36NiCr6
2014-10-27 14:36:18 Origin： Remark：0 Click：
DIN 10083-2 Specifications hardened and tempered steel 36NiCr6 Round bar, flat bar, plale forgings, 36NiCr6 Stock available, Hot rolling, heat treatment
TECHNICAL DATA SHEET - DIN 36NiCr6
MATERIAL CATEGORY - hardened and tempered steel
MATERIAL SPECIFICATIONS - DIN EN 10083-2 (2006), DIN 17200 (1987)
CHEMICAL COMPOSITIONS (mass fraction - %)
Carbon, C (％): 0.32 ~ 0.40
Silicon, Si (％): 0.15 ~ 0.35
Manganese, Mn (％): 0.40 ~ 0.80
Phosphorus, P (％) ≤: 0.035
Sulfur, S (％) ≤: 0.035
Chromium, Cr (％): 0.30 ~ 0.70
Molybdenum, Mo (％): -
Nickel, Ni (％): 1.25 ~ 1.75
Silicon, Si (％): 0.15 ~ 0.35
Manganese, Mn (％): 0.40 ~ 0.80
Phosphorus, P (％) ≤: 0.035
Sulfur, S (％) ≤: 0.035
Chromium, Cr (％): 0.30 ~ 0.70
Molybdenum, Mo (％): -
Nickel, Ni (％): 1.25 ~ 1.75
MECHANICAL PROPERTIES - HOT WORKING, HEAT TREATMENT AND HARDNESS
Hot working temperature /℃: 1100～850
Heat treatment temperature /℃| annealing: 620～650
Heat treatment temperature /℃| Normalizing: 850～880
Heat treatment temperature /℃| Quenching: 830～860 Oil
Heat treatment temperature /℃| Tempering : 500～650
Hardness after annealing ≤ HBS: -
Heat treatment temperature /℃| annealing: 620～650
Heat treatment temperature /℃| Normalizing: 850～880
Heat treatment temperature /℃| Quenching: 830～860 Oil
Heat treatment temperature /℃| Tempering : 500～650
Hardness after annealing ≤ HBS: -
Steel dimension / mm: ≤ 16
Tensile strength, |Rm ≥ MPa: 980 ~ 1180
Yield strength, Rp0.2 ≥ MPa: 785
Elongation, A5 ≥ (%): 11.0
Reduction of area, Z ≥ (%): 45.0
Impact strength, AKv ≥ J: 48
Tensile strength, |Rm ≥ MPa: 980 ~ 1180
Yield strength, Rp0.2 ≥ MPa: 785
Elongation, A5 ≥ (%): 11.0
Reduction of area, Z ≥ (%): 45.0
Impact strength, AKv ≥ J: 48
Steel dimension /mm: 17 - 40
| σb ≥ MPa: 880 ~ 1030
| σs ≥ MPa: 685
| δ5 ≥ (%): 13.0
| σb ≥ MPa: 880 ~ 1030
| σs ≥ MPa: 685
| δ5 ≥ (%): 13.0
| ψ ≥ (%): 50.0
|AKv ≥ J: 62
|AKv ≥ J: 62
Steel dimension /mm: 41 - 100
| σb ≥ MPa: 780 ~ 930
| σs ≥ MPa: 590
| δ5 ≥ (%): 14
| ψ ≥ (%): 55
| AKv ≥ J: 69
| σb ≥ MPa: 780 ~ 930
| σs ≥ MPa: 590
| δ5 ≥ (%): 14
| ψ ≥ (%): 55
| AKv ≥ J: 69
TYPICAL APPLICATIONS
Alloy structural steels are widely used in the filed of ship, vehicle, airplane, guided missile, weapons, railway, bridges, pressure vessel, machine tools, mechanical components with a bigger sectional size and so on.
Mechanical gears, gear shaft, main axis, valve rod.
Mechanical parts - connecting rod, bolt and nut.
Multidiameter shaft, Pressure vessel.
PRODUCT PROFILE & DIMENSIONS
Round bar / rod / disc (diameter): 5.5mm ~ 850mm
Square bar / flat bar: 10mm to 610mm
Plate / sheet steel / Steel strip: 0.1mm to 300mm
Width: 8mm to 1200mm
Length: random length or based on the customer's special requirement.
Forged steel shape: stepped shafts, other different shapes based on OEM.
TECHNICAL SALES ASSISTANCE
If you meet further on any technical enquiry. pleased to email or call our resident team of qualified production engineers, Email: sales@ccsteels.com
Hot search：36NiCr6
Total list
Monthly rank
- 3438NCD4
- 3424CrMo5
- 3119CrNi5
- 2938B3
- 28ASTM A739 type B11
- 2826NiCrMoV11-5
- 2742Cr4Mo2
- 24S135
- 24EN 38
- 22EN20B