High temperature structural steel 1.7709 Instock, Round bar 1.7709 Sheet, Inventory 1.7709 Forgings ESR melt, Blooming, Hot forging, Hot rolling, Heat treatment
MATERIAL DATASHEET - W-Nr 1.7709
MATERIAL CATEGORY - High temperature structural steel
PRODUCT DESCRIPTION
Alloy structural steel is provided with higher yield strength, tensile strength, endurance strength, yield ratio (about 0.85 generally ) enough plasticity and toughness.
The concentration of alloy element of this kind of steel is quite high, mainly are corrosion resistant steel, heat resistant steel, wear resistant steel, and other special steels of physical and chemical properties. Alloy structural steel has preferable mechanical property than that of carbon structural steel, high performance of heat treatment especially.
The alloy is usually produced by EAF /VD /LF followed by electroslag refining (ESR) if necessary for special purpose. Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different level according to the buyers' requirements.
Bars are usually supplied bright in the annealed condition.
Final heat treatment - Quenched and tempered.
MATERIAL SPECIFICATIONS - DIN EN 10028-2 (2003), DIN 17755 (1983)
CHEMICAL COMPOSITION (mass weight - %)
Carbon, C (％): 0.17 ~ 0.25
Silicon, Si (％): ≤ 0.40
Manganese, Mn (％): 0.40 ~ 0.80
Phosphorus, P (％) ≤: 0.030
Sulfur, S (％) ≤: 0.030
Chromium, Cr (％): 1.20 ~ 1.50
Molybdenum, Mo (％): 0.55 ~ 0.85
Nickel, Ni (％): ≤ 0.60
Vanadium, V (%): 0.20 ~ 0.35
Other (％): Al ≤ 0.030
MECHANICAL PROPERTIES - HOT WORKING, HEAT TREATMENT AND HARDNESS
Hot working temperature /℃: 1100～850
Heat treatment temperature /℃|annealing / normalizing : 650~730
Heat treatment temperature /℃|quenching: 890~940 oil or air
Heat treatment temperature /℃|tempering: 680~720
HBW: 205~250
Tensile strength, (≥) Rm / MPa: 700～850
Yield strength, (≥) Rp0.2 / MPa: 550
Elongation, (≥) A5 (%): 20.0
Impact, (≥) |AKv / J: 69
MECHANICAL PROPERTIES UNDER HIGH TEMP.
Yield strength σ0.2≥/MPa|200℃: 500
Yield strength σ0.2≥/MPa|300℃: 460
Yield strength σ0.2≥/MPa|350℃: 441
Yield strength σ0.2≥/MPa|400℃: 412
Yield strength σ0.2≥/MPa|450℃: 372
Yield strength σ0.2≥/MPa|500℃: 334
AVAILABLE SHAPES
Round bar / flat bar / hollow bar / steel strip / forgings
Bright - peeled + polishing, centerless grinding
Forged - ring, tube, pipe casing, discs, shaft
TYPICAL APPLICATIONS
Alloy structural steels are widely used in the filed of ship, vehicle, airplane, guided missile, weapons, railway, bridges, pressure vessel, machine tools, mechanical components with a bigger sectional size and so on.
Mechanical gears, gear shaft, main axis, valve rod.
Mechanical parts - connecting rod, bolt and nut.
Multidiameter shaft.
Pressure vessel, seamless pipe.
PROFILE AND DIMENSIONS
Round bar / Wire rod (Diameter): 5.5mm to 500mm
Square bar / Flat bar: 3mm to 1000mm
Plate / Sheet steel / Steel strip: 0.1mm to 1500mm
Width: 8mm to 1500mm
Length: random length or based on the customer's special requirement.
Forged steel shape: stepped shafts, other different shapes based on OEM.
TECHNICAL SALES ASSISTANCE
If you meet further on any technical enquiry, pleased to email or call our resident team of qualified production engineers, Email: sales@ccsteels.com.
MATERIAL CATEGORY - High temperature structural steel
PRODUCT DESCRIPTION
Alloy structural steel is provided with higher yield strength, tensile strength, endurance strength, yield ratio (about 0.85 generally ) enough plasticity and toughness.
The concentration of alloy element of this kind of steel is quite high, mainly are corrosion resistant steel, heat resistant steel, wear resistant steel, and other special steels of physical and chemical properties. Alloy structural steel has preferable mechanical property than that of carbon structural steel, high performance of heat treatment especially.
The alloy is usually produced by EAF /VD /LF followed by electroslag refining (ESR) if necessary for special purpose. Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different level according to the buyers' requirements.
Bars are usually supplied bright in the annealed condition.
Final heat treatment - Quenched and tempered.
MATERIAL SPECIFICATIONS - DIN EN 10028-2 (2003), DIN 17755 (1983)
CHEMICAL COMPOSITION (mass weight - %)
Carbon, C (％): 0.17 ~ 0.25
Silicon, Si (％): ≤ 0.40
Manganese, Mn (％): 0.40 ~ 0.80
Phosphorus, P (％) ≤: 0.030
Sulfur, S (％) ≤: 0.030
Chromium, Cr (％): 1.20 ~ 1.50
Molybdenum, Mo (％): 0.55 ~ 0.85
Nickel, Ni (％): ≤ 0.60
Vanadium, V (%): 0.20 ~ 0.35
Other (％): Al ≤ 0.030
MECHANICAL PROPERTIES - HOT WORKING, HEAT TREATMENT AND HARDNESS
Hot working temperature /℃: 1100～850
Heat treatment temperature /℃|annealing / normalizing : 650~730
Heat treatment temperature /℃|quenching: 890~940 oil or air
Heat treatment temperature /℃|tempering: 680~720
HBW: 205~250
Tensile strength, (≥) Rm / MPa: 700～850
Yield strength, (≥) Rp0.2 / MPa: 550
Elongation, (≥) A5 (%): 20.0
Impact, (≥) |AKv / J: 69
MECHANICAL PROPERTIES UNDER HIGH TEMP.
Yield strength σ0.2≥/MPa|200℃: 500
Yield strength σ0.2≥/MPa|300℃: 460
Yield strength σ0.2≥/MPa|350℃: 441
Yield strength σ0.2≥/MPa|400℃: 412
Yield strength σ0.2≥/MPa|450℃: 372
Yield strength σ0.2≥/MPa|500℃: 334
AVAILABLE SHAPES
Round bar / flat bar / hollow bar / steel strip / forgings
Bright - peeled + polishing, centerless grinding
Forged - ring, tube, pipe casing, discs, shaft
TYPICAL APPLICATIONS
Alloy structural steels are widely used in the filed of ship, vehicle, airplane, guided missile, weapons, railway, bridges, pressure vessel, machine tools, mechanical components with a bigger sectional size and so on.
Mechanical gears, gear shaft, main axis, valve rod.
Mechanical parts - connecting rod, bolt and nut.
Multidiameter shaft.
Pressure vessel, seamless pipe.
PROFILE AND DIMENSIONS
Round bar / Wire rod (Diameter): 5.5mm to 500mm
Square bar / Flat bar: 3mm to 1000mm
Plate / Sheet steel / Steel strip: 0.1mm to 1500mm
Width: 8mm to 1500mm
Length: random length or based on the customer's special requirement.
Forged steel shape: stepped shafts, other different shapes based on OEM.
TECHNICAL SALES ASSISTANCE
If you meet further on any technical enquiry, pleased to email or call our resident team of qualified production engineers, Email: sales@ccsteels.com.
Hot search：1.7709
Previous page：21CrMoV5-7
Last page：21CrMoV5-11
Total list
Monthly rank
- 3438NCD4
- 3424CrMo5
- 3119CrNi5
- 2938B3
- 28ASTM A739 type B11
- 2826NiCrMoV11-5
- 2742Cr4Mo2
- 24S135
- 24EN 38
- 22EN20B