X3CrNiMoBN17-13-3
2014-09-11 10:15:30 Origin： Remark：0 Click：
Description X3CrNiMoBN17-13-3 datasheet, X3CrNiMoBN17-13-3 Chemical, X3CrNiMoBN17-13-3 Properties Steelmaking, ESR & VAR technique, Blooming, Hot forging & rolling, Heat treatment, Straightening, 100% Ultrasonic flaw detection test, Cold working or Machined. All of these materials conform to Military standard, nuclear power. 100% Ultrasonic test ASTM E2375 /SAE AMS 2154 /SEP 1923 /GB/T 4162 /EN 10228-3.
TECHNICAL DATA SHEET - Grade X3CrNiMoBN17-13-3
OFFICIAL TEST CERTIFICATE: issued by TUV - SGS - BV
MATERIAL CATEGORY: Nickel base Superalloy
CHEMICAL COMPOSITION (WEIGHT %)
C (％): ≤ 0.04
Si (％): ≤ 0.75
Mn (％): ≤ 1.20
P (％)≤: 0.035
S (％)≤: 0.015
Cr (％): 16.0 ~ 18.0
Ni (％): 12.0 ~ 14.0
Mo (％): 2.00 ~ 2.80
N (％): 0.10 ~ 0.18
Si (％): ≤ 0.75
Mn (％): ≤ 1.20
P (％)≤: 0.035
S (％)≤: 0.015
Cr (％): 16.0 ~ 18.0
Ni (％): 12.0 ~ 14.0
Mo (％): 2.00 ~ 2.80
N (％): 0.10 ~ 0.18
B (%): 0.0015 ~ 0.0050
TYPICAL MECHANICAL PROPERTIES
Hot forming temperature /℃: 1150～750
Heat treatment temperature /℃ | annealing: -
Heat treatment temperature /℃ | quenching or solution: 1020 ~ 1100 air / water
Heat treatment temperature /℃ | tempering: -
Heat treatment temperature /℃ | ageing: -
Condition: solution treatment
Mechanical property under room temperature |σb/MPa: 550~750
Mechanical property under room temperature |σs≥/MPa: 260
Mechanical property under room temperature |δ5≥(％): 35
Mechanical property under room temperature |Akv(DVM): -
Heat stability temperature/℃: -
Non-scale temperature in air /℃: -
TYPICAL APPLICATIONS
Superalloy is widely used to produce the high temperature components for gas turbine in the field of aviation, naval vessels and industry, such as turbine blade, guide blade, turbine disc, high pressure compressor disc, combustor, and also production of energy conversion devices, such as aerospace craft, rocket motor, nuclear reactor, petrochemical equipments, coaly transforming and so on.
The alloy is usually produced by AOD / VD / VIM followed by electroslag refining (ESR) / VAR if necessary for special purpose.
Bars are usually supplied bright surface in the solution annealed condition.
Final heat treatment - solution + Aged or Double aged.
Gas turbine
Turbine blade
Fuel nozzle
Heat treating fixture
Furnace muffle
Nuclear reactor
Final heat treatment - solution + Aged or Double aged.
Gas turbine
Turbine blade
Fuel nozzle
Heat treating fixture
Furnace muffle
Nuclear reactor
Turbine engine parts - mechanical gears, gear shaft, main axis, blade
Mechanical parts - bolt and nut, fastener
Heat treatment furnace flask and components, especially in the carbonization.
These materials must stand up to high heat, extreme oxidation potential and recycling.
These materials must stand up to high heat, extreme oxidation potential and recycling.
AVAILABLE FORMS AND SHAPES
Round bar (Diameter): 5.5 ~ 450mm
Square bar / Flat bar: 3 ~ 350mm
Round bar (Diameter): 5.5 ~ 450mm
Square bar / Flat bar: 3 ~ 350mm
Wire rod (Diameter): 0.10 ~ 16mm
Steel strip via cold rolled: T0.1 - 3mm X W5 - 200mm X L (or in coil form)
Forging piece: Different shapes based on OEM.
Steel strip via cold rolled: T0.1 - 3mm X W5 - 200mm X L (or in coil form)
Forging piece: Different shapes based on OEM.
Other sizes can be supplied to meet specific requirements.
TECHNICAL SALES ASSISTANCE
If you meet further on any technical enquiry, pleased to EMAIL (sales@ccsteels.com) our qualified production engineers.
If you meet further on any technical enquiry, pleased to EMAIL (sales@ccsteels.com) our qualified production engineers.
Hot search：X3CrNiMoBN17-13-3
Previous page：X3CrNiMoN17-13
Last page：1.4910