21CrMoVH
2024-01-24 15:10:27 Origin： Remark：0 Click：
IS 1570-5 Material Specification Refractory Steel 21CrMoVH Round bar, flat bar, plate and forgings Instock 21CrMoVH Heat treatment, Rough machining.
MATERIAL TECHNICAL DATASHEET - Grade 21CrMoVH
Official Test Report: issued by TUV - SGS - BV
Special Melting Practice - BEF + AOD / + ESR
HS Code For Customs - 72284000 / 72286000
Available stock on hand - Round bar Diam. 80 ~ 155mm
Material Specifications - refractory Steel IS 1570-5
CHEMICAL COMPOSITION (mass weight - %)
Carbon, C (％): 0.17 ~ 0.25
Silicon, Si (％): ≤ 0.40
Manganese, Mn (％): 0.40 ~ 0.80
Phosphorus, P (％) ≤: 0.030
Sulfur, S (％) ≤: 0.030
Chromium, Cr (％): 1.20 ~ 1.50
Nickel, Ni (％): ≤ 0.60
Molybdenum, Mo (％): 0.65 ~ 0.80
Vanadium, V (%): 0.25 ~ 0.35
Official Test Report: issued by TUV - SGS - BV
Special Melting Practice - BEF + AOD / + ESR
HS Code For Customs - 72284000 / 72286000
Available stock on hand - Round bar Diam. 80 ~ 155mm
Material Specifications - refractory Steel IS 1570-5
CHEMICAL COMPOSITION (mass weight - %)
Carbon, C (％): 0.17 ~ 0.25
Silicon, Si (％): ≤ 0.40
Manganese, Mn (％): 0.40 ~ 0.80
Phosphorus, P (％) ≤: 0.030
Sulfur, S (％) ≤: 0.030
Chromium, Cr (％): 1.20 ~ 1.50
Nickel, Ni (％): ≤ 0.60
Molybdenum, Mo (％): 0.65 ~ 0.80
Vanadium, V (%): 0.25 ~ 0.35
MECHANICAL PROPERTY AT ROOM TEMPERATURE
Forms: Round bar, flat bar, forgings and plate
Quenching temp: 920 ~ 980 ℃, water or oil cooling, tempering 680℃, air cooling.
Tensile strength, σb/≥ MPa: 585
Yield strength, σ0.2/MPa: 415
Elongation, δ ≥(％): 20.0
Reduction of area, ф ≥ (％): -
Hardness via annealing /HBW: 215
Forms: Round bar, flat bar, forgings and plate
Quenching temp: 920 ~ 980 ℃, water or oil cooling, tempering 680℃, air cooling.
Tensile strength, σb/≥ MPa: 585
Yield strength, σ0.2/MPa: 415
Elongation, δ ≥(％): 20.0
Reduction of area, ф ≥ (％): -
Hardness via annealing /HBW: 215
PRODUCT DESCRIPTION
The alloy is usually produced by EAF +LF + VD / AOD / EF followed by electroslag refining (ESR) / VAR if necessary for special purpose.
Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied black/bright in the annealed condition.
Final heat treatment - Quenched and tempered
The alloy is usually produced by EAF +LF + VD / AOD / EF followed by electroslag refining (ESR) / VAR if necessary for special purpose.
Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied black/bright in the annealed condition.
Final heat treatment - Quenched and tempered
TECHNICAL SALES ASSISTANCE
20+ years Focus On Special Steel Manufacturing and processing.
Stock over 60 grades with a competitive price, along with cutting service for specific requirement.
Customizing special material is welcome.
20+ years Focus On Special Steel Manufacturing and processing.
Stock over 60 grades with a competitive price, along with cutting service for specific requirement.
Customizing special material is welcome.
We closely cooperate with the professional inspection partners to strictly control the quality and improve the quality manage system, and guarantee the goods delivery each time. It is proved that we are worth of trusting and will be the strategic partner of the supplying chains in the special steels field.
If you meet further on any technical enquiry, pleased to EMAIL our resident team of qualified production engineers, Email: sales@ccsteels.com.
Hot search：21CrMoVH
Previous page：40CrMoH
Last page：XT122W6Mo5Cr4V3
Total list
Monthly rank
- 6124CrMo5
- 5542Cr4Mo2
- 52EN 14B
- 4838NCD4
- 47EN 38
- 4534CrNiMo4
- 44ASTM A739 Gr. B11
- 43EN 355
- 42X20CrMoV12-1
- 4240Cr4