1.5864
2024-11-23 03:55:00 Origin： Remark：0 Click：
DIN EN 10083-2 Specifications 1.5864 Round bar, Flat bar, Plate 1.5864 Stock Available, Melting, ESR & VAR technique, Heat treatment
MATERIAL DATA SHEET - W-Nr 1.5864
MATERIAL CATEGORY: hardened and tempered steel
PRODUCT DESCRIPTION
Alloy structural steel is provided with higher yield strength, tensile strength, endurance strength, yield ratio (about 0.85 generally ) enough plasticity and toughness.
The concentration of alloy element of this kind of steel is quite high, mainly are corrosion resistant steel, heat resistant steel, wear resistant steel, and other special steels of physical and chemical properties. Alloy structural steel has preferable mechanical property than that of carbon structural steel, high performance of heat treatment especially.
The alloy is usually produced by EAF /VD /LF followed by electroslag refining (ESR) if necessary for special purpose. Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different level according to the buyers' requirements.
Bars are usually supplied bright in the annealed condition.
Final heat treatment - Quenched and tempered.
MATERIAL SPECIFICATIONS - DIN EN 10083-2 (2006), DIN 17200 (1987)
CHEMICAL COMPOSITION (mass weight - %)
Carbon, C (％): 0.30 ~ 0.40
Silicon, Si (％): 0.15 ~ 0.35
Manganese, Mn (％): 0.40 ~ 0.80
Phosphorus, P (％) ≤: 0.035
Sulfur, S (％) ≤: 0.035
Chromium, Cr (％): 1.10 ~ 1.50
Molybdenum, Mo (％): -
Nickel, Ni (％): 4.25 ~ 4.75
MECHANICAL PROPERTIES - HOT WORKING, HEAT TREATMENT AND HARDNESSSilicon, Si (％): 0.15 ~ 0.35
Manganese, Mn (％): 0.40 ~ 0.80
Phosphorus, P (％) ≤: 0.035
Sulfur, S (％) ≤: 0.035
Chromium, Cr (％): 1.10 ~ 1.50
Molybdenum, Mo (％): -
Nickel, Ni (％): 4.25 ~ 4.75
Hot working temperature /℃: 1100～850
Heat treatment temperature /℃| annealing: 580～610
Heat treatment temperature /℃| annealing: 580～610
Heat treatment temperature /℃| Normalizing: 830～860
Heat treatment temperature /℃| Quenching: 820～850 Oil or air cooling
Heat treatment temperature /℃| Tempering: 450～650
Hardness after annealing ≤HBS: -
Heat treatment temperature /℃| Quenching: 820～850 Oil or air cooling
Heat treatment temperature /℃| Tempering: 450～650
Hardness after annealing ≤HBS: -
Steel dimension /mm: 41 - 100
Tensile strength, Rm ≥ MPa: 1270 ~ 1470
Yield strength, Rp0.2 ≥ MPa: 1030
Elongation, A5 ≥ (%): 7
Reduction of area, Z ≥ (%): 35
Impact strength, AKv ≥ J: 34
Tensile strength, Rm ≥ MPa: 1270 ~ 1470
Yield strength, Rp0.2 ≥ MPa: 1030
Elongation, A5 ≥ (%): 7
Reduction of area, Z ≥ (%): 35
Impact strength, AKv ≥ J: 34
TYPICAL APPLICATIONS
Alloy structural steels are widely used in the filed of ship, vehicle, airplane, guided missile, weapons, railway, bridges, pressure vessel, machine tools, mechanical components with a bigger sectional size and so on.
Mechanical gears, gear shaft, main axis, valve rod.
Mechanical parts - connecting rod, bolt and nut.
Multidiameter shaft, Pressure vessel, seamless pipe.
TECHNICAL SALES ASSISTANCE
If you meet further on any technical enquiry. pleased to Email (sales@ccsteels.com) or call our resident team of qualified production engineers.
PRODUCT PROFILE
Round bar / Dics (diameter): 5.5 ~ 800mm
Square bar / Flat bar: 8 ~ 600mm
Plate / Sheet steel / Steel strip: 0.1mm to 1000mm
Width: 8mm to 1000mm
Length: random length or based on the customer's special requirement.
Forged steel shape: stepped shafts, other different shapes based on OEM.
Hot search：1.5864
Total list
Monthly rank
- 6038NCD4
- 5338B3
- 5342Cr4Mo2
- 4719CrNi5
- 4624CrMo5
- 3926NiCrMoV11-5
- 34ASTM A739 type B11
- 32EN 38
- 3214NiCr10 / 1.5732
- 30S135