DIN X40CoGrNi20-20 & W-Nr 1.4977 - DATA SHEET
MECHANICAL PROPERTIES - HOT WORKING, HEAT TREATMENT AND HARDNESS
MATERIAL CATEGORY
High temperature high strength steel and superalloy
PRODUCT DESCRIPTION
The alloy is usually produced by AOD / VIM / VD followed by electroslag refining (ESR) or VAR if necessary for special purpose.
Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different level according to the buyers' requirements.
Bars are usually supplied bright in the solution annealing condition.
Final heat treatment - heat treatment / QT / solution treatment
MATERIAL SPECIFICATIONS
DIN 17742, 17460, 17480 (2002/1992), DIN EN 103021, 10296, 10095 (2002/1999)
AVAILABLE SHAPES
Black bar /Flat bar /square bar
Bright - peeled + polishing /centerless grinding /peeled + slidabrading
Forged - ring /pipe casing /discs /shaft
CHEMICAL COMPOSITION (WEIGHT %) -
C (％): 0.35～0.45
Si (％): ≤ 1.00
Mn (％): ≤ 1.50
P (％)≤: 0.045
S (％)≤: 0.030
Cr (％): 19.0～21.0
Ni (％): 19.0～21.0
Mo (％): 3.50～4.50
Other (％): Co 19.0～21.0, W 3.50～4.50, Nb/Ta 3.50～4.50
Si (％): ≤ 1.00
Mn (％): ≤ 1.50
P (％)≤: 0.045
S (％)≤: 0.030
Cr (％): 19.0～21.0
Ni (％): 19.0～21.0
Mo (％): 3.50～4.50
Other (％): Co 19.0～21.0, W 3.50～4.50, Nb/Ta 3.50～4.50
Hot forming temperature /℃: 1150～950
Heat treatment temperature /℃ | annealing: -
Heat treatment temperature /℃ | quenching or solution: 1150~1220 air / water
Heat treatment temperature /℃ | tempering: 750~800
Heat treatment temperature /℃ | ageing: -
Condition: precipitation hardening
Mechanical property under room temperature |σb/MPa: 780~980
Mechanical property under room temperature |σs≥/MPa: 390
Mechanical property under room temperature |σs≥/MPa: 390
Mechanical property under room temperature |δ5≥(％): 20
Mechanical property under room temperature |Akv(DVM): 27
Heat stability temperature/℃: 800
Non-scale temperature in air /℃: 950
MECHANICAL PROPERTY UNDER HIGH TEMPERATURE
Mechanical property above 200℃ σ0.2/MPa，at following temperature /℃|200: 353
Mechanical property above 200℃ σ0.2/MPa，at following temperature /℃|300: 333
Mechanical property above 200℃ σ0.2/MPa，at following temperature /℃|400: 314
Mechanical property above 200℃ σ0.2/MPa，at following temperature /℃|500: 294
Mechanical property above 200℃ σ0.2/MPa，at following temperature /℃|600: 245
Mechanical property above 200℃ σ0.2/MPa，at following temperature /℃|700: 206
Mechanical property above 200℃ σ0.2/MPa，at following temperature /℃|800: -
Mechanical property above 200℃ σ0.2/MPa，at following temperature /℃|300: 333
Mechanical property above 200℃ σ0.2/MPa，at following temperature /℃|400: 314
Mechanical property above 200℃ σ0.2/MPa，at following temperature /℃|500: 294
Mechanical property above 200℃ σ0.2/MPa，at following temperature /℃|600: 245
Mechanical property above 200℃ σ0.2/MPa，at following temperature /℃|700: 206
Mechanical property above 200℃ σ0.2/MPa，at following temperature /℃|800: -
Creep rupture strength /MPa，at following time/h and temperature /℃|1000h|600: -
Creep rupture strength /MPa，at following time/h and temperature /℃|1000h|700: -
Creep rupture strength /MPa，at following time/h and temperature /℃|1000h|800: -
Creep rupture strength /MPa，at following time/h and temperature /℃|1000h|900:
Creep rupture strength /MPa，at following time/h and temperature /℃|10000h|600: 294
Creep rupture strength /MPa，at following time/h and temperature /℃|10000h|700: 147
Creep rupture strength /MPa，at following time/h and temperature /℃|10000h|800: 64
Creep rupture strength /MPa，at following time/h and temperature /℃|10000h|900: -
Creep rupture strength /MPa，at following time/h and temperature /℃|100000h|600: 226
Creep rupture strength /MPa，at following time/h and temperature /℃|1000h|700: -
Creep rupture strength /MPa，at following time/h and temperature /℃|1000h|800: -
Creep rupture strength /MPa，at following time/h and temperature /℃|1000h|900:
Creep rupture strength /MPa，at following time/h and temperature /℃|10000h|600: 294
Creep rupture strength /MPa，at following time/h and temperature /℃|10000h|700: 147
Creep rupture strength /MPa，at following time/h and temperature /℃|10000h|800: 64
Creep rupture strength /MPa，at following time/h and temperature /℃|10000h|900: -
Creep rupture strength /MPa，at following time/h and temperature /℃|100000h|600: 226
Creep rupture strength /MPa，at following time/h and temperature /℃|100000h|700: 98
Creep rupture strength /MPa，at following time/h and temperature /℃|100000h|800: 34
Creep rupture strength /MPa，at following time/h and temperature /℃|100000h|900: -
Creep rupture strength /MPa，at following time/h and temperature /℃|100000h|800: 34
Creep rupture strength /MPa，at following time/h and temperature /℃|100000h|900: -
TYPICAL APPLICATIONS
Superalloy is widely used to produce the high temperature components for gas turbine in the field of aviation, naval vessels and industry, such as turbine blade, guide blade, turbine disc, high pressure compressor disc, combustor, and also production of energy conversion devices, such as aerospace craft, rocket motor, nuclear reactor, petrochemical equipments, coaly transforming and so on.
Gas turbine
Turbine blade
Fuel nozzle
Heat treating fixture
Furnace muffle
Nuclear reactor
Turbine blade
Fuel nozzle
Heat treating fixture
Furnace muffle
Nuclear reactor
Turbine engine parts - mechanical gears, gear shaft, main axis, blade
Mechanical parts - bolt and nut, fastener
Heat treatment furnace flask and components, especially in the carbonization.
These materials must stand up to high heat, extreme oxidation potential and recycling.
These materials must stand up to high heat, extreme oxidation potential and recycling.
PRODUCT PROFILE
Round bar / Wire rod (Diameter): 5.5mm to 600mm
Square bar / Flat bar: 10mm to 600mm
Plate / Sheet steel / Steel strip: 0.1mm to 1000mm
Width: 8mm to 1000mm
Length: random length or based on the customer's special requirement.
Forged steel shape: stepped shafts with flanks / discs /tubes /slugs /donuts /cubes /other different shapes based on OEM.