EN 56A
2021-05-08 10:01:54 Origin： Remark：0 Click：
BS 970 Part 5 Material standards EN 56A Round bar, Flat bar, Forgings EN 56B Heat treatment, 100% Ultrasonic flaw detection test, Cold worked or machined.
TECHNICAL DATA SHEET - Grade EN 56A
MELTING: Consumable electrode remelted
OFFICIAL TEST REPORT - issued by TUV - SGS - BV
OFFICIAL TEST REPORT - issued by TUV - SGS - BV
CHEMICAL COMPOSITIONS (mass weight - %)
Carbon, C (％): 0.08 ~ 0.15
Manganese, Mn (％): ≤ 1.50
Silicon, Si (％): ≤ 1.50
Phosphorus, P (％)≤: 0.035
Sulfur, S (％)≤: 0.025
Chromium, Cr (%): 12.0 ~ 14.0
Nickel, Ni (%): 0.80 ~ 1.30
MECHANICAL PROPERTY AND HARDNESS
Quenching temperature /℃:-
Tempering temperature /℃:-
Tensile strength,σb/≥ MPa: 695
Carbon, C (％): 0.08 ~ 0.15
Manganese, Mn (％): ≤ 1.50
Silicon, Si (％): ≤ 1.50
Phosphorus, P (％)≤: 0.035
Sulfur, S (％)≤: 0.025
Chromium, Cr (%): 12.0 ~ 14.0
Nickel, Ni (%): 0.80 ~ 1.30
MECHANICAL PROPERTY AND HARDNESS
Quenching temperature /℃:-
Tempering temperature /℃:-
Tensile strength,σb/≥ MPa: 695
Yield strength, σ0.2/≥ MPa: 275
Elongation, δ ≥(％): 20.0
Reduction of area, ф ≥(％): -
Hardness under condition of annealing +A: HB255 max.
MELTING PROCESS & APPLICATION
This alloy is generally smelt in Electric Arc Furnace (EAF), EAF+LF+VD, BEF + Electroslag remelting (ESR). For a purpose of superior quality, it should be smelt via technology of vacuum refining or by agreement.
It is suitable for applications such as high tensile shafts, bolts and nuts, gears, pinions spindles and so on.
AVAILABLE FORMS & DIMENSIONS
Round bar & Disc: 5.5mm to 450mm
Square bar / Flat bar: 10mm to 600mm
Length: Fixed length or random length or based on the customer's special requirement.
Other different shapes based on OEM.
TECHNICAL SALES ASSISTANCE & SERVICE
If you meet further on any technical enquiry, pleased to EMAIL our resident team of qualified production engineers. E-mail: sales@ccsteels.com.
Reduction of area, ф ≥(％): -
Hardness under condition of annealing +A: HB255 max.
MELTING PROCESS & APPLICATION
This alloy is generally smelt in Electric Arc Furnace (EAF), EAF+LF+VD, BEF + Electroslag remelting (ESR). For a purpose of superior quality, it should be smelt via technology of vacuum refining or by agreement.
It is suitable for applications such as high tensile shafts, bolts and nuts, gears, pinions spindles and so on.
AVAILABLE FORMS & DIMENSIONS
Round bar & Disc: 5.5mm to 450mm
Square bar / Flat bar: 10mm to 600mm
Length: Fixed length or random length or based on the customer's special requirement.
Other different shapes based on OEM.
TECHNICAL SALES ASSISTANCE & SERVICE
If you meet further on any technical enquiry, pleased to EMAIL our resident team of qualified production engineers. E-mail: sales@ccsteels.com.
Total list
Monthly rank
- 3438NCD4
- 3424CrMo5
- 3119CrNi5
- 2938B3
- 28ASTM A739 type B11
- 2826NiCrMoV11-5
- 2742Cr4Mo2
- 24S135
- 24EN 38
- 22EN20B