Specifications X6Cr17 Ex-stock suppliers, Stocklist X6Cr17 Chemical, Inventory X6Cr17 properties from steelmaking, Hot forging, Hot rolling, Heat treat, Cold working. We also possess advanced precision machining equipments for further processing.
MATERIAL DATA SHEET - DIN X6Cr17
MATERIAL CATEGORY - Common alloy steel
PRODUCT DESCRIPTION
The alloy is usually produced by BEF AOD followed by electroslag refining (ESR) / VAR if necessary for special purpose.
Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied black/bright in the annealed condition.
Final heat treatment - solution treatment / QT
MATERIAL SPECIFICATIONS - DIN 17445,17440, DIN EN 10088-1, 10297,10272,10312
CHEMICAL COMPOSITION (WEIGHT %)
C (％): ≤ 0.08
Si (％): ≤ 1.00
Mn (％): ≤ 1.50
P (％)≤: 0.040
S (％)≤: 0.030
Cr (％): 16.0 ~ 18.0
Ni (％): -
Mo (％): -
MECHANICAL PROPERTIES UNDER ROOM TEMPERATURE
Condition: annealed
Thickness/mm: 100
σb/MPa: 400~630
σ0.2≥/MPa: 240
δ5≥(％): 20.0
ψ≥(％): 60.0
Akv≥/J: -
Hardness HBS30: 200max
MECHANICAL PROPERTIES FINAL HEAT TREATMENT ABOVE ROOM TEMPERATURE
Hot forming temp/℃: 1100 ~ 800
Heat treatment temperature and cooling methods|annealing: 750 ~ 800 air cooling
Heat treatment temperature and cooling methods|quenching: -
Heat treatment temperature and cooling methods|tempering: -
Condition: annealed
High temperature yield strength σ0.2/MPa≥/MPa，at below temp/℃|100: 220
High temperature yield strength σ0.2/MPa≥/MPa，at below temp/℃|200: 210
High temperature yield strength σ0.2/MPa≥/MPa，at below temp/℃|300: 200
High temperature yield strength σ0.2/MPa≥/MPa，at below temp/℃|400: 190
High temperature yield strength σ0.2/MPa≥/MPa，at below temp/℃|500: -
AVAILABILITY
Black bar /Flat bar / steel strip / square bar
Bright - peeled + polishing, centerless grinding
Forged - ring, tube, pipe casing, discs, shaft
MATERIAL CATEGORY - Common alloy steel
PRODUCT DESCRIPTION
The alloy is usually produced by BEF AOD followed by electroslag refining (ESR) / VAR if necessary for special purpose.
Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied black/bright in the annealed condition.
Final heat treatment - solution treatment / QT
MATERIAL SPECIFICATIONS - DIN 17445,17440, DIN EN 10088-1, 10297,10272,10312
CHEMICAL COMPOSITION (WEIGHT %)
C (％): ≤ 0.08
Si (％): ≤ 1.00
Mn (％): ≤ 1.50
P (％)≤: 0.040
S (％)≤: 0.030
Cr (％): 16.0 ~ 18.0
Ni (％): -
Mo (％): -
MECHANICAL PROPERTIES UNDER ROOM TEMPERATURE
Condition: annealed
Thickness/mm: 100
σb/MPa: 400~630
σ0.2≥/MPa: 240
δ5≥(％): 20.0
ψ≥(％): 60.0
Akv≥/J: -
Hardness HBS30: 200max
MECHANICAL PROPERTIES FINAL HEAT TREATMENT ABOVE ROOM TEMPERATURE
Hot forming temp/℃: 1100 ~ 800
Heat treatment temperature and cooling methods|annealing: 750 ~ 800 air cooling
Heat treatment temperature and cooling methods|quenching: -
Heat treatment temperature and cooling methods|tempering: -
Condition: annealed
High temperature yield strength σ0.2/MPa≥/MPa，at below temp/℃|100: 220
High temperature yield strength σ0.2/MPa≥/MPa，at below temp/℃|200: 210
High temperature yield strength σ0.2/MPa≥/MPa，at below temp/℃|300: 200
High temperature yield strength σ0.2/MPa≥/MPa，at below temp/℃|400: 190
High temperature yield strength σ0.2/MPa≥/MPa，at below temp/℃|500: -
AVAILABILITY
Black bar /Flat bar / steel strip / square bar
Bright - peeled + polishing, centerless grinding
Forged - ring, tube, pipe casing, discs, shaft
PRODUCT PROFILE
Round bar / Wire rod (Diameter): 5.5mm to 800mm
Square bar / Flat bar: 3mm to 800mm
Length: Fixed length or random length or based on the customer's special requirement.
Heavy/middle plate via hot rolled: T60 - 400mm X W50 - 1000mm X L1000 - 5000mm
Sheet steel via cold rolled: T0.5 - 6mm X W600- 1000mm X L1000 - 2000mm
Steel strip via cold rolled: T0.1 - 3mm X W5 - 200mm X L (or in coil form)
Forging piece: stepped shafts with flanks / discs /tubes /slugs /donuts /cubes /other different shapes based on OEM.
TYPICAL APPLICATIONS
Medical equipment
Chemical equipments
Mechanical parts used in the condition of corrosion resistance
Bolt and nut
Pressure vessel
TECHNICAL SALES ASSISTANCE
If you meet further on any technical enquiry. pleased to EMAIL our resident team of qualified production engineers, E-mail: sales@ccsteels.com
Round bar / Wire rod (Diameter): 5.5mm to 800mm
Square bar / Flat bar: 3mm to 800mm
Length: Fixed length or random length or based on the customer's special requirement.
Heavy/middle plate via hot rolled: T60 - 400mm X W50 - 1000mm X L1000 - 5000mm
Sheet steel via cold rolled: T0.5 - 6mm X W600- 1000mm X L1000 - 2000mm
Steel strip via cold rolled: T0.1 - 3mm X W5 - 200mm X L (or in coil form)
Forging piece: stepped shafts with flanks / discs /tubes /slugs /donuts /cubes /other different shapes based on OEM.
TYPICAL APPLICATIONS
Medical equipment
Chemical equipments
Mechanical parts used in the condition of corrosion resistance
Bolt and nut
Pressure vessel
TECHNICAL SALES ASSISTANCE
If you meet further on any technical enquiry. pleased to EMAIL our resident team of qualified production engineers, E-mail: sales@ccsteels.com
Hot search：X6Cr17
Previous page：1.2324
Last page：X6Cr17/DIN 1.4016
Total list
Monthly rank
- 3438NCD4
- 3424CrMo5
- 3119CrNi5
- 2938B3
- 28ASTM A739 type B11
- 2826NiCrMoV11-5
- 2742Cr4Mo2
- 24S135
- 24EN 38
- 22EN20B