qualified production engineers.
PRODUCT PROFILE
Round bar / Wire rod (Diameter): 5.5mm to 800mm
Square bar / Flat bar: 10mm to 800mm
Plate / Sheet steel / Steel strip: 0.1mm to 1000mm
Width: 8mm to 1000mm
Length: random length or based on the customer's special requirement.
Forged steel shape: stepped shafts with flanks / discs /tubes /slugs /donuts /cubes /other different shapes based on OEM.
Hot search：1.0482
Previous page：P310GH
Last page：C35E & Ck35
Total list
Monthly rank
- 3438NCD4
- 3424CrMo5
- 3119CrNi5
- 2938B3
- 28ASTM A739 type B11
- 2826NiCrMoV11-5
- 2742Cr4Mo2
- 24S135
- 24EN 38
- 22EN20B