EN23
2020-10-07 07:51:34 Origin： Remark：0 Click：
BS970 Part 3 of High Tensile Steel EN23 Round bar, flat bar, Forgings EN 23 Steelmaking, Blooming, Hot forging, Hot rolling, Heat treatment
TECHNICAL DATA SHEET - EN23 & EN 23
MELTING: EF + Consumable electrode remelted
OFFICIAL TEST REPORT - issued by TUV - SGS - BV
OFFICIAL TEST REPORT - issued by TUV - SGS - BV
CHEMICAL COMPOSITIONS (mass weight - %)
Carbon, C (％): 0.25 ~ 0.35
Manganese, Mn (％): 0.45 ~ 0.70
Silicon, Si (％): 0.10 ~ 0.35
Phosphorus, P (％)≤: 0.035
Sulfur, S (％)≤: 0.015
Chromium, Cr (%): 0.50 ~ 1.00
Nickel, Ni (%): 3.25 ~ 3.75
Molybdenum, Mo (%): 0.40 ~ 0.80
MECHANICAL PROPERTY AND HARDNESS
Quenching temperature /℃: 830, oil
Tempering temperature /℃: 480, water or oil
Tensile strength, Rm ≥ MPa: 850 ~ 1000
Carbon, C (％): 0.25 ~ 0.35
Manganese, Mn (％): 0.45 ~ 0.70
Silicon, Si (％): 0.10 ~ 0.35
Phosphorus, P (％)≤: 0.035
Sulfur, S (％)≤: 0.015
Chromium, Cr (%): 0.50 ~ 1.00
Nickel, Ni (%): 3.25 ~ 3.75
Molybdenum, Mo (%): 0.40 ~ 0.80
MECHANICAL PROPERTY AND HARDNESS
Quenching temperature /℃: 830, oil
Tempering temperature /℃: 480, water or oil
Tensile strength, Rm ≥ MPa: 850 ~ 1000
Yield strength, Rp0.2 ≥ MPa: 735
Elongation, A5 ≥ (％): 20.0
Reduction of area, Z ≥ (％): -
Hardness in annealed condition: HB295 max.
MELTING PROCESS & APPLICATION
This alloy is generally smelt in Electric Arc Furnace (EAF), EAF+LF+VD, BEF + Electroslag remelting (ESR).
For a purpose of superior quality, it should be smelt via technology of vacuum refining or by agreement.
It is suitable for applications such as high tensile shafts, bolts and nuts, gears, pinions spindles and so on.
AVAILABLE FORMS & DIMENSIONS
Round bar & Disc (diameter): 5.5 ~ 550mm
Square bar / Flat bar: 10 ~ 800mm
Length: Fixed length or random length or based on the customer's special requirement.
Other different shapes based on OEM.
TECHNICAL SALES ASSISTANCE & SERVICE
If you meet further on any technical enquiry, pleased to EMAIL (sales@ccsteels.com) our resident team of qualified production engineers.
Elongation, A5 ≥ (％): 20.0
Reduction of area, Z ≥ (％): -
Hardness in annealed condition: HB295 max.
MELTING PROCESS & APPLICATION
This alloy is generally smelt in Electric Arc Furnace (EAF), EAF+LF+VD, BEF + Electroslag remelting (ESR).
For a purpose of superior quality, it should be smelt via technology of vacuum refining or by agreement.
It is suitable for applications such as high tensile shafts, bolts and nuts, gears, pinions spindles and so on.
AVAILABLE FORMS & DIMENSIONS
Round bar & Disc (diameter): 5.5 ~ 550mm
Square bar / Flat bar: 10 ~ 800mm
Length: Fixed length or random length or based on the customer's special requirement.
Other different shapes based on OEM.
TECHNICAL SALES ASSISTANCE & SERVICE
If you meet further on any technical enquiry, pleased to EMAIL (sales@ccsteels.com) our resident team of qualified production engineers.
Hot search：EN23
Previous page：F317L
Last page：ASTM A182 Gr.S31703
Total list
Monthly rank
- 3438NCD4
- 3424CrMo5
- 3119CrNi5
- 2938B3
- 28ASTM A739 type B11
- 2826NiCrMoV11-5
- 2742Cr4Mo2
- 24S135
- 24EN 38
- 22EN20B