Descriptions NiCr20Mo datasheet, NiCr20Mo Chemical, NiCr20Mo Properties from Steelmaking, Blooming, Hot forging, Hot rolling, Heat treatment, Straightening, 100% Ultrasonic flaw detection test, Cold working or Machined. All of these materials conform to Military standard, nuclear power. 100% Ultrasonic test ASTM E2375 /SAE AMS 2154 /SEP 1923 /GB/T 4162 /EN 10228-3.
MATERIAL TECHNICAL DATASHEET - DIN NiCr20Mo
MATERIAL CATEGORY - High temperature high strength steel and superalloy
PRODUCT DESCRIPTION
The alloy is usually produced by AOD/VIM/VOD followed by electroslag refining (ESR) or VAR if necessary for special purpose.
Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different level according to the buyers' requirements.
Bars are usually supplied bright in the solution annealing condition.
Final heat treatment - heat treatment / QT / solution treatment
MATERIAL SPECIFICATIONS - DIN 17742, 17460, 17480), DIN EN 103021, 10296
AVAILABLE SHAPES
Round bar / flat bar / square bar / ring / valve body / forge piece
Bright - peeled + polishing /centerless grinding /peeled + slidabrading
Forged - ring /pipe casing /discs /shaft
CHEMICAL COMPOSITION (WEIGHT %)
C (%): ≤ 0.10
Si (%): ≤ 1.00
Mn (%): ≤ 1.00
P (%)≤: 0.020
S (%)≤: 0.100
Cr (%): 18.0 ~ 21.0
Ni (%): Balance
Mo (%): 4.00 ~ 5.00
Al (%): 0.50 ~ 1.80
Si (%): ≤ 1.00
Mn (%): ≤ 1.00
P (%)≤: 0.020
S (%)≤: 0.100
Cr (%): 18.0 ~ 21.0
Ni (%): Balance
Mo (%): 4.00 ~ 5.00
Al (%): 0.50 ~ 1.80
Ti (%): 1.80 ~ 2.70
Others (%): Co ≤2.00, Fe ≤5.00
MECHANICAL PROPERTIES - HOT WORKING, HEAT TREATMENT AND HARDNESS
Hot forming temperature /℃: 1150~1050
Heat treatment temperature /℃ | annealing: -
Heat treatment temperature /℃ | quenching or solution: 1065~1095 water
Heat treatment temperature /℃ | tempering: 700~720
Heat treatment temperature /℃ | ageing: -
Condition: precipitation hardening
Mechanical property under room temperature |σb/MPa: ≥1180
Mechanical property under room temperature |σs≥/MPa: 735
Mechanical property under room temperature |σs≥/MPa: 735
Mechanical property under room temperature |δ5≥(%): 20
Mechanical property under room temperature |Akv(DVM): 27
Heat stability temperature/℃: -
Non-scale temperature in air /℃: 1000
MECHANICAL PROPERTY UNDER HIGH TEMPERATURE
Mechanical property above 200℃ σ0.2/MPa,at following temperature /℃|200: 706
Mechanical property above 200℃ σ0.2/MPa,at following temperature /℃|300: 706
Mechanical property above 200℃ σ0.2/MPa,at following temperature /℃|400: 696
Mechanical property above 200℃ σ0.2/MPa,at following temperature /℃|500: 696
Mechanical property above 200℃ σ0.2/MPa,at following temperature /℃|600: 686
Mechanical property above 200℃ σ0.2/MPa,at following temperature /℃|700: 667
Mechanical property above 200℃ σ0.2/MPa,at following temperature /℃|800: 490
Mechanical property above 200℃ σ0.2/MPa,at following temperature /℃|300: 706
Mechanical property above 200℃ σ0.2/MPa,at following temperature /℃|400: 696
Mechanical property above 200℃ σ0.2/MPa,at following temperature /℃|500: 696
Mechanical property above 200℃ σ0.2/MPa,at following temperature /℃|600: 686
Mechanical property above 200℃ σ0.2/MPa,at following temperature /℃|700: 667
Mechanical property above 200℃ σ0.2/MPa,at following temperature /℃|800: 490
Creep rupture strength /MPa,at following time/h and temperature /℃|1000h|600: 637
Creep rupture strength /MPa,at following time/h and temperature /℃|1000h|700: 343
Creep rupture strength /MPa,at following time/h and temperature /℃|1000h|800: 127
Creep rupture strength /MPa,at following time/h and temperature /℃|1000h|900: 29
Creep rupture strength /MPa,at following time/h and temperature /℃|10000h|600: 520
Creep rupture strength /MPa,at following time/h and temperature /℃|10000h|700: 245
Creep rupture strength /MPa,at following time/h and temperature /℃|10000h|800: 78
Creep rupture strength /MPa,at following time/h and temperature /℃|10000h|900: -
Creep rupture strength /MPa,at following time/h and temperature /℃|100000h|600: 412
Creep rupture strength /MPa,at following time/h and temperature /℃|1000h|700: 343
Creep rupture strength /MPa,at following time/h and temperature /℃|1000h|800: 127
Creep rupture strength /MPa,at following time/h and temperature /℃|1000h|900: 29
Creep rupture strength /MPa,at following time/h and temperature /℃|10000h|600: 520
Creep rupture strength /MPa,at following time/h and temperature /℃|10000h|700: 245
Creep rupture strength /MPa,at following time/h and temperature /℃|10000h|800: 78
Creep rupture strength /MPa,at following time/h and temperature /℃|10000h|900: -
Creep rupture strength /MPa,at following time/h and temperature /℃|100000h|600: 412
Creep rupture strength /MPa,at following time/h and temperature /℃|100000h|700: 162
Creep rupture strength /MPa,at following time/h and temperature /℃|100000h|800: 39
Creep rupture strength /MPa,at following time/h and temperature /℃|100000h|900: -
Creep rupture strength /MPa,at following time/h and temperature /℃|100000h|800: 39
Creep rupture strength /MPa,at following time/h and temperature /℃|100000h|900: -
TYPICAL APPLICATIONS
Superalloy is widely used to produce the high temperature components for gas turbine in the field of aviation, naval vessels and industry, such as turbine blade, guide blade, turbine disc, high pressure compressor disc, combustor, and also production of energy conversion devices, such as aerospace craft, rocket motor, nuclear reactor, petrochemical equipments, coaly transforming and so on.
Gas turbine
Turbine blade
Fuel nozzle
Heat treating fixture
Furnace muffle
Nuclear reactor
Turbine blade
Fuel nozzle
Heat treating fixture
Furnace muffle
Nuclear reactor
Turbine engine parts - mechanical gears, gear shaft, main axis, blade
Mechanical parts - bolt and nut, fastener
Heat treatment furnace flask and components, especially in the carbonization.
These materials must stand up to high heat, extreme oxidation potential and recycling.
These materials must stand up to high heat, extreme oxidation potential and recycling.
TECHNICAL SALES ASSISTANCE
If you meet further on any technical enquiry. pleased to email or call our resident team of qualified production engineers, Email: sales@ccsteels.com
PRODUCT PROFILE & FORM SIZES
Round bar / Wire rod (Diameter): 5.5mm to 450mm
Square bar / Flat bar: 3mm to 1000mm
Plate / Sheet steel / Steel strip: 0.1mm to 1000mm
Width: 8mm to 1000mm
Length: random length or based on the customer's special requirement.
Forged steel shape: stepped shafts with flanks / discs /tubes /slugs /donuts /cubes /other different shapes based on OEM.