AISI 601
2020-11-06 10:33:13 Origin： Remark：0 Click：
AMS 6103L material Specifications AISI 601 Round bar, Flat bar, Plate and forgings AISI 601 forging, Hot rolling, Heat treatment, Cold worked
TECHNICAL DATA SHEET - AISI 601
MELTING: Consumable electrode remelted
OFFICIAL TEST REPORT - issued by TUV - SGS - BV
OFFICIAL TEST REPORT - issued by TUV - SGS - BV
CHEMICAL COMPOSITIONS (mass weight - %)
Carbon, C (％): 0.40 ~ 0.60
Manganese, Mn (％): 0.40 ~ 0.70
Silicon, Si (％): 0.15 ~ 0.35
Phosphorus, P (％) ≤: 0.025
Sulfur, S (％) ≤: 0.025
Chromium, Cr (%): 0.80 ~ 1.10
Vanandium, V (%): 0.25 ~ 0.35
Molybdenum, Mo (%): 0.45 ~ 0.65
Carbon, C (％): 0.40 ~ 0.60
Manganese, Mn (％): 0.40 ~ 0.70
Silicon, Si (％): 0.15 ~ 0.35
Phosphorus, P (％) ≤: 0.025
Sulfur, S (％) ≤: 0.025
Chromium, Cr (%): 0.80 ~ 1.10
Vanandium, V (%): 0.25 ~ 0.35
Molybdenum, Mo (%): 0.45 ~ 0.65
Nickel, Ni (%): ≤ 0.25
Copper, Cu (%): ≤ 0.35
MECHANICAL PROPERTY AND HARDNESS
Quenching temperature / ℃:
Tempering temperature /℃:200
Tensile strength, σb ≥ MPa: 785
MECHANICAL PROPERTY AND HARDNESS
Quenching temperature / ℃:
Tempering temperature /℃:200
Tensile strength, σb ≥ MPa: 785
Yield strength, σ0.2 ≥ MPa: 590
Elongation, δ5 ≥( ％): 12.0
Reduction of area, ф ≥ (％): 50
Hardness in condition of annealing +A: HB229 max.
MELTING PROCESS & APPLICATION
This alloy is generally smelt in Electric Arc Furnace (EAF), EAF+LF+VD, BEF + Electroslag remelting (ESR).
For a purpose of superior quality, it should be smelt via technology of vacuum refining or by agreement.
It is suitable for applications such as high tensile shafts, bolts and nuts, gears, pinions spindles and so on.
AVAILABLE FORMS & DIMENSIONS
Round bar / rod / disc: 5.5mm to 850mm
Square bar / Flat bar: 10mm to 800mm
Length: Fixed length or random length or based on the customer's special requirement.
Other different shapes based on OEM.
TECHNICAL SALES ASSISTANCE & SERVICE
If you meet further on any technical enquiry, pleased to EMAIL our resident team of qualified production engineers. E-mail: sales@ccsteels.com.
Elongation, δ5 ≥( ％): 12.0
Reduction of area, ф ≥ (％): 50
Hardness in condition of annealing +A: HB229 max.
MELTING PROCESS & APPLICATION
This alloy is generally smelt in Electric Arc Furnace (EAF), EAF+LF+VD, BEF + Electroslag remelting (ESR).
For a purpose of superior quality, it should be smelt via technology of vacuum refining or by agreement.
It is suitable for applications such as high tensile shafts, bolts and nuts, gears, pinions spindles and so on.
AVAILABLE FORMS & DIMENSIONS
Round bar / rod / disc: 5.5mm to 850mm
Square bar / Flat bar: 10mm to 800mm
Length: Fixed length or random length or based on the customer's special requirement.
Other different shapes based on OEM.
TECHNICAL SALES ASSISTANCE & SERVICE
If you meet further on any technical enquiry, pleased to EMAIL our resident team of qualified production engineers. E-mail: sales@ccsteels.com.
Total list
Monthly rank
- 3438NCD4
- 3424CrMo5
- 3119CrNi5
- 2938B3
- 28ASTM A739 type B11
- 2826NiCrMoV11-5
- 2742Cr4Mo2
- 24S135
- 24EN 38
- 22EN20B