11CrMo9-10
2014-10-11 09:44:27 Origin： Remark：0 Click：
Description 11CrMo9-10 Ex-stock, Inventory 11CrMo9-10 Suppliers, 11CrMo9-10 Forgings Bar Plate - Technical Specifications Melting, ESR & VAR technique, Hot blooming, Hot forging, Hot rolling, Heat treatment, Straightening, Ultrasonic flaw detection test.
MATERIAL DATA SHEET - Grade DIN 11CrMo9-10
MATERIAL CATEGORY: High temperature structural steel
PRODUCT DESCRIPTION
Alloy structural steel is provided with higher yield strength, tensile strength, endurance strength, yield ratio (about 0.85 generally ) enough plasticity and toughness.
The concentration of alloy element of this kind of steel is quite high, mainly are corrosion resistant steel, heat resistant steel, wear resistant steel, and other special steels of physical and chemical properties. Alloy structural steel has preferable mechanical property than that of carbon structural steel, high performance of heat treatment especially.
The alloy is usually produced by EAF /VD /LF followed by electroslag refining (ESR) if necessary for special purpose.
Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different level according to the buyers' requirements.
Bars are usually supplied bright in the annealed condition.
Final heat treatment - heat treatment / QT
MATERIAL SPECIFICATIONS - DIN EN 10028-2 (2003), DIN 17755 (1983)
CHEMICAL COMPOSITION (Mass weight - %)
C (％): 0.08 ~ 0.15
Si (％): ≤ 0.50
Mn (％): 0.40 ~ 0.80
P (％)≤: 0.030
S (％)≤: 0.025
Cr (％): 2.00 ~ 2.50
Mo (％): 0.90 ~ 1.10
Ni (％): —
Other (％): Cu ≤0.30, +Al
Si (％): ≤ 0.50
Mn (％): 0.40 ~ 0.80
P (％)≤: 0.030
S (％)≤: 0.025
Cr (％): 2.00 ~ 2.50
Mo (％): 0.90 ~ 1.10
Ni (％): —
Other (％): Cu ≤0.30, +Al
MECHANICAL PROPERTIES - HOT WORKING, HEAT TREATMENT AND HARDNESS
Hot working temperature /℃: 1100～850
Heat treatment temperature /℃|annealing / normalizing : 650~700
Heat treatment temperature /℃|quenching: 920~980 air or oil
Heat treatment temperature /℃|tempering: 650~750
HBS: -
(≥)| σb/MPa: 520 ~ 670
(≥)| σs/MPa: 310
(≥)| δ5(%): 18.0
(≥)| AKV/J: 40
Heat treatment temperature /℃|annealing / normalizing : 650~700
Heat treatment temperature /℃|quenching: 920~980 air or oil
Heat treatment temperature /℃|tempering: 650~750
HBS: -
(≥)| σb/MPa: 520 ~ 670
(≥)| σs/MPa: 310
(≥)| δ5(%): 18.0
(≥)| AKV/J: 40
MECHANICAL PROPERTY UNDER HIGH TEMPERATURE
Yield strength σ0.2≥/MPa|200℃: -
Yield strength σ0.2≥/MPa|300℃: 225
Yield strength σ0.2≥/MPa|350℃: 225
Yield strength σ0.2≥/MPa|400℃: 215
Yield strength σ0.2≥/MPa|450℃: 205
Yield strength σ0.2≥/MPa|500℃: 195
Yield strength σ0.2≥/MPa|300℃: 225
Yield strength σ0.2≥/MPa|350℃: 225
Yield strength σ0.2≥/MPa|400℃: 215
Yield strength σ0.2≥/MPa|450℃: 205
Yield strength σ0.2≥/MPa|500℃: 195
AVAILABLE SHAPES
Round bar / flat bar / hollow bar / strip / sheet
Bright - peeled + polishing, centerless grinding
Forged - ring, tube, pipe casing, discs, shaft
PRODUCT PROFILE
Round bar / Wire rod (Diameter): 5.5mm to 800mm
Square bar / Flat bar: 10mm to 1000mm
Plate / Sheet steel / Steel strip: 0.5mm to 300mm
Width: 8mm to 1000mm
Length: random length or based on the customer's special requirement.
Forged steel shape: stepped shafts with flanks / discs /tubes /slugs /donuts /cubes /other different shapes based on OEM.
TYPICAL APPLICATIONS
Alloy structural steels are widely used in the filed of ship, vehicle, airplane, guided missile, weapons, railway, bridges, pressure vessel, machine tools, mechanical components with a bigger sectional size and so on.
Mechanical gears, gear shaft, main axis, valve rod.
Mechanical parts - connecting rod, bolt and nut.
Multidiameter shaft and pressure vessel.
TECHNICAL SALES ASSISTANCE
If you meet further on any technical enquiry. pleased to Email (sales@ccsteels.com) or call our resident team of qualified production engineers.
Hot search：11CrMo9-10
Total list
Monthly rank
- 3438NCD4
- 3424CrMo5
- 3119CrNi5
- 2938B3
- 28ASTM A739 type B11
- 2826NiCrMoV11-5
- 2742Cr4Mo2
- 24S135
- 24EN 38
- 22EN20B