X20CrMoV11-1
2014-10-21 10:58:06 Origin： Remark：0 Click：
Specifications X20CrMoV11-1 Datasheet, Inventory X20CrMoV11-1 Chemical, Grade X20CrMoV11-1 Properties from Steelmaking, ESR melted,Blooming, Forging, Hot rolling, Heat treatment, Straightening, Ultrasonic test, Cold working or Machined. We also possess the advanced precision machining equipments for further processing. Please just let us know what you inquire. Technical specification - DIN EN 10028-2.
Official Test Certificate: issued by TUV - SGS - BV
TECHNICAL DATA SHEET - X20CrMoV11-1
MATERIAL STANDARDS - DIN EN 10028-2 (2003), DIN 17755 (1983)
CHEMICAL COMPOSITION (WEIGHT %)
C (％): 0.17 ~ 0.23
Si (％): ≤ 0.50
Mn (％): ≤ 1.00
P (％)≤: 0.030
S (％)≤: 0.030
Cr (％): 10.0 ~ 12.5
Mo (％): 0.80 ~ 1.20
Ni (％): 0.30 ~ 0.80
V (％): 0.25 ~ 0.35
Si (％): ≤ 0.50
Mn (％): ≤ 1.00
P (％)≤: 0.030
S (％)≤: 0.030
Cr (％): 10.0 ~ 12.5
Mo (％): 0.80 ~ 1.20
Ni (％): 0.30 ~ 0.80
V (％): 0.25 ~ 0.35
MECHANICAL PROPERTIES - HOT WORKING, HEAT TREATMENT AND HARDNESS
Hot working temperature /℃: 1100～850
Heat treatment temperature /℃|annealing / normalizing: 700~780
Heat treatment temperature /℃|quenching: 1020~1070 Oil or Air
Heat treatment temperature /℃|tempering: 700~760
HBW: 205 ~ 250
Tensile strength, (≥)|σb/MPa: 690～830
Yield strength, (≥)|σs/MPa: 490
Elongation, (≥)|δ5(%): 16.0
Impact strength, (≥)|AKV/J: 41
Heat treatment temperature /℃|annealing / normalizing: 700~780
Heat treatment temperature /℃|quenching: 1020~1070 Oil or Air
Heat treatment temperature /℃|tempering: 700~760
HBW: 205 ~ 250
Tensile strength, (≥)|σb/MPa: 690～830
Yield strength, (≥)|σs/MPa: 490
Elongation, (≥)|δ5(%): 16.0
Impact strength, (≥)|AKV/J: 41
MECHANICAL PROPERTY UNDER HIGH TEMPERATURE