X6CrNiMoTiB17-13
2015-01-07 10:41:33 Origin： Remark：0 Click：
Specifications X6CrNiMoTiB17-13 data sheet, X6CrNiMoTiB17-13 Chemical, X6CrNiMoTiB17-13 properties from steelmaking, ESR, blooming, hot forging, rolling, heat treatment, straightened, ultrasonic test, cold working, machined. We also possess advanced precision machining equipments for further processing
TECHNICAL DATA SHEET - Heat Resisting Steel - DIN X6CrNiMoTiB17-13
MATERIAL CATEGORY - Austenitic creep-resisting steels
FEATURES AND CLASSIFICATIONS
Heat-resistant steel means one type of steel possesses inoxidizability, enough high-temperature strength and excellent heat-resistant quality under high temperature. Heat resistant steel is divided into oxidation resistant steel and refractory steel according to its performance. Further into Austenitic heat-resistant steel, Martensitic heat-resistant steel, Ferritic heat-resistant steel and Pearlitic heat-resistant steel according to its normalizing.
Heat-resistant steel means one type of steel possesses inoxidizability, enough high-temperature strength and excellent heat-resistant quality under high temperature. Heat resistant steel is divided into oxidation resistant steel and refractory steel according to its performance. Further into Austenitic heat-resistant steel, Martensitic heat-resistant steel, Ferritic heat-resistant steel and Pearlitic heat-resistant steel according to its normalizing.
MATERIAL SPECIFICATIONS - DIN 17442, 17744 (2002), DIN 10302, 10095, EN 10088-1 (2005)
CHEMICAL COMPOSITION (WEIGHT %)
C (％): 0.04 ~ 0.08
Si (％): ≤ 0.75
Mn (％): ≤ 2.00
Si (％): ≤ 0.75
Mn (％): ≤ 2.00
P (％)≤: 0.035
S (％)≤: 0.015
Cr (％): 16.0 ~ 18.0
Ni (％): 12.0 ~ 14.0
S (％)≤: 0.015
Cr (％): 16.0 ~ 18.0
Ni (％): 12.0 ~ 14.0
Mo (%): 2.00 ~ 2.50
W (%): -
N (%): -
V (%): -
Al (%): -
Nb (%): -
B (％): 0.0015 ~ 0.0060
Ti (%): 5XC ~ 0.80
MECHANICAL PROPERTIES UNDER ROOM TEMPERATURE
Condition: solution treatment
Tensile strength, σb/MPa: 530 min.
Condition: solution treatment
Tensile strength, σb/MPa: 530 min.
Yield strength, σs≥/MPa: 255 min.
Elongation, δ5≥(％): 35
Elongation, δ5≥(％): 35
APPLICATION FIELD
Heat-resistant steel is widely used in the field of manufacturing the boiler, steam turbine, motive power machine, industrial furnace, and other mechanical parts of aviation, petrochemical engineering operating at high temperature. Those parts must hold the features: high temperature strength, resistance to high temperature oxide etch, enough toughness, excellent machinability, weldability, structure stability based on different usages.
Heat-resistant steel is widely used in the field of manufacturing the boiler, steam turbine, motive power machine, industrial furnace, and other mechanical parts of aviation, petrochemical engineering operating at high temperature. Those parts must hold the features: high temperature strength, resistance to high temperature oxide etch, enough toughness, excellent machinability, weldability, structure stability based on different usages.
MANUFACTURING TECHNOLOGY - SMELTING
Heat resistant steel is generally smelt in electric arc furnace or induction furnace. For higher quality,it should be smelt via technology of vacuum refining and external refining.
TECHNICAL SALES ASSISTANCE
If you meet further on any technical enquiry, pleased to EMAIL our resident team of qualified production engineers, Email: sales@ccsteels.com
Heat resistant steel is generally smelt in electric arc furnace or induction furnace. For higher quality,it should be smelt via technology of vacuum refining and external refining.
TECHNICAL SALES ASSISTANCE
If you meet further on any technical enquiry, pleased to EMAIL our resident team of qualified production engineers, Email: sales@ccsteels.com
PRODUCT PROFILE & DIMENSIONS
Round bar / Wire rod (Diameter): 5.5mm to 450mm
Square bar / Flat bar: 3mm to 800mm
Length: Fixed length or random length or based on the customer's special requirement.
Round bar / Wire rod (Diameter): 5.5mm to 450mm
Square bar / Flat bar: 3mm to 800mm
Length: Fixed length or random length or based on the customer's special requirement.
Heavy/middle plate via hot rolled: T60 - 400mm X W50 - 1000mm X L1000 - 12000mm
Sheet steel via cold rolled: T0.5 - 6mm X W100 - 1000mm X L1000 - 2000mm
Steel strip via cold rolled: T0.1 - 3mm X W5 - 200mm X L (or in coil form)
Forging piece: stepped shafts with flanks / discs /tubes /slugs /donuts /cubes /other different shapes based on OEM.
Sheet steel via cold rolled: T0.5 - 6mm X W100 - 1000mm X L1000 - 2000mm
Steel strip via cold rolled: T0.1 - 3mm X W5 - 200mm X L (or in coil form)
Forging piece: stepped shafts with flanks / discs /tubes /slugs /donuts /cubes /other different shapes based on OEM.