20Cr1Mo1V1A
2024-04-10 09:17:28 Origin： Remark：0 Click：
Specificatioin GB/T 20410 Steels for Turbine Mechanical Parts at high tmperature 20Cr1Mo1V1A Stock Available Round bar, Flat bar 20Cr1Mo1V1A bolts and nuts
TECHNICAL DATASHEET - GB 20Cr1Mo1V1A
MATERIAL CATEGORY - Steels for Turbine bolts and nuts at high tmperature
PRODUCT DESCRIPTION
The alloy is usually produced by EAF + VD + LF followed by electroslag refining (ESR) if necessary for special purpose. Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different level according to the buyers' requirements.
Bars are usually supplied bright in the annealed condition, or bright annealing specially.
Final heat treatment - Quenched and tempered.
Bars are usually supplied bright in the annealed condition, or bright annealing specially.
Final heat treatment - Quenched and tempered.
Working Temperature: 470 ℃ Max.
Stock Available: Round bar diam. 40 ~ 180mm
MATERIAL CATEGORY - Steels for Turbine bolts and nuts at high tmperature
PRODUCT DESCRIPTION
The alloy is usually produced by EAF + VD + LF followed by electroslag refining (ESR) if necessary for special purpose. Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different level according to the buyers' requirements.
Bars are usually supplied bright in the annealed condition, or bright annealing specially.
Final heat treatment - Quenched and tempered.
Bars are usually supplied bright in the annealed condition, or bright annealing specially.
Final heat treatment - Quenched and tempered.
Working Temperature: 470 ℃ Max.
Stock Available: Round bar diam. 40 ~ 180mm
MATERIAL SPECIFICATIONS - GB/T 20410 - 2006
CHEMICAL COMPOSITION (mass weight - %)
Carbon, C (％): 0.18 ~ 0.25
Silicon, Si (％): ≤ 0.35
Manganese, Mn (％): ≤ 0.50
Phosphorus, P (％) ≤: 0.025
Sulfur, S (％) ≤: 0.020
Chromium, Cr (％): 1.00 ~ 1.30
Molybdenum, Mo (％): 0.80 ~ 1.10
Nickel, Ni (%): ≤ 0.60
Copper, Cu (％): ≤ 0.25
Vanadium, V (%): 0.70 ~ 1.10
Titanium, Ti (%): -
Boron, B (%): -
Nitrogen, N (%): -
MECHANICAL PROPERTIES - HOT WORKING, HEAT TREATMENT AND HARDNESS
Heat treatment temperature /℃| annealing: 690 ~ 710 air cooling.
Heat treatment temperature /℃| Normalizing: -
Heat treatment temperature /℃| Quenching: 1000 Oil
Heat treatment temperature /℃| Tempering : 700
Hardness after annealing ≤HBS: 269 Max.
Tensile strength, Rm ≥ MPa: 835
Yield strength, Rp0.2 ≥ MPa: 735
Elongation, A ≥ (%): 14.0
Reduction of area, Z ≥ (%): 50.0
Impact strength, AKu ≥ J: 47
PRODUCT PROFILE & DIMENSIONS
Round bar & Disc (diameter): 5.5mm to 1100mm
Square bar / Flat bar: 8mm to 600mm
Length: Fixed length or random length or based on the customer's special requirement.
Sheet steel via cold rolled: T0.5 - 6mm X W60 - 1000mm X L1000 - 2000mm
TYPICAL APPLICATIONS
Alloy structural steels are widely used in the filed of ship, vehicle, airplane, guided missile, weapons, railway, bridges, pressure vessel, machine tools, mechanical components with a bigger sectional size and so on.
Power generation – turbine fasteners – boiler support rods.
Process plant – fasteners, Mechanical gears, gear shaft, main axis, valve rod
Mechanical parts - connecting rod, bolt and nuts.
Multidiameter shaft, Pressure vessel parts.
TECHNICAL SALES ASSISTANCE
If you meet further on any technical enquiry, pleased to email or call our resident team of qualified production engineers, Email: sales@ccsteels.com
Hot search：
Previous page：45Cr1MoVA
Last page：15Cr3 / 15Cr65
Total list
Monthly rank
- 3438NCD4
- 3424CrMo5
- 3119CrNi5
- 2938B3
- 28ASTM A739 type B11
- 2826NiCrMoV11-5
- 2742Cr4Mo2
- 24S135
- 24EN 38
- 22EN20B