Description 1.6311 Ex-stock, Stocklist 1.6311 Suppliers, Round bar 1.6311 Forgings, Technical Specifications Melting, ESR & VAR technique, Hot blooming, Hot forging, Hot rolling, Heat treatment, Straightening, Ultrasonic flaw detection test.
MATERIAL DATA SHEET - Grade W-Nr 1.6311
MATERIAL CATEGORY - High temperature structural steel 
PRODUCT DESCRIPTION
Alloy structural steel is provided with higher yield strength, tensile strength, endurance strength, yield ratio (about 0.85 generally ) enough plasticity and toughness.
The concentration of alloy element of this kind of steel is quite high, mainly are corrosion resistant steel, heat resistant steel, wear resistant steel, and other special steels of physical and chemical properties. Alloy structural steel has preferable mechanical property than that of carbon structural steel, high performance of heat treatment especially.
The alloy is usually produced by EAF /VD /LF followed by electroslag refining (ESR) if necessary for special purpose.
Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different level according to the buyers' requirements.
Bars are usually supplied bright in the annealed condition.
Final heat treatment - heat treatment / QT 
MATERIAL SPECIFICATIONS - DIN EN 10028-2 (2003), DIN 17755 (1983) 
CHEMICAL COMPOSITION (Mass weight - %)
C (%):     0.17 ~ 0.23
Si (%):    ≤ 0.40
Mn (%):   1.00 ~ 1.50
P (%)≤:   0.035
S (%)≤:   0.035
Cr (%):    ≤ 0.50
Mo (%):   0.45 ~ 0.60
Ni (%):    0.40 ~ 0.80
MECHANICAL PROPERTIES - HOT WORKING, HEAT TREATMENT AND HARDNESS
Hot working temperature /℃:  1100~850
Heat treatment temperature /℃|annealing / normalizing:   580~620
Heat treatment temperature /℃|quenching: 870~940  Oil or Air
Heat treatment temperature /℃|tempering:  610~690
HBW:    -
Tensile strength, (≥)|σb/MPa: 570 ~ 750
Yield strength, (≥)|σs/MPa: 430
Elongation, (≥)|δ5(%): 18.0
Impact strength, (≥)|AKv /J: 41   
    
         
MECHANICAL PROPERTY UNDER HIGH TEMPERATURE
Yield strength σ0.2≥/MPa|200℃:    392
Yield strength σ0.2≥/MPa|300℃:    371
Yield strength σ0.2≥/MPa|350℃:    363
Yield strength σ0.2≥/MPa|400℃:    353
Yield strength σ0.2≥/MPa|450℃:    -
Yield strength σ0.2≥/MPa|500℃:   
AVAILABLE SHAPES  
Round bar / flat bar / hollow bar / strip / sheet
Bright - peeled + polishing, centerless grinding
Forged - ring, tube, pipe casing, discs, shaft
PROFILE / DIMENSION 
Round bar / Wire rod (Diameter): 5.5mm to 800mm
Square bar / Flat bar: 10mm to 1000mm
Plate / Sheet steel / Steel strip: 0.5mm to 1000mm
Width: 8mm to 1000mm
Length: random length or based on the customer's special requirement.
Forged steel shape: stepped shafts with flanks / discs /tubes /slugs /donuts /cubes /other different shapes based on OEM.
TYPICAL APPLICATIONS
Alloy structural steels are widely used in the filed of ship, vehicle, airplane, guided missile, weapons, railway, bridges, pressure vessel, machine tools, mechanical components with a bigger sectional size and so on. 
Mechanical gears, gear shaft, main axis, valve rod
Mechanical parts - connecting rod, bolt and nut
Multidiameter shaft and Pressure vessel