EN 353
2021-12-23 13:53:58 Origin： Remark：0 Click：
Description EN 353 Datasheet, Stocklist EN 353 Chemical, Inventory EN 353 Property Steelmaking, Blooming, Hot forging, Hot rolling, Heat treatment, Straightening, 100% Ultrasonic flaw detection test, Cold working or Machined. All of these materials conform to Military standard, nuclear power. 100% Ultrasonic test ASTM E2375 /SAE AMS 2154 /SEP 1923 /GB/T 4162 /EN 10228-3.
TECHNICAL SPECIFICATION - BS970 Part 7
MELTING PROCESS - Consumable electrode remelted steel
MELTING PROCESS - Consumable electrode remelted steel
H S CODE For Customs - 7228 4000 / 7228 5000 / 7228 6000
OFFICIAL TEST REPORT - issued by TUV - SGS - BV
CHEMICAL COMPOSITIONS ( Mass Weight - %)
C (％): ≤ 0.20
OFFICIAL TEST REPORT - issued by TUV - SGS - BV
CHEMICAL COMPOSITIONS ( Mass Weight - %)
C (％): ≤ 0.20
Mn (％): 0.60 ~ 1.00
Si (％): 0.10 ~ 0.35
Si (％): 0.10 ~ 0.35
P (％)≤: 0.030
S (％)≤: 0.015
Cr (%): 0.75 ~ 1.25
Ni (%): 1.00 ~ 1.50
Mo (%): 0.08 ~ 0.15
S (％)≤: 0.015
Cr (%): 0.75 ~ 1.25
Ni (%): 1.00 ~ 1.50
Mo (%): 0.08 ~ 0.15
MECHANICAL PROPERTY UNDER ROOM TEMP.
Quenching temperature /℃: -
Tempering temperature /℃: -
Tensile strength,σb/≥ MPa: 985
Yield strength, σ0.2/≥ MPa: 775
Elongation, δ ≥(％): 12.0
Reduction of area, ф ≥(％): -
Hardness in condition of annealing +A: HB269
MELTING PROCESS & APPLICATION
This alloy is generally smelt in Electric Arc Furnace (EAF), EAF+LF+VD, EF + Electroslag remelting (ESR). For a purpose of superior quality, it should be smelt via technology of vacuum refining or by agreement. It is suitable for applications such as high tensile shafts, bolts and nuts, gears, pinions spindles and so on.
Quenching temperature /℃: -
Tempering temperature /℃: -
Tensile strength,σb/≥ MPa: 985
Yield strength, σ0.2/≥ MPa: 775
Elongation, δ ≥(％): 12.0
Reduction of area, ф ≥(％): -
Hardness in condition of annealing +A: HB269
MELTING PROCESS & APPLICATION
This alloy is generally smelt in Electric Arc Furnace (EAF), EAF+LF+VD, EF + Electroslag remelting (ESR). For a purpose of superior quality, it should be smelt via technology of vacuum refining or by agreement. It is suitable for applications such as high tensile shafts, bolts and nuts, gears, pinions spindles and so on.
AVAILABLE FORMS & DIMENSIONS
Round bar: 5.5mm to 450mm
Square bar / Flat bar: 10mm to 600mm
Rolled / forged plate: 10mm to 600mm
Length: Fixed length or random length or based on the customer's special requirement.
Stock over 60 grades with a competitive price, along with cutting service for specific requirement.
Round bar: 5.5mm to 450mm
Square bar / Flat bar: 10mm to 600mm
Rolled / forged plate: 10mm to 600mm
Length: Fixed length or random length or based on the customer's special requirement.
Stock over 60 grades with a competitive price, along with cutting service for specific requirement.
Customizing special material is welcome.
TECHNICAL SALES ASSISTANCE & SERVICE
If you meet further on any technical enquiry or help, pleased to EMAIL our resident team of qualified production engineers. E-mail: sales@ccsteels.com.
Total list
Monthly rank
- 3438NCD4
- 3424CrMo5
- 3119CrNi5
- 2938B3
- 28ASTM A739 type B11
- 2826NiCrMoV11-5
- 2742Cr4Mo2
- 24S135
- 24EN 38
- 22EN20B