Inventory AMS 6342 Datasheet, Ex-stock Suppliers AMS 6342 Chemical, AMS 6342 Property from Steelmaking, Blooming, Hot forging, Hot rolling, Heat treatment, Straightening, 100% Ultrasonic flaw detection test, Cold working or Machined. All of these materials conform to Military standard, nuclear power. 100% Ultrasonic test ASTM E2375 /SAE AMS 2154 /SEP 1923 /GB/T 4162 /EN 10228-3.
TECHNICAL SPECIFICATIONS - Grade AMS 6342
MATERIAL FORM - round bar, flat bar, forgings
TECHNICAL STANDARDS - AMS 6342K
MATERIAL TYPE - Aerospace Material Specification - Structural steel
Official Test Certificate Report: issued by TUV - SGS - BV
HS Code For Customs - 72284000 / 72285000
CHEMICAL COMPOSITION ( MASS WEIGHT %)
C (％): 0.38 ~ 0.43
Si (％): 0.15 ~ 0.35
Mn (％): 0.75 ~ 1.00
P (％) ≤: 0.025
S (％) ≤: 0.020
Cr (％): 0.70 ~ 0.90
Ni (％): 0.85 ~ 1.15
C (％): 0.38 ~ 0.43
Si (％): 0.15 ~ 0.35
Mn (％): 0.75 ~ 1.00
P (％) ≤: 0.025
S (％) ≤: 0.020
Cr (％): 0.70 ~ 0.90
Ni (％): 0.85 ~ 1.15
Cu (％): ≤ 0.35
Mo (%): 0.20 ~ 0.30
MECHANICAL PROPERTY UNDER ROOM TEMP.
Condition: Quenched and tempered
Condition: Quenched and tempered
Tensile strength, σb/ ≥ MPa: 1085
Yield strength, σ0.2/ ≥ MPa: 975
Elongation, δ (％) ≥: 15.5
Reduction of area, ф (％) ≥: 55.0
Hardness under solution anneal ≤ (HBW): 226 Max.
Yield strength, σ0.2/ ≥ MPa: 975
Elongation, δ (％) ≥: 15.5
Reduction of area, ф (％) ≥: 55.0
Hardness under solution anneal ≤ (HBW): 226 Max.
PRODUCT DESCRIPTION
The alloy is usually produced by BEF / EAF followed by electroslag refining (ESR), Vacuum Arc Melting (VAR) if necessary for special purpose.
Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' specific requirements.
Round bar / Wire rod (Diameter): 5.5mm to 500mm
Square bar / Flat bar: 3mm to 600mm
Length: Fixed length or random length or based on the customer's special requirement.
Heavy/middle plate via hot rolled: T60 - 300mm X W50 - 1200mm X L1000-12000mm
Forging piece: stepped shafts with flanks / discs and other different shapes based on OEM.
The alloy is usually produced by BEF / EAF followed by electroslag refining (ESR), Vacuum Arc Melting (VAR) if necessary for special purpose.
Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' specific requirements.
Round bar / Wire rod (Diameter): 5.5mm to 500mm
Square bar / Flat bar: 3mm to 600mm
Length: Fixed length or random length or based on the customer's special requirement.
Heavy/middle plate via hot rolled: T60 - 300mm X W50 - 1200mm X L1000-12000mm
Forging piece: stepped shafts with flanks / discs and other different shapes based on OEM.
TECHNICAL SALES ASSISTANCE & SERVICE
If you meet further on any technical enquiry or help, pleased to EMAIL our resident team of qualified production engineers, Email: sales@ccsteels.com.
If you meet further on any technical enquiry or help, pleased to EMAIL our resident team of qualified production engineers, Email: sales@ccsteels.com.
Total list
Monthly rank
- 3438NCD4
- 3424CrMo5
- 3119CrNi5
- 2938B3
- 28ASTM A739 type B11
- 2826NiCrMoV11-5
- 2742Cr4Mo2
- 24S135
- 24EN 38
- 22EN20B