X12CrCoNi21-20 Wholesalers Steels, X12CrCoNi21-20 Ex-stock Suppliers & Manufacturers, Grade X12CrCoNi21-20 Forge bar plate machined, X12CrCoNi21-20 Alloy exporter, from Melting, ESR & VAR technique, Blooming, Hot forging, Hot rolling, Heat treatment, Straightening, 100% Ultrasonic flaw detection test,
DIN X12CrCoNi21-20 & AMS 1.4974 - DATA SHEET
MATERIAL CATEGORY
High temperature high strength steel and superalloy
PRODUCT DESCRIPTION
The alloy is usually produced by AOD / EAF / BEF followed by electroslag refining (ESR) or VAR if necessary for special purpose.
Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different level according to the buyers' requirements.
Bars are usually supplied bright in the solution annealing condition.
Final heat treatment - heat treatment / QT / solution treatment
MATERIAL SPECIFICATIONS
DIN 17742, 17460, 17480 (2002/1992), DIN EN 103021, 10296, 10095 (2002/1999)
AVAILABLE SHAPES
Black bar /Flat bar /square bar
Bright - peeled + polishing /centerless grinding /peeled + slidabrading
Forged - ring /pipe casing /discs /shaft
CHEMICAL COMPOSITION (WEIGHT %)
C (%): 0.08 ~ 0.16
Si (%): ≤ 1.00
Mn (%): 1.00 ~ 2.00
P (%)≤: 0.040
S (%)≤: 0.030
Cr (%): 20.0 ~ 22.5
Ni (%): 19.0 ~ 21.0
Mo (%): 2.50 ~ 3.50
Co (%): 18.5 ~ 21.0
Si (%): ≤ 1.00
Mn (%): 1.00 ~ 2.00
P (%)≤: 0.040
S (%)≤: 0.030
Cr (%): 20.0 ~ 22.5
Ni (%): 19.0 ~ 21.0
Mo (%): 2.50 ~ 3.50
Co (%): 18.5 ~ 21.0
W (%): 2.00~3.00
Nb/Ta (%): 0.75 ~ 1.25
N (%): 0.10 ~ 0.20
MECHANICAL PROPERTIES - HOT WORKING, HEAT TREATMENT AND HARDNESS
Hot forming temperature /℃: 1150~950
Heat treatment temperature /℃ | annealing: -
Heat treatment temperature /℃ | quenching or solution: 1165~1195 air
Heat treatment temperature /℃ | tempering: 800~830
Heat treatment temperature /℃ | ageing: -
Condition: precipitation hardening
Mechanical property under room temperature |σb/MPa: 690~930
Mechanical property under room temperature |σs≥/MPa: 345
Mechanical property under room temperature |σs≥/MPa: 345
Mechanical property under room temperature |δ5≥(%): 20
Mechanical property under room temperature |Akv(DVM): 41
Heat stability temperature/℃: 730
Non-scale temperature in air /℃: 980
MECHANICAL PROPERTY UNDER HIGH TEMPERATURE
Mechanical property above 200℃ σ0.2/MPa,at following temperature /℃|200: 275
Mechanical property above 200℃ σ0.2/MPa,at following temperature /℃|300: 255
Mechanical property above 200℃ σ0.2/MPa,at following temperature /℃|400: 245
Mechanical property above 200℃ σ0.2/MPa,at following temperature /℃|500: 245
Mechanical property above 200℃ σ0.2/MPa,at following temperature /℃|600: 235
Mechanical property above 200℃ σ0.2/MPa,at following temperature /℃|700: 216
Mechanical property above 200℃ σ0.2/MPa,at following temperature /℃|800: 157
Mechanical property above 200℃ σ0.2/MPa,at following temperature /℃|300: 255
Mechanical property above 200℃ σ0.2/MPa,at following temperature /℃|400: 245
Mechanical property above 200℃ σ0.2/MPa,at following temperature /℃|500: 245
Mechanical property above 200℃ σ0.2/MPa,at following temperature /℃|600: 235
Mechanical property above 200℃ σ0.2/MPa,at following temperature /℃|700: 216
Mechanical property above 200℃ σ0.2/MPa,at following temperature /℃|800: 157
Creep rupture strength /MPa,at following time/h and temperature /℃|1000h|600: 353
Creep rupture strength /MPa,at following time/h and temperature /℃|1000h|700: 206
Creep rupture strength /MPa,at following time/h and temperature /℃|1000h|800: 103
Creep rupture strength /MPa,at following time/h and temperature /℃|1000h|900: 39
Creep rupture strength /MPa,at following time/h and temperature /℃|10000h|600: 284
Creep rupture strength /MPa,at following time/h and temperature /℃|10000h|700: 147
Creep rupture strength /MPa,at following time/h and temperature /℃|10000h|800: 65
Creep rupture strength /MPa,at following time/h and temperature /℃|10000h|900: -
Creep rupture strength /MPa,at following time/h and temperature /℃|1000h|700: 206
Creep rupture strength /MPa,at following time/h and temperature /℃|1000h|800: 103
Creep rupture strength /MPa,at following time/h and temperature /℃|1000h|900: 39
Creep rupture strength /MPa,at following time/h and temperature /℃|10000h|600: 284
Creep rupture strength /MPa,at following time/h and temperature /℃|10000h|700: 147
Creep rupture strength /MPa,at following time/h and temperature /℃|10000h|800: 65
Creep rupture strength /MPa,at following time/h and temperature /℃|10000h|900: -