1.0485
2014-10-10 10:15:30 Origin： Remark：0 Click：
Steels 1.0485 Ex-stock, Alloy 1.0485 Suppliers, Properties 1.0485 Forging Bar Plate, Grade 1.0485 Technical specifications Melting, ESR & VAR technique, Heat treatment
MATERIAL DATA SHEET - W-Nr.1.0485
MATERIAL CATEGORY: High temperature structural steel
PRODUCT DESCRIPTION
Alloy structural steel is provided with higher yield strength, tensile strength, endurance strength, yield ratio (about 0.85 generally ) enough plasticity and toughness.
The concentration of alloy element of this kind of steel is quite high, mainly are corrosion resistant steel, heat resistant steel, wear resistant steel, and other special steels of physical and chemical properties. Alloy structural steel has preferable mechanical property than that of carbon structural steel, high performance of heat treatment especially.
The alloy is usually produced by EAF /VD /LF followed by electroslag refining (ESR) if necessary for special purpose. Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different level according to the buyers' requirements.
Bars are usually supplied bright in the annealed condition.
MATERIAL SPECIFICATIONS - DIN EN 10028-2 (2003), DIN 17755 (1983)
CHEMICAL COMPOSITION (mass weight - %)
Carbon, C (％): ≤ 0.23
Silicon, Si (％): ≤ 0.60
Manganese, Mn (％): 1.15 ~ 1.60
Phosphorus, P (％) ≤: 0.045
Sulfur, S (％) ≤: 0.045
Chromium, Cr (％): -
Molybdenum, Mo (％): -
Nickel, Ni (％): -
Silicon, Si (％): ≤ 0.60
Manganese, Mn (％): 1.15 ~ 1.60
Phosphorus, P (％) ≤: 0.045
Sulfur, S (％) ≤: 0.045
Chromium, Cr (％): -
Molybdenum, Mo (％): -
Nickel, Ni (％): -
MECHANICAL PROPERTIES - HOT WORKING, HEAT TREATMENT AND HARDNESS
Hot working temperature /℃: 1100～850
Heat treatment temperature /℃|annealing / normalizing : 880～940
Heat treatment temperature /℃|quenching: -
Heat treatment temperature /℃|tempering: -
HBS: -
Tensile strength, (≥) Rm / MPa: 510～610
Yield strength, (≥) Rp0.2 / MPa: 335
Elongation, (≥)| δ5 (%): 19
Reduction of area, (≥) | AKv / J: 31
Heat treatment temperature /℃|annealing / normalizing : 880～940
Heat treatment temperature /℃|quenching: -
Heat treatment temperature /℃|tempering: -
HBS: -
Tensile strength, (≥) Rm / MPa: 510～610
Yield strength, (≥) Rp0.2 / MPa: 335
Elongation, (≥)| δ5 (%): 19
Reduction of area, (≥) | AKv / J: 31
MECHANICAL PROPERTY UNDER HIGH TEMPERATURE
Yield strength σ0.2≥/MPa|200℃: 294
Yield strength σ0.2≥/MPa|300℃: 245
Yield strength σ0.2≥/MPa|350℃: 226
Yield strength σ0.2≥/MPa|400℃: 206
Yield strength σ0.2≥/MPa|450℃: —
Yield strength σ0.2≥/MPa|500℃: —
Yield strength σ0.2≥/MPa|300℃: 245
Yield strength σ0.2≥/MPa|350℃: 226
Yield strength σ0.2≥/MPa|400℃: 206
Yield strength σ0.2≥/MPa|450℃: —
Yield strength σ0.2≥/MPa|500℃: —
TYPICAL APPLICATIONS
Alloy structural steels are widely used in the filed of ship, vehicle, airplane, guided missile, weapons, railway, bridges, pressure vessel, machine tools, mechanical components with a bigger sectional size and so on.
Mechanical gears, gear shaft, main axis, valve rod.
Mechanical parts - connecting rod, bolt and nut.
Multidiameter shaft, Pressure vessel.
TECHNICAL SALES ASSISTANCE
If you meet further on any technical enquiry. pleased to email (sales@ccsteels.com) or call our resident team of qualified production engineers.
PRODUCT PROFILE & DIMENSIONS
Round bar / Disc (diameter): 5.5mm to 800mm
Square bar / Flat bar: 10mm to 1000mm
Plate / Sheet steel / Steel strip: 0.5mm to 1000mm
Width: 8mm to 1000mm
Length: random length or based on the customer's special requirement.
Forged steel shape: stepped shaft, and other different shapes based on OEM.
Hot search：1.0485
Total list
Monthly rank
- 3438NCD4
- 3424CrMo5
- 3119CrNi5
- 2938B3
- 28ASTM A739 type B11
- 2826NiCrMoV11-5
- 2742Cr4Mo2
- 24S135
- 24EN 38
- 22EN20B